Effect of Scanning Speed on Structure and Wear Resistance of Laser Cladding Mo2FeB2 Cermet Layer
摘 要
采用激光熔覆工艺在Q235钢板表面制备Mo2FeB2金属陶瓷熔覆层,研究了激光扫描速度对熔覆层组织、显微硬度和耐磨性能的影响。结果表明:Mo2FeB2金属陶瓷熔覆层由Mo2FeB2、(Mo,Fe,Cr)3B2、CrB、MoB、Fe-Cr等相组成;随着扫描速度的增大,Mo2FeB2硬质相由长条状转变成块状,尺寸减小;扫描速度对硬质相含量的影响不大;随着扫描速度的增大,Mo2FeB2金属陶瓷熔覆层的平均显微硬度和磨损质量损失均先减小后增大;扫描速度为400 mm·min-1时熔覆层的硬度较高,耐磨性能最好。
Abstract
Mo2FeB2 cermet cladding layer was prepared on Q235 steel plate surface by laser cladding technique. The effect of laser scanning speed on the structure, microhardness, and wear resistance of the cladding layer was studied. The results show that the Mo2FeB2 cermet cladding layer was composed of Mo2FeB2, (Mo,Fe,Cr)3B2, CrB, MoB, and Fe-Cr phases. With the increase of scanning speed, the morphology of the Mo2FeB2 hard phase changed from long strip to block, and the size decreased. The scanning speed had little effect on the content of the hard phase. With the increase of scanning speed, the average microhardness and the wear mass loss of Mo2FeB2 cermet cladding layer decreased first and then increased. When the scanning speed was 400 mm·min-1, the hardness of the cladding layer was relatively high and the wear resistance was the best.
中图分类号 TG135 TG148 TG456.7 DOI 10.11973/jxgccl202306012
所属栏目 材料性能及应用
基金项目 泰安市科技创新重大专项项目(2021ZDZX020)
收稿日期 2022/4/14
修改稿日期 2023/5/19
网络出版日期
作者单位点击查看
备注孙俊生(1963-),男,山东聊城人,教授,博士
引用该论文: SUN Junsheng,GUAN Changyong,XU Hu,WANG Dezhu. Effect of Scanning Speed on Structure and Wear Resistance of Laser Cladding Mo2FeB2 Cermet Layer[J]. Materials for mechancial engineering, 2023, 47(6): 67~71
孙俊生,关常勇,徐虎,王德柱. 扫描速度对Mo2FeB2金属陶瓷激光熔覆层组织和耐磨性能的影响[J]. 机械工程材料, 2023, 47(6): 67~71
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘宇,魏祥,魏修宇,等.Mo2FeB2基金属陶瓷的研究进展[J].硬质合金,2021,38(5):376-385. LIU Y,WEI X,WEI X Y,et al.Research progress on Mo2FeB2 based cermets[J].Cemented Carbide,2021,38(5):376-385.
【2】魏祥,彭广威,鱼宏斌,等.硼含量对Fe2B-Mo2FeB2基金属陶瓷微观组织与性能的影响[J].金属热处理,2021,46(10):58-64. WEI X,PENG G W,YU H B,et al.Effect of boron content on microstructure and mechanical properties of Fe2B-Mo2FeB2-based cermets[J].Heat Treatment of Metals,2021,46(10):58-64.
【3】JIN J,SUN J S,WANG W M,et al.Effect of rare earth on microstructure and wear resistance of in-situ-synthesized Mo2FeB2 ceramics-reinforced Fe-based cladding[J].Materials,2020,13(16):3633.
【4】ZHOU X P,HU X B,XU Y S.The microstructure and properties of coating from Mo2FeB2 cermet on surface of H13 steel by reactive flame spraying[J].Advanced Materials Research,2010,97/98/99/100/101:1321-1327.
【5】王敏,赵伟文,孙勇涛.激光熔覆制备发动机传动装置零部件表面高硬度涂层及性能研究[J].工程机械,2023,54(2):26-31. WANG M,ZHAO W W,SUN Y T.Research on preparation of high hardness coatings on engine transmission parts by laser cladding and their properties[J].Construction Machinery and Equipment,2023,54(2):26-31.
