万向轴十字销断裂原因
Fracture reason of cross pin of universal shaft
摘 要
某万向轴十字销在机车运行过程中发生断裂,采用宏观观察、化学成分分析、硬度测试、金相检验、扫描电镜分析等方法对其断裂原因进行了分析。结果表明:不良的淬火马氏体组织及大尺寸的MnS夹杂降低了十字销倒角部位的抗疲劳性能,在交变应力的作用下,十字销发生疲劳断裂。
疲劳断裂
MnS夹杂
淬火马氏体
cross pin
fatigue fracture
MnS inclusion
quenched martensite
Abstract
A universal shaft cross pin fractured during the operation of the locomotive. The fracture cause was analyzed by means of macroscopic observation, chemical composition analysis, hardness test, metallographic examination and scanning electron microscope analysis. The results show that the poor quenched martensite structure and large size MnS inclusions reduced the fatigue resistance of the chamfered part of the cross pin. Under the action of alternating stress, the fatigue fracture of the cross pin occurred.
中图分类号 TB31 TG115.2 DOI 10.11973/lhjy-wl202308010
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/12/22
修改稿日期
网络出版日期
作者单位点击查看
备注汪瑞俊(1983-),男,高级工程师,主要从事材料理化性能测试分析工作,chzwangrj@aliyun.com
引用该论文: WANG Ruijun. Fracture reason of cross pin of universal shaft[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(8): 40～42
汪瑞俊. 万向轴十字销断裂原因[J]. 理化检验－物理分册, 2023, 59(8): 40～42
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘嘉伟,王天剑,刘禹炯.油动机底座连接螺栓断裂原因[J].理化检验(物理分册),2020,56(10):39-41,46.
【2】黄丽荣,汤宏智.40Cr钢汽车半轴断裂失效分析[J].机械工程材料,2009,33(5):73-75,79.
【3】贺凯林,金丽萍.40CrNiMo钢主轴断裂原因分析[J].理化检验(物理分册),2017,53(9):668-670,674.
【2】黄丽荣,汤宏智.40Cr钢汽车半轴断裂失效分析[J].机械工程材料,2009,33(5):73-75,79.
【3】贺凯林,金丽萍.40CrNiMo钢主轴断裂原因分析[J].理化检验(物理分册),2017,53(9):668-670,674.
相关信息