离合器减振弹簧断裂原因
Causes of clutch damping spring fracture
摘 要
某型号离合器从动盘总成在扭转耐久性试验过程中,其减振弹簧发生断裂。采用宏观观察、化学成分分析、硬度测试、金相检验、扫描电镜及能谱分析等方法研究了该弹簧断裂的原因。结果表明:减振弹簧内侧存在原始裂纹和摩擦损伤,使弹簧在低应力作用下发生弯曲疲劳断裂。
扭转耐久试验
摩擦损伤
疲劳断裂
damping spring
torsional durability test
friction damage
fatigue fracture
Abstract
During the torsion durability test of a certain type of clutch driven plate assembly, its damping spring fractured. The reasons for the fracture of the spring were studied by macroscopic observation, chemical composition analysis, hardness testing, metallographic examination, scanning electron microscopy and energy spectrum analysis. The results show that there were original cracks and friction damage on the inner side of the damping spring which caused the spring to bend fatigue fracture under low stress.
中图分类号 TB31 TG115. 2 DOI 10. 11973/lhjy-wl202311017
所属栏目 质量控制与失效分析
基金项目 广西自然科学基金项目(2021GXNSFBA196038);广西科技计划项目(桂科AD22035116);中国博士后科学基金项目(2022M710920)
收稿日期 2023/1/4
修改稿日期
网络出版日期
作者单位点击查看
备注骆玉城(1990-),男,硕士,工程师,主要从事汽车零部件失效分析、理化检验和曲轴疲劳失效分析等工作
引用该论文: LUO Yucheng,YUE Gao,TIAN Shuangxi,LIN Shengyao. Causes of clutch damping spring fracture[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(11): 62～65
骆玉城,岳高,田双息,林升垚. 离合器减振弹簧断裂原因[J]. 理化检验－物理分册, 2023, 59(11): 62～65
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】于汇泳,周慧琳,胡俊华. 弹簧振动失效断口分析[J]. 机械设计与制造,2013(3):260-261,264.
【2】沈献民,邢献强,肖今春. 扭转弹簧断裂原因分析[J]. 金属制品,2012,38(1):30-33.
【3】薛喜才,邵白明. 汽车悬架弹簧断裂原因分析[J]. 理化检验(物理分册),2020,56(1):66-69.
【4】周绍信,蒙秋红,邓颖章,等. 装载机分配阀弹簧断裂失效原因分析及预防[J]. 工程机械,2012,43(9):32-38.
【2】沈献民,邢献强,肖今春. 扭转弹簧断裂原因分析[J]. 金属制品,2012,38(1):30-33.
【3】薛喜才,邵白明. 汽车悬架弹簧断裂原因分析[J]. 理化检验(物理分册),2020,56(1):66-69.
【4】周绍信,蒙秋红,邓颖章,等. 装载机分配阀弹簧断裂失效原因分析及预防[J]. 工程机械,2012,43(9):32-38.
相关信息