【6】何军委,吴保桥,吴湄庄,等.热处理对钢基/Mo2FeB2金属陶瓷的性能影响[J].安徽冶金科技职业学院学报,2021,31(1):17-19. HE J W,WU B Q,WU M Z,et al.Effect of heat treatment on properties of steel matrix/Mo2FeB2 cermet[J].Journal of Anhui Vocational College of Metallurgy and Technology,2021,31(1):17-19.
【7】WANG H Q,SUN J S,LI C N,et al.Microstructure and mechanical properties of molybdenum-iron-boron-chromium cladding using argon arc welding[J].Materials Science and Technology,2016,32(16):1694-1701.
【8】顾建,李冬青,王开明.42CrMo钢表面激光熔覆镍基复合熔覆层组织和性能的研究[J].热加工工艺,2019,48(24):111-114. GU J,LI D Q,WANG K M.Study on microstructure and properties of laser coated Ni-based composite coating on 42CrMo steel[J].Hot Working Technology,2019,48(24):111-114.
【9】倪晓杰,刘福康,胡肇炜,等.激光熔覆Mo2NiB2熔覆层的制备及其性能表征[J].应用激光,2021,41(1):122-130. NI X J,LIU F K,HU Z W,et al.Investigation on the preparation and property of the laser-cladded Mo2NiB2 coatings[J].Applied Laser,2021,41(1):122-130.
【2】魏祥,彭广威,鱼宏斌,等.硼含量对Fe2B-Mo2FeB2基金属陶瓷微观组织与性能的影响[J].金属热处理,2021,46(10):58-64. WEI X,PENG G W,YU H B,et al.Effect of boron content on microstructure and mechanical properties of Fe2B-Mo2FeB2-based cermets[J].Heat Treatment of Metals,2021,46(10):58-64.
【3】JIN J,SUN J S,WANG W M,et al.Effect of rare earth on microstructure and wear resistance of in-situ-synthesized Mo2FeB2 ceramics-reinforced Fe-based cladding[J].Materials,2020,13(16):3633.
【4】ZHOU X P,HU X B,XU Y S.The microstructure and properties of coating from Mo2FeB2 cermet on surface of H13 steel by reactive flame spraying[J].Advanced Materials Research,2010,97/98/99/100/101:1321-1327.
【5】王敏,赵伟文,孙勇涛.激光熔覆制备发动机传动装置零部件表面高硬度涂层及性能研究[J].工程机械,2023,54(2):26-31. WANG M,ZHAO W W,SUN Y T.Research on preparation of high hardness coatings on engine transmission parts by laser cladding and their properties[J].Construction Machinery and Equipment,2023,54(2):26-31.
【6】何军委,吴保桥,吴湄庄,等.热处理对钢基/Mo2FeB2金属陶瓷的性能影响[J].安徽冶金科技职业学院学报,2021,31(1):17-19. HE J W,WU B Q,WU M Z,et al.Effect of heat treatment on properties of steel matrix/Mo2FeB2 cermet[J].Journal of Anhui Vocational College of Metallurgy and Technology,2021,31(1):17-19.
【7】WANG H Q,SUN J S,LI C N,et al.Microstructure and mechanical properties of molybdenum-iron-boron-chromium cladding using argon arc welding[J].Materials Science and Technology,2016,32(16):1694-1701.
【8】顾建,李冬青,王开明.42CrMo钢表面激光熔覆镍基复合熔覆层组织和性能的研究[J].热加工工艺,2019,48(24):111-114. GU J,LI D Q,WANG K M.Study on microstructure and properties of laser coated Ni-based composite coating on 42CrMo steel[J].Hot Working Technology,2019,48(24):111-114.
【9】倪晓杰,刘福康,胡肇炜,等.激光熔覆Mo2NiB2熔覆层的制备及其性能表征[J].应用激光,2021,41(1):122-130. NI X J,LIU F K,HU Z W,et al.Investigation on the preparation and property of the laser-cladded Mo2NiB2 coatings[J].Applied Laser,2021,41(1):122-130.
相关信息