油井套管腐蚀原因分析与防腐蚀措施的效果评价
Corrosion Cause Analysis of Oil Well Casing and Effect Evaluation ofCorrosion Protection Measures
摘 要
在对某油田套损井工况调研的基础上,通过采出水成分、腐蚀产物成分等分析,明确了套管内、外腐蚀环境及腐蚀原因。通过化学成分分析及模拟工况环境的腐蚀速率测试评价了在用套管材料的耐蚀性;通过有限元模拟方法计算得到套管内置和外置牺牲阳极在不同环境中的有效保护距离;通过释放率和缓蚀率测试评价了在用固体缓蚀剂的缓蚀性能。最后根据评价结果对防腐蚀措施提出了改进建议。
腐蚀原因
防腐蚀效果
改进措施
oil well casing
corrosion cause
corrosion protection effect
improvement measure
Abstract
Based on the investigation of casing damage wells in an oilfield, the internal and external corrosion environment and corrosion reasons of the casing were clarified by analyzing the composition of produced water and corrosion products. The corrosion resistance of the casing material in use was evaluated by chemical composition analysis and corrosion rate test under simulated working conditions. The effective protection distances of built-in and external sacrificial anodes for casing in different environments were calculated by finite element simulation method. The corrosion inhibition performance of the solid corrosion inhibitor in use was evaluated by the release rate and inhibition rate test. Finally, some improvement suggestions for corrosion protection measures were put forward according to the evaluation results.
中图分类号 TG174. 1 DOI 10.11973/fsyfh-202311016
所属栏目 应用技术
基金项目
收稿日期 2022/4/23
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHAO Kaifeng,CHEN Zuoming,XU Jianguo,SUN Xiaoguang,ZHANG Xinxin,LYU Xianghong,DENG Jingyu,WANG Chen,LIAN Yujiang,LI Ning. Corrosion Cause Analysis of Oil Well Casing and Effect Evaluation ofCorrosion Protection Measures[J]. Corrosion & Protection, 2023, 44(11): 86
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】周妍, 李震,甘宁,等.长庆油田套损井综合防治技术[J].测井技术,2021,45(2):196-200.
【2】向蓉, 王飞,徐杰斌.套损井原因分析及治理对策[J].西部探矿工程,2012,24(6):120-124.
【3】董志刚, 张雪珍,丁欣.油套管腐蚀影响因素与防腐蚀技术研究[J].设备管理与维修,2021(14):115-116.
【4】王尚卫, 魏磊,杨焕英.长庆油田镇340区块油井套管腐蚀机理[J].长江大学学报(自然科学版),2020,17(3):56-60,7.
【5】LIU Q Y,MAO L J,ZHOU S W.Effects of chloride content on CO2 corrosion of carbon steel in simulated oil and gas well environments[J].Corrosion Science,2014,84:165-171.
【6】吕祥鸿, 闫亚丽,王悦.某区块油井套管腐蚀破坏机理及防护措施研究[J].焊管,2019,42(1):10-16.
【7】张凤奎, 张林,周志平,等.陇东地区油田套管腐蚀破损与洛河组沉积相的关系研究[J].中国地质,2007,34(3):450-454.
【8】付彩利, 程碧海,董晓焕,等.长庆油田油水井套管防腐工艺实施效果与分析[J].山东化工,2016,45(17):88-90.
【9】王林平, 陆梅,杨全安,等.长庆油田油水井套管防腐技术综述[J].中国石油和化工,2007(8):45-48.
【10】吴明, 宗月,谢飞,等.模拟海水中Cl-浓度对Q235和X70管线钢腐蚀行为的影响[J].金属热处理,2017,42(2):62-66.
【11】耿玉广, 张伟,刘云,等.油井管杆腐蚀结垢原因分析及防治技术[J].腐蚀科学与防护技术,2015,27(3):305-309.
【12】黄廷林, 赵建伟,李仲恺,等.陇东油田采出水系统的腐蚀及防护[J].西安建筑科技大学学报(自然科学版),2002,34(4):320-324.
【13】邢希金, 武治强,吴晓冬,等.A2井表层套管腐蚀机理分析与防护对策[J].表面技术,2018,47(12):30-36.
【14】孙建波, 柳伟,路民旭.成分和组织影响钢CO2腐蚀的研究进展[J].中国腐蚀与防护学报,2008,28(4):246-250.
【15】MORA-MENDOZA J L,TURGOOSE S.Fe3C influence on the corrosion rate of mild steel in aqueous CO2 systems under turbulent flow conditions[J].Corrosion Science,2002,44(6):1223-1246.
【2】向蓉, 王飞,徐杰斌.套损井原因分析及治理对策[J].西部探矿工程,2012,24(6):120-124.
【3】董志刚, 张雪珍,丁欣.油套管腐蚀影响因素与防腐蚀技术研究[J].设备管理与维修,2021(14):115-116.
【4】王尚卫, 魏磊,杨焕英.长庆油田镇340区块油井套管腐蚀机理[J].长江大学学报(自然科学版),2020,17(3):56-60,7.
【5】LIU Q Y,MAO L J,ZHOU S W.Effects of chloride content on CO2 corrosion of carbon steel in simulated oil and gas well environments[J].Corrosion Science,2014,84:165-171.
【6】吕祥鸿, 闫亚丽,王悦.某区块油井套管腐蚀破坏机理及防护措施研究[J].焊管,2019,42(1):10-16.
【7】张凤奎, 张林,周志平,等.陇东地区油田套管腐蚀破损与洛河组沉积相的关系研究[J].中国地质,2007,34(3):450-454.
【8】付彩利, 程碧海,董晓焕,等.长庆油田油水井套管防腐工艺实施效果与分析[J].山东化工,2016,45(17):88-90.
【9】王林平, 陆梅,杨全安,等.长庆油田油水井套管防腐技术综述[J].中国石油和化工,2007(8):45-48.
【10】吴明, 宗月,谢飞,等.模拟海水中Cl-浓度对Q235和X70管线钢腐蚀行为的影响[J].金属热处理,2017,42(2):62-66.
【11】耿玉广, 张伟,刘云,等.油井管杆腐蚀结垢原因分析及防治技术[J].腐蚀科学与防护技术,2015,27(3):305-309.
【12】黄廷林, 赵建伟,李仲恺,等.陇东油田采出水系统的腐蚀及防护[J].西安建筑科技大学学报(自然科学版),2002,34(4):320-324.
【13】邢希金, 武治强,吴晓冬,等.A2井表层套管腐蚀机理分析与防护对策[J].表面技术,2018,47(12):30-36.
【14】孙建波, 柳伟,路民旭.成分和组织影响钢CO2腐蚀的研究进展[J].中国腐蚀与防护学报,2008,28(4):246-250.
【15】MORA-MENDOZA J L,TURGOOSE S.Fe3C influence on the corrosion rate of mild steel in aqueous CO2 systems under turbulent flow conditions[J].Corrosion Science,2002,44(6):1223-1246.
相关信息