再热器TP347H钢受热面管开裂原因
Cracking cause of TP347H steel heating surface tube of reheater
摘 要
某电厂后屏再热器TP347H奥氏体不锈钢受热面管发生开裂,采用宏观观察、扫描电镜和能谱分析、室温拉伸试验等方法分析其开裂原因。结果表明:TP347H奥氏体不锈钢受热面管发生脆性开裂,其显微组织老化级别为4. 5级;受热面管长期过热运行后,晶界析出粗大的碳化物,组织发生劣化,材料的脆性增加,导致管子开裂。
析出相
组织劣化
开裂
TP347H austenitic stainless steel
precipitated phase
organizational deterioration
cracking
Abstract
The TP347H austenitic stainless steel heating surface tube of the rear platen reheater of a power plant cracked. The cracking cause was analyzed by macroscopic observation, scanning electron microscopy and energy spectrum analysis, room temperature tensile test and other methods.The results show that the TP347H austenitic stainless steel heating surface tube had brittle cracking, and its microstructure aging level was 4.5. After the heating surface tube was overheated for a long time, coarse carbides were precipitated at the grain boundary, the microstructure deteriorated, and the brittleness of the material increased, resulting in cracking of the tube.
中图分类号 TB31 TG115.2 DOI 10.11973/lhjy-wl202308013
所属栏目 质量控制与失效分析
基金项目
收稿日期 2023/3/7
修改稿日期
网络出版日期
作者单位点击查看
备注周浩(1995-),男,硕士,工程师,主要从事火电厂金属高温部件失效分析等方面的研究工作,ustbzhouhao@163.com
引用该论文: ZHOU Hao. Cracking cause of TP347H steel heating surface tube of reheater[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(8): 51～54
周浩. 再热器TP347H钢受热面管开裂原因[J]. 理化检验－物理分册, 2023, 59(8): 51～54
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】徐连勇,赵雷,荆洪阳.高参数火电机蒸汽管道高温完整性研究进展[J].华东交通大学学报,2017,34(6):1-25.
【2】迟成宇,于鸿垚,谢锡善.600℃超超临界电站锅炉过热器及再热器管道用先进奥氏体耐热钢的研究与发展[J].世界钢铁,2012,12(4):50-65.
【3】于鸿,董建新,迟成宇,等.650℃奥氏体耐热钢TP347H组织稳定性的研究[J].材料科学,2011,1(1):15-24.
【4】张健,王波,杨平,等.深度调峰机组TP347H高温过热器管的超温老化[J].材料热处理学报,2023,44(1):137-145.
【5】张骏,郑准备,杨占君,等.TP347H锅炉钢管失效机理研究进展[J].机械工程材料,2021,45(2):7-14.
【6】杨宏辉.TP304H,TP347H钢的材料特性与金属监督[J].湖南电力,2000,20(6):51-52.
【7】ISEDA A,OKADA H,SEMBA H,et al.Long term creep properties and microstructure of SUPER304H,TP347HFG and HR3C for A-USC boilers[J].Energy Materials,2007,2(4):199-206.
【8】王伟,王志武,李文胜,等.不同Cr、Ni含量下TP347H钢的热力学平衡相[J].金属热处理,2016,41(10):99-101.
【9】MIAO K,HE Y L,ZHU N Q,et al.Coarsening of carbides during different heat treatment conditions[J].Journal of Alloys and Compounds,2015,622:513-523.
【10】郑坊平,张红军,高磊,等.TP347H奥氏体不锈钢锅炉管开裂原因分析[J].热加工工艺,2014,43(21):225-228.
【11】张志强,安冬冬,曲同良,等.大型火电机组过热器爆管原因分析[J].山东电力技术,2021,48(10):75-80.
【12】林志福,林琳,高磊.屏式过热器管泄漏原因分析[J].电力设备管理,2018(7):75-80.
【13】刘杰,赵永峰,刘翔,等.600 MW超临界锅炉TP347H高温过热器管爆管的显微分析[J].热加工工艺,2020,49(2):159-162.
【14】郝维勋,徐世斌,张嘉琳.电厂高温再热器SA-213 TP347H钢管开裂原因分析[J].黑龙江电力,2018,40(2):181-184.
【2】迟成宇,于鸿垚,谢锡善.600℃超超临界电站锅炉过热器及再热器管道用先进奥氏体耐热钢的研究与发展[J].世界钢铁,2012,12(4):50-65.
【3】于鸿,董建新,迟成宇,等.650℃奥氏体耐热钢TP347H组织稳定性的研究[J].材料科学,2011,1(1):15-24.
【4】张健,王波,杨平,等.深度调峰机组TP347H高温过热器管的超温老化[J].材料热处理学报,2023,44(1):137-145.
【5】张骏,郑准备,杨占君,等.TP347H锅炉钢管失效机理研究进展[J].机械工程材料,2021,45(2):7-14.
【6】杨宏辉.TP304H,TP347H钢的材料特性与金属监督[J].湖南电力,2000,20(6):51-52.
【7】ISEDA A,OKADA H,SEMBA H,et al.Long term creep properties and microstructure of SUPER304H,TP347HFG and HR3C for A-USC boilers[J].Energy Materials,2007,2(4):199-206.
【8】王伟,王志武,李文胜,等.不同Cr、Ni含量下TP347H钢的热力学平衡相[J].金属热处理,2016,41(10):99-101.
【9】MIAO K,HE Y L,ZHU N Q,et al.Coarsening of carbides during different heat treatment conditions[J].Journal of Alloys and Compounds,2015,622:513-523.
【10】郑坊平,张红军,高磊,等.TP347H奥氏体不锈钢锅炉管开裂原因分析[J].热加工工艺,2014,43(21):225-228.
【11】张志强,安冬冬,曲同良,等.大型火电机组过热器爆管原因分析[J].山东电力技术,2021,48(10):75-80.
【12】林志福,林琳,高磊.屏式过热器管泄漏原因分析[J].电力设备管理,2018(7):75-80.
【13】刘杰,赵永峰,刘翔,等.600 MW超临界锅炉TP347H高温过热器管爆管的显微分析[J].热加工工艺,2020,49(2):159-162.
【14】郝维勋,徐世斌,张嘉琳.电厂高温再热器SA-213 TP347H钢管开裂原因分析[J].黑龙江电力,2018,40(2):181-184.
相关信息