大牛地气田某输气管道内腐蚀的原因
Causes of Internal Corrosion of a Gas Pipeline in Daniudi Gas Field
摘 要
采用扫描电镜(SEM)、能谱仪(EDS)、X射线衍射仪(XRD)对大牛地气田某集气站外输管道内腐蚀的原因进行分析。结果表明:固态与液态腐蚀产物均呈疏松多孔结构,对金属基体的保护作用较差;腐蚀产物的主要元素为Fe、O、S、C,其中C和S元素含量超标, 腐蚀产物主要由FeS、FeCO3、Fe2O3和Fe3O4组成;输气管道内发生了H2S、CO2的协同腐蚀,H2S、CO2溶解于管道内沉积的凝析水后,与金属基体发生腐蚀反应,腐蚀形式主要为局部腐蚀。
腐蚀机理
局部腐蚀
腐蚀产物
pipeline internal corrosion
corrosion mechanism
localized corrosion
corrosion product
Abstract
The causes of internal corrosion of the external pipeline of a gas gathering station in Daniudi gas field were analyzed by scanning electron microscope (SEM), energy dispersive spectrometer (EDS) and X-ray diffractometer (XRD). The results showed that the solid and liquid corrosion products was loose and porous structures, and the protective effect on metal matrix was poor. The main elements of the corrosion products were Fe, O, S and C, and the contents of C and S elements exceeded the standard. The corrosion products were mainly composed of FeS, FeCO3, Fe2O3 and Fe3O4. The synergistic corrosion of H2S and CO2 occurred in the gas pipeline. H2S and CO2 dissolved in the condensate water deposited in the pipeline and reacted with the metal matrix. The main corrosion form was localized corrosion.
中图分类号 TG172 DOI 10.11973/fsyfh-202309005
所属栏目 油气工业腐蚀与防护
基金项目
收稿日期 2022/12/29
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: HAN Jielin,ZHOU Jun,LIU Yuelong,PENG Sizhou,LIU Shitao,XIONG Zihao. Causes of Internal Corrosion of a Gas Pipeline in Daniudi Gas Field[J]. Corrosion & Protection, 2023, 44(9): 32
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】石钻. 大牛地奥陶系风化壳天然气开发获突破[J]. 石油钻探技术,2015,43(4):132.
【2】谢飞,李佳航,王国付,等. 天然气管道内腐蚀直接评价方法的改进[J]. 油气储运,2022,41(2):219-226.
【3】解树旺,张振华,赵杉林. 硫化氢腐蚀产物氧化历程的研究[J]. 应用化工,2015,44(7):1190-1193,1197.
【4】鲍明昱,熊建嘉,崔铭芳,等. 某单井站场管道积液及腐蚀特性研究[J]. 中国安全生产科学技术,2021,17(7):60-64.
【5】BERNARDUS F,KAPUSTA S,WHITHAM T,et al. Improvements on de Waard-Milliams Corrosion Prediction and Applications to Corrosion Management[C]//Corrosion 2002. Houston,Texas:NACE International,2002.
【6】李彦鹏,朱世东,李金灵,等. 油气管道H2S/CO2腐蚀与防护技术研究进展[J]. 腐蚀与防护,2022,43(6):1-6,12.
【7】王帆,李娟,李金灵,等. 金属管道在CO2/H2S环境中的腐蚀行为[J]. 热加工工艺,2021,50(4):1-7.
【8】李玲杰,杜宁波,崔健军,等. 长庆油田某采油厂集输管道内腐蚀原因及腐蚀机理[J]. 腐蚀与防护,2020,41(2):69-73,77.
【9】王小红,李子硕,唐御峰,等. CO2-H2S-Cl-共存的地层水环境中Cr含量对钢的腐蚀产物膜特性的影响[J]. 中国腐蚀与防护学报,2022,42(6):1043-1050.
【10】罗立辉,牛大宇,宋鹏迪,等. L290输油管道腐蚀穿孔失效分析[J]. 热加工工艺,2023(18):139-142.
【11】杨全毅,张朝阳,王永虎,等. 管线钢在酸性环境中的腐蚀行为[J]. 腐蚀与防护,2022,43(10):33-37.
【12】姚彬,高秋英,张超,等. X80管线钢焊接接头的组织对其超临界CO2腐蚀行为的影响[J]. 腐蚀与防护,2022,43(8):36-41.
【13】郭克星. 油气管道用钢材料的局部腐蚀研究进展[J]. 石油化工腐蚀与防护,2023,40(1):29-34.
【14】王艳飞. L360钢在H2S-CO2-Cl-体系中元素硫沉积下的点蚀机理[D]. 西安:西安石油大学,2021.
【2】谢飞,李佳航,王国付,等. 天然气管道内腐蚀直接评价方法的改进[J]. 油气储运,2022,41(2):219-226.
【3】解树旺,张振华,赵杉林. 硫化氢腐蚀产物氧化历程的研究[J]. 应用化工,2015,44(7):1190-1193,1197.
【4】鲍明昱,熊建嘉,崔铭芳,等. 某单井站场管道积液及腐蚀特性研究[J]. 中国安全生产科学技术,2021,17(7):60-64.
【5】BERNARDUS F,KAPUSTA S,WHITHAM T,et al. Improvements on de Waard-Milliams Corrosion Prediction and Applications to Corrosion Management[C]//Corrosion 2002. Houston,Texas:NACE International,2002.
【6】李彦鹏,朱世东,李金灵,等. 油气管道H2S/CO2腐蚀与防护技术研究进展[J]. 腐蚀与防护,2022,43(6):1-6,12.
【7】王帆,李娟,李金灵,等. 金属管道在CO2/H2S环境中的腐蚀行为[J]. 热加工工艺,2021,50(4):1-7.
【8】李玲杰,杜宁波,崔健军,等. 长庆油田某采油厂集输管道内腐蚀原因及腐蚀机理[J]. 腐蚀与防护,2020,41(2):69-73,77.
【9】王小红,李子硕,唐御峰,等. CO2-H2S-Cl-共存的地层水环境中Cr含量对钢的腐蚀产物膜特性的影响[J]. 中国腐蚀与防护学报,2022,42(6):1043-1050.
【10】罗立辉,牛大宇,宋鹏迪,等. L290输油管道腐蚀穿孔失效分析[J]. 热加工工艺,2023(18):139-142.
【11】杨全毅,张朝阳,王永虎,等. 管线钢在酸性环境中的腐蚀行为[J]. 腐蚀与防护,2022,43(10):33-37.
【12】姚彬,高秋英,张超,等. X80管线钢焊接接头的组织对其超临界CO2腐蚀行为的影响[J]. 腐蚀与防护,2022,43(8):36-41.
【13】郭克星. 油气管道用钢材料的局部腐蚀研究进展[J]. 石油化工腐蚀与防护,2023,40(1):29-34.
【14】王艳飞. L360钢在H2S-CO2-Cl-体系中元素硫沉积下的点蚀机理[D]. 西安:西安石油大学,2021.
相关信息