摘 要
对C110无缝钢管进行调质处理,研究了调质次数对C110钢组织和摩擦磨损行为的影响。结果表明:随着调质次数的增加,C110钢晶粒发生细化,但细化效果越来越不明显,且材料中第二相不断聚集、长大;在晶粒度和第二相的共同影响下,C110钢的硬度随着调质次数的增加呈先升高后降低的趋势;经二次调质处理后,C110钢的晶粒细化明显,细晶强化效果显著,而第二相长大不明显,材料的耐磨性能最好。
调质处理
晶粒细化
摩擦磨损行为
耐磨性能
C110 steel
quenching and tempering treatment
grain refinement
friction and wear behavior
wear resistance
Abstract
The effect of quenching and tempering times on the microstructure and friction and wear behavior of C110 seamless steel pipe was studied. The results show that with the increased of quenching and tempering times, the grain size of C110 steel was refined, but the refinement effect was becoming less and less obvious, and the second phase in the material continued to aggregate and grow. Under the joint influence of grain size and second phase, the hardness of C110 steel showed a trend of first increasing and then decreasing with the increased of quenching and tempering times. After secondary quenching and tempering treatment, the grain refinement and fine grain strengthening effect of C110 steel were significant, while the growth of the second phase was not significant, indicated the best wear resistance of the material.
中图分类号 TG142. 41 TB31 DOI 10. 11973/lhjy-wl202311007
所属栏目 试验与研究
基金项目 湖南省科技厅重点研发计划项目(2020GK2049);衡阳市科技计划项目(202002071982)
收稿日期 2023/1/9
修改稿日期
网络出版日期
作者单位点击查看
备注赵映辉(1981-),女,高级工程师,主要从事油气用管产品的设计开发及失效分析工作,28604751@qq.com
引用该论文: ZHAO Yinghui,SUN Qunfeng,LIU Chao,LIU Anmin. The effect of multiple quenching and tempering on the structure and friction and wear behavior of C110 steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(11): 23～27
赵映辉,孙群峰,刘超,刘安民. 多次调质对C110钢组织和摩擦磨损行为的影响[J]. 理化检验－物理分册, 2023, 59(11): 23～27
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】康娅娟,刘少军.深海采矿提升系统研究综述[J].机械工程学报,2021,57(20):232-243.
【2】邹伟生,李浩天,康娅娟.深海开采矿浆泵水力管道提升理论与设计[J].中国有色金属学报,2021,31(10):2953-2962.
【3】IUNGEMEISTER D A,KOROLEV R I,SERZHAN S L,et al.Materials of devices and equipment for deep-sea mining of manganese resources[J].Journal of Physics:Conference Series,2020,1582(1):012098.
【4】MENDIBIDE C,DURET-THUAL C.Formation of microgrooving on C110 casing steel after sulfide stress cracking test[J].Corrosion,2021,77(4):433-444.
【5】方剑,黄彦,唐应波.C110抗腐蚀套管的热处理工艺及性能[J].金属热处理,2018,43(12):174-178.
【6】田昊,潘学福,巨彪,等.轧制工艺对管线钢耐磨性的影响[J].热加工工艺,2014,43(23):50-53.
【7】姜金星,于新攀,潘学福,等.碳、铬、钼元素对X70管线钢显微组织与性能的影响[J].机械工程材料,2018,42(7):37-40.
【8】张季惠,唐林虎.油气管道X80管线钢的干式滑动摩擦磨损特性研究[J].化工机械,2017,44(6):633-637.
【9】OKONKWO P C,SHAKOOR R A,AHMED E,et al.Erosive wear performance of API X42 pipeline steel[J].Engineering Failure Analysis,2016,60:86-95.
【10】徐钢新,陈亮,李勃,等.多次调质对42CrMo钢组织和力学性能的影响[J].金属热处理,2014,39(5):112-114.
【11】陈亮,徐钢新.多次调质对980钢组织和力学性能的影响[J].金属热处理,2015,40(5):121-123.
【2】邹伟生,李浩天,康娅娟.深海开采矿浆泵水力管道提升理论与设计[J].中国有色金属学报,2021,31(10):2953-2962.
【3】IUNGEMEISTER D A,KOROLEV R I,SERZHAN S L,et al.Materials of devices and equipment for deep-sea mining of manganese resources[J].Journal of Physics:Conference Series,2020,1582(1):012098.
【4】MENDIBIDE C,DURET-THUAL C.Formation of microgrooving on C110 casing steel after sulfide stress cracking test[J].Corrosion,2021,77(4):433-444.
【5】方剑,黄彦,唐应波.C110抗腐蚀套管的热处理工艺及性能[J].金属热处理,2018,43(12):174-178.
【6】田昊,潘学福,巨彪,等.轧制工艺对管线钢耐磨性的影响[J].热加工工艺,2014,43(23):50-53.
【7】姜金星,于新攀,潘学福,等.碳、铬、钼元素对X70管线钢显微组织与性能的影响[J].机械工程材料,2018,42(7):37-40.
【8】张季惠,唐林虎.油气管道X80管线钢的干式滑动摩擦磨损特性研究[J].化工机械,2017,44(6):633-637.
【9】OKONKWO P C,SHAKOOR R A,AHMED E,et al.Erosive wear performance of API X42 pipeline steel[J].Engineering Failure Analysis,2016,60:86-95.
【10】徐钢新,陈亮,李勃,等.多次调质对42CrMo钢组织和力学性能的影响[J].金属热处理,2014,39(5):112-114.
【11】陈亮,徐钢新.多次调质对980钢组织和力学性能的影响[J].金属热处理,2015,40(5):121-123.
相关信息