Monel 400合金阀体裂纹产生原因
Cause of cracks in Monel 400 alloy valve body
摘 要
在阀门的焊接过程中,其表面出现了裂纹,采用宏观观察、化学成分分析、金相检验、扫描电镜和能谱分析等方法对裂纹形成的原因进行了分析,结果表明:产生裂纹的主要原因是熔炼过程中残留了未完全反应的电渣。
阀体
非金属夹杂物
裂纹
Monel 400 alloy
valve body
non-metallic inclusion
crack
Abstract
During the welding process of the valve, cracks appeared on the surface of the valve. The cause of the cracks was analyzed by means of macroscopic observation, chemical composition analysis, metallographic examination, scanning electron microscopy and energy spectrum analysis. The results show that the main cause of the cracks was the residual incomplete reaction of electroslag in the smelting process.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202308007
所属栏目 质量控制与失效分析
基金项目
收稿日期 2023/4/16
修改稿日期
网络出版日期
作者单位点击查看
备注尉成栋(1986-),男,硕士,主要从事金属材料的理化检验与失效分析工作,232422734@qq.com
引用该论文: WEI Chengdong,ZHAO Jiefang. Cause of cracks in Monel 400 alloy valve body[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(8): 28～31
尉成栋,赵洁芳. Monel 400合金阀体裂纹产生原因[J]. 理化检验－物理分册, 2023, 59(8): 28～31
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张涛,郑文杰,李才巨.冷拔后退火对Monel 400合金丝材的再结晶过程及力学性能的影响[J].金属热处理,2022,47(1):56-62.
【2】翁文林,李雄,周怀杰,等.蒙乃尔合金在海洋石油管线中的应用[J].石油和化工设备,2021,24(1):82-86.
【3】陆钰珍.特殊阀门用蒙乃尔合金性能及应用[J].机械研究与应用,2020,33(2):143-146,150.
【4】方轶,刘庭耀.Monel K-500合金电渣重熔锭内裂纹分析及改进措施[J].特钢技术,2022,28(3):33-38.
【2】翁文林,李雄,周怀杰,等.蒙乃尔合金在海洋石油管线中的应用[J].石油和化工设备,2021,24(1):82-86.
【3】陆钰珍.特殊阀门用蒙乃尔合金性能及应用[J].机械研究与应用,2020,33(2):143-146,150.
【4】方轶,刘庭耀.Monel K-500合金电渣重熔锭内裂纹分析及改进措施[J].特钢技术,2022,28(3):33-38.
相关信息