X80钢铜衬垫自动焊外根焊接头的组织与性能
Microstructure and Properties of X80 Steel Joint by Copper Liner Automatic External Root Welding
摘 要
采用铜衬垫自动焊外根焊工艺对X80钢进行焊接，研究了焊缝成形质量以及粘铜区域和未粘铜区域的铜含量、显微组织及力学性能。结果表明：焊缝成形良好，未发现裂纹、未熔合等缺陷。未粘铜区域的铜含量与母材一致，粘铜区域的铜质量分数约为0.46%，渗铜深度约为0.18 mm；未粘铜区域焊缝组织主要由针状铁素体和少量的先共析铁素体组成，粘铜区域则主要是块状铁素体、粒状贝氏体以及游离铜组成。未粘铜区域和粘铜区域硬度变化趋势基本一致，焊缝根部粘铜区域的硬度略高于未粘铜区域；粘铜区域和未粘铜区域的抗拉强度分别为730，732 MPa，冲击性能基本一致，弯曲试验后均未见裂纹。焊缝根部渗铜未对接头的力学性能产生明显影响。
铜衬垫自动焊外根焊
渗铜
力学性能
显微组织
X80 steel
copper liner automatic external root welding
copper infiltration
mechanical property
microstructure
Abstract
X80 steel was welded by copper liner automatic external root welding.The quality of weld formation and the copper content, microstructure and mechanical properties of the copper bonded and non-copper bonded areas were studied. The results show that the weld was well formed and no defects such as cracks or incomplete fusion were found. The copper content in the non-copper bonded area was consistent with the base metal. The copper mass fraction of the copper bonded area was about 0.46%, and the copper infiltration depth was about 0.18 mm. The microstructure of the weld in the non-copper bonded area was mainly composed of acicular ferrite and a small amount of pre-eutectoid ferrite, while that of the copper bonded area was mainly composed of block ferrite, granular bainite, and free copper. The hardness variation trend of the non-copper bonded area and the copper bonded area was basically the same. The hardness of the copper bonded area of weld root was slightly higher than that of the non-copper bonded area. The tensile strength of the copper bonded area and the non-copper bonded area was 730, 732 MPa, respectively. The impact properties of the two areas were basically the same, and no cracks were found after bending test. The copper infiltration at the root of the weld had no obvious effect on the mechanical properties of the joint.
中图分类号 TE973.8 DOI 10.11973/jxgccl202309011
所属栏目 材料性能及应用
基金项目
收稿日期 2023/3/4
修改稿日期 2023/8/2
网络出版日期
作者单位点击查看
备注杨天冰(1974-),男,黑龙江青冈人,工程师,硕士
引用该论文: YANG Tianbing,LI Dan. Microstructure and Properties of X80 Steel Joint by Copper Liner Automatic External Root Welding[J]. Materials for mechancial engineering, 2023, 47(9): 65～69
杨天冰,李丹. X80钢铜衬垫自动焊外根焊接头的组织与性能[J]. 机械工程材料, 2023, 47(9): 65～69
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】LI G Q, LYU H B, ZHANG C.Post-fire mechanical properties of high strength Q690 structural steel[J].Journal of Constructional Steel Research, 2017, 132:108-116.
【2】WAN X L, WU K M, NUNE K C, et al.In situ observation of acicular ferrite formation and grain refinement in simulated heat affected zone of high strength low alloy steel[J].Science and Technology of Welding and Joining, 2015, 20(3):254-263.
【3】ZHAO L P, ZHANG H M, LIU W, et al.Effect of different tempering processes on microstructure and hardness of Q690 steel[J].Advanced Materials Research, 2013, 721:49-53.
【4】LIU C J, CHEN X D, CHEN T, et al.Phase transformation of Nb in carburized zone of 25Cr35NiNb+MA alloy after service[J].Procedia Engineering, 2015, 130:693-700.
【5】ALVINO A, LEGA D, GIACOBBE F, et al.Damage characterization in two reformer heater tubes after nearly 10 years of service at different operative and maintenance conditions[J].Engineering Failure Analysis, 2010, 17(7/8):1526-1541.
【6】LIU C J, CHEN Y.Variations of the microstructure and mechanical properties of HP40Nb hydrogen reformer tube with time at elevated temperature[J].Materials & Design, 2011, 32(4):2507-2512.
【7】常丽艳, 宋西平, 李宏良, 等.7075铝合金激光-MIG复合焊接接头组织及性能的分析[J].热加工工艺, 2014, 43(9):25-28. CHANG L Y, SONG X P, LI H L, et al.Microstructure and mechanical properties of laser-MIG hybrid welded joint of 7075-T6 aluminum alloy[J].Hot Working Technology, 2014, 43(9):25-28.
【8】贾晨程, 周弋琳, 张华军, 等.LNG储罐用9Ni低温钢横位置焊条电弧焊和埋弧焊接头微观组织与力学性能对比[J].起重运输机械, 2022(7):80-86. JIA C C, ZHOU Y L, ZHANG H J, et al.Comparison of microstructure and mechanical properties of transverse shielded metal arc welding and submerged arc welding joints of 9Ni low temperature steel for LNG storage tank[J].Hoisting and Conveying Machinery, 2022(7):80-86.
【9】王光大.BWELDY700QL4低合金高强钢焊接接头组织与力学性能研究[D].大连:大连交通大学, 2012. WANG G D.Study on microstructure and mechanical properties of welded joint of BWELDY700QL4 low alloy high strength steel[D].Dalian:Dalian Jiaotong University, 2012.
