Causes of deformation of polyamide insulation adhesive for aluminum alloy windows
摘 要
在某穿条式隔热铝合金建筑型材的生产过程中,其聚酰胺隔热胶在复合部位发生变形。采用组分分析、微观分析、差式扫描量热分析、力学性能测试、红外光谱分析等方法分析了聚酰胺隔热胶变形的原因。结果表明:短碎的玻璃纤维与树脂的结合作用力较小;材料的成型温度不足、结晶程度低、熔融峰对应温度偏低使材料的力学性能变差,最终导致聚酰胺隔热胶变形。
Abstract
During the production of threaded insulation aluminum alloy building profiles, the polyamide insulation adhesive deformed in the composite part. The causes of deformation of polyamide insulation adhesive were analyzed by component analysis, microscopic analysis, differential scanning calorimetry analysis, mechanical property testing, and infrared spectroscopy analysis. The results show that the binding force between short and fragmented glass fibers and resin was low. The insufficient molding temperature, low crystallinity and low temperature corresponded to the melting peak made the mechanical properties of the material worse, ultimately led to deformation of the polyamide insulation adhesive.
中图分类号 TB31 TG115. 2 DOI 10. 11973/lhjy-wl202311010
所属栏目 质量控制与失效分析
基金项目
收稿日期 2023/2/21
修改稿日期
网络出版日期
作者单位点击查看
备注钟国生(1985-),男,硕士,工程师,主要从事金属材料测试工作,87030518@qq.com
引用该论文: ZHONG Guosheng,HUANG Jianzhen,LI Zhijing. Causes of deformation of polyamide insulation adhesive for aluminum alloy windows[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(11): 35~37
钟国生,黄间珍,李志劲. 铝合金窗用聚酰胺隔热胶变形原因[J]. 理化检验-物理分册, 2023, 59(11): 35~37
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘建伟,王召青,田国锋,等.增韧尼龙612/尼龙6合金的性能[J].工程塑料应用,2019,47(1):15-19.
【2】谭支林,汪艳.尼龙12/氧化石墨烯纳米复合粉末的制备及性能[J].工程塑料应用,2018,46(5):93-97.
【3】华阳,刘振明,刘权毅,等.尼龙66国内外生产现状及发展建议[J].弹性体,2010,20(6):78-82.
【4】桂源,邓建平,李玉才,等.重复挤出对聚酰胺热塑性弹性体性能的影响[J].现代塑料加工应用,2022,34(4):12-15.
【5】GERETSCHLÄGER K J,WALLNER G M.Aging characteristics of glass fiber-reinforced polyamide in hot water and air[J].Polymer Composites,2018,39(4):997-1005.
【6】张豫坤,牛宏校,邓晨兴.碳纤维增强热塑性树脂基复合材料的力学性能研究[J].当代化工研究,2017(6):66-67.
【2】谭支林,汪艳.尼龙12/氧化石墨烯纳米复合粉末的制备及性能[J].工程塑料应用,2018,46(5):93-97.
【3】华阳,刘振明,刘权毅,等.尼龙66国内外生产现状及发展建议[J].弹性体,2010,20(6):78-82.
【4】桂源,邓建平,李玉才,等.重复挤出对聚酰胺热塑性弹性体性能的影响[J].现代塑料加工应用,2022,34(4):12-15.
【5】GERETSCHLÄGER K J,WALLNER G M.Aging characteristics of glass fiber-reinforced polyamide in hot water and air[J].Polymer Composites,2018,39(4):997-1005.
【6】张豫坤,牛宏校,邓晨兴.碳纤维增强热塑性树脂基复合材料的力学性能研究[J].当代化工研究,2017(6):66-67.
相关信息