【10】车焕文, 姚军.回火温度对9Cr0.11V钢TIG焊缝组织与力学性能的影响[J].铸造技术, 2017, 38(10):2383-2385. CHE H W, YAO J.Effect of tempering temperature on microstructure and mechanical properties of 9Cr0.11V steel welding line by TIG[J].Foundry Technology, 2017, 38(10):2383-2385.
【11】文学, 汪宏辉, 钱建康, 等.X80M管线钢铜衬垫外根焊接头冷裂敏感性分析[J].焊接学报, 2022, 43(12):105-112. WEN X, WANG H H, QIAN J K, et al.Cold crack susceptibility analysis of the copper backing outside root welding joints of X80M pipeline steel[J].Transactions of the China Welding Institution, 2022, 43(12):105-112.
【12】汪宏辉, 雷正龙, 杨雨禾, 等.X70钢管道采用铜衬垫根焊的焊接接头疲劳性能[J].焊接学报, 2015, 36(10):100-104. WANG H H, LEI Z L, YANG Y H, et al.Fatigue property of X70 steel pipeline girth welding joint with copper back-up shoes root welding[J].Transactions of the China Welding Institution, 2015, 36(10):100-104.
【13】马才女.轧制及时效工艺对含铜钢显微组织演变与力学行为的影响[D].包头:内蒙古科技大学, 2022. MA C N.Effect of rolling and aging process on microstructure evolution and mechanical behavior of copper-containing steel[D].Baotou:Inner Mongolia University of Science & Technology, 2022.
【2】WAN X L, WU K M, NUNE K C, et al.In situ observation of acicular ferrite formation and grain refinement in simulated heat affected zone of high strength low alloy steel[J].Science and Technology of Welding and Joining, 2015, 20(3):254-263.
【3】ZHAO L P, ZHANG H M, LIU W, et al.Effect of different tempering processes on microstructure and hardness of Q690 steel[J].Advanced Materials Research, 2013, 721:49-53.
【4】LIU C J, CHEN X D, CHEN T, et al.Phase transformation of Nb in carburized zone of 25Cr35NiNb+MA alloy after service[J].Procedia Engineering, 2015, 130:693-700.
【5】ALVINO A, LEGA D, GIACOBBE F, et al.Damage characterization in two reformer heater tubes after nearly 10 years of service at different operative and maintenance conditions[J].Engineering Failure Analysis, 2010, 17(7/8):1526-1541.
【6】LIU C J, CHEN Y.Variations of the microstructure and mechanical properties of HP40Nb hydrogen reformer tube with time at elevated temperature[J].Materials & Design, 2011, 32(4):2507-2512.
【7】常丽艳, 宋西平, 李宏良, 等.7075铝合金激光-MIG复合焊接接头组织及性能的分析[J].热加工工艺, 2014, 43(9):25-28. CHANG L Y, SONG X P, LI H L, et al.Microstructure and mechanical properties of laser-MIG hybrid welded joint of 7075-T6 aluminum alloy[J].Hot Working Technology, 2014, 43(9):25-28.
【8】贾晨程, 周弋琳, 张华军, 等.LNG储罐用9Ni低温钢横位置焊条电弧焊和埋弧焊接头微观组织与力学性能对比[J].起重运输机械, 2022(7):80-86. JIA C C, ZHOU Y L, ZHANG H J, et al.Comparison of microstructure and mechanical properties of transverse shielded metal arc welding and submerged arc welding joints of 9Ni low temperature steel for LNG storage tank[J].Hoisting and Conveying Machinery, 2022(7):80-86.
【9】王光大.BWELDY700QL4低合金高强钢焊接接头组织与力学性能研究[D].大连:大连交通大学, 2012. WANG G D.Study on microstructure and mechanical properties of welded joint of BWELDY700QL4 low alloy high strength steel[D].Dalian:Dalian Jiaotong University, 2012.
【10】车焕文, 姚军.回火温度对9Cr0.11V钢TIG焊缝组织与力学性能的影响[J].铸造技术, 2017, 38(10):2383-2385. CHE H W, YAO J.Effect of tempering temperature on microstructure and mechanical properties of 9Cr0.11V steel welding line by TIG[J].Foundry Technology, 2017, 38(10):2383-2385.
【11】文学, 汪宏辉, 钱建康, 等.X80M管线钢铜衬垫外根焊接头冷裂敏感性分析[J].焊接学报, 2022, 43(12):105-112. WEN X, WANG H H, QIAN J K, et al.Cold crack susceptibility analysis of the copper backing outside root welding joints of X80M pipeline steel[J].Transactions of the China Welding Institution, 2022, 43(12):105-112.
【12】汪宏辉, 雷正龙, 杨雨禾, 等.X70钢管道采用铜衬垫根焊的焊接接头疲劳性能[J].焊接学报, 2015, 36(10):100-104. WANG H H, LEI Z L, YANG Y H, et al.Fatigue property of X70 steel pipeline girth welding joint with copper back-up shoes root welding[J].Transactions of the China Welding Institution, 2015, 36(10):100-104.
【13】马才女.轧制及时效工艺对含铜钢显微组织演变与力学行为的影响[D].包头:内蒙古科技大学, 2022. MA C N.Effect of rolling and aging process on microstructure evolution and mechanical behavior of copper-containing steel[D].Baotou:Inner Mongolia University of Science & Technology, 2022.
相关信息