不同工艺热处理后汽车用中锰钢的显微组织与力学性能
Microstructure and Mechanical Properties of Medium Manganese Steel for Automobile after Different Heat Treatments
摘 要
对汽车用中锰钢先分别进行不同温度(150,550,600,750 ℃)预热、750 ℃淬火、-75 ℃深冷处理,再进行逆相变退火处理,研究了不同工艺热处理后的显微组织与力学性能。结果表明:预热处理后中锰钢中的残余奥氏体含量均较铸态高,当预热温度为600 ℃时残余奥氏体体积分数达到最大值42.2%,此时组织为块状/板条状马氏体+残余奥氏体;随着预热温度升高,逆相变退火后中锰钢的抗拉强度增大,断后伸长率和强塑积先增大后减小,当预热温度为600 ℃时,强塑积达到最大值51.99 GPa·%;相较于淬火+逆相变退火,深冷+逆相变退火处理后中锰钢的抗拉强度和屈服强度较小,断后伸长率、强塑积和-40 ℃冲击功较高。
逆相变退火
深冷处理
显微组织
力学性能
medium manganese steel
reverted transformation annealing
cryogenic treatment
microstructure
mechanical property
Abstract
The medium manganese steels for automobile were treated by preheating at different temperatures (150, 550, 600, 750 ℃), quenching at 750 ℃, cryogenic treatment at -75 ℃, respectively, and then were subjected to reverted transformation annealing. The microstructure and mechanical properties after different heat treatments were studied. The results show that the retained austenite content in medium manganese steel after preheating was higher than that in as-cast steel. The volume fraction of the retained austenite reached the maximum value of 42.2% after preheating at 600 ℃, and the microstructure was composed of block/strip martensite and retained austenite. With the increase of preheating temperature, the tensile strength of medium manganese steel after reverted transformation annealing increased, and the elongation after fracture and the product of strength and elongation increased first and then decrease. When the preheating temperature was 600 ℃, the product of strength and elongation reached the maximum value of 51.99 GPa·%. Compared with those after quenching and reverted transformation annealing, the tensile strength and yield strength of the medium manganese steel after cryogenic treatment and reverted transformation annealing were smaller, and the elongation after fracture, the product of strength and elongation and the impact energy at -40 ℃ were higher.
中图分类号 TG142.1 U465.11 DOI 10.11973/jxgccl202310009
所属栏目 新材料 新工艺
基金项目 国家重点研发计划项目(2020YFB0301012-4);山西省重点研发计划项目(2017KKJH)
收稿日期 2022/6/2
修改稿日期 2023/7/4
网络出版日期
作者单位点击查看
备注张丽凤(1980-),女,山西太原人,副教授,硕士
引用该论文: ZHANG Lifeng,WANG Sheze,TIAN Botong. Microstructure and Mechanical Properties of Medium Manganese Steel for Automobile after Different Heat Treatments[J]. Materials for mechancial engineering, 2023, 47(10): 55～61
张丽凤,王社则,田博彤. 不同工艺热处理后汽车用中锰钢的显微组织与力学性能[J]. 机械工程材料, 2023, 47(10): 55～61
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵征志,陈伟健,高鹏飞,等.先进高强度汽车用钢研究进展及展望[J].钢铁研究学报,2020,32(12):1059-1076. ZHAO Z Z,CHEN W J,GAO P F,et al.Progress and perspective of advanced high strength automotive steel[J].Journal of Iron and Steel Research,2020,32(12):1059-1076.
【2】宋仁伯,霍巍丰,周乃鹏,等.Fe-Mn-Al-C系中锰钢的研究现状与发展前景[J].工程科学学报,2020,42(7):814-828. SONG R B,HUO W F,ZHOU N P,et al.Research progress and prospect of Fe-Mn-Al-C medium Mn steels[J].Chinese Journal of Engineering,2020,42(7):814-828.
【3】张丽凤,王社则,田博彤.高强塑积汽车钢板的显微组织与力学性能[J].塑性工程学报,2021,28(11):181-188. ZHANG L F,WANG S Z,TIAN B T.Microstructure and mechanical properties of automobile steel sheet with high strength-ductility balance[J].Journal of Plasticity Engineering,2021,28(11):181-188.
【4】胡斌,屠鑫,王玉,等.中锰钢塑性失稳现象的研究进展及未来研究展望[J].工程科学学报,2020,42(1):48-59. HU B,TU X,WANG Y,et al.Recent progress and future research prospects on the plastic instability of medium-Mn steels:A review[J].Chinese Journal of Engineering,2020,42(1):48-59.
【5】WANG F L,YE X Y,REN S B,et al.Effect of intercritical annealing time on microstructure evolution and mechanical properties of low carbon medium manganese steel subjected to multi-step heat treatment process[J].Materials,2022,15(7):2425.
【6】MA Y.Medium-manganese steels processed by austenite-reverted-transformation annealing for automotive applications[J].Materials Science and Technology,2017,33(15):1713-1727.
【7】WENG Z J,GU K X,WANG K K,et al.The reinforcement role of deep cryogenic treatment on the strength and toughness of alloy structural steel[J].Materials Science and Engineering:A,2020,772:138698.
【8】李康丽,李永志,孙国栋.正火预热处理对42CrMo曲轴钢调质后的组织与性能影响[J].特殊钢,2020,41(4):26-29. LI K L,LI Y Z,SUN G D.Effect of normalizing preheat treatment on structure and properties of 42CrMo forging crankshaft steel after quenching and tempering treatment[J].Special Steel,2020,41(4):26-29.
【9】LIU G,LI B,XU S,et al.Effect of intercritical annealing temperature on multiphase microstructure evolution in ultra-low carbon medium manganese steel[J].Materials Characterization,2021,173:110920.
【10】邵成伟,惠卫军,张永健,等.一种新型高强度高塑性冷轧中锰钢的组织和力学性能[J].金属学报,2019,55(2):191-201. SHAO C W,HUI W J,ZHANG Y J,et al.Microstructure and mechanical properties of a novel cold rolled medium-Mn steel with superior strength and ductility[J].Acta Metallurgica Sinica,2019,55(2):191-201.
【11】YE Q Z,HAN G,XU J P,et al.Effect of a two-step annealing process on deformation-induced transformation mechanisms in cold-rolled medium manganese steel[J].Materials Science and Engineering:A,2022,831:142244.
【12】孙荣民,李国阳,王辉,等.逆相变退火处理Fe-Mn-C中锰钢的组织与性能[J].钢铁,2021,56(6):82-88. SUN R M,LI G Y,WANG H,et al.Microstructure and properties of Fe-Mn-C medium-Mn steel processed by ART-annealing[J].Iron & Steel,2021,56(6):82-88.
【13】WU Z Q,DING H,LI H Y,et al.Microstructural evolution and strain hardening behavior during plastic deformation of Fe-12Mn-8Al-0.8C steel[J].Materials Science and Engineering:A,2013,584:150-155.
【14】田亚强,蔡志新,毕文强,等.中锰钢两相区温轧淬火处理后的组织性能[J].材料热处理学报,2021,42(9):128-135. TIAN Y Q,CAI Z X,BI W Q,et al.Microstructure and properties of medium manganese steel after intercritical warm-rolling and quenching[J].Transactions of Materials and Heat Treatment,2021,42(9):128-135.
【15】HUANG C P,HUANG M X.Effect of processing parameters on mechanical properties of deformed and partitioned (D&P) medium Mn steels[J].Metals,2021,11(2):356.
【16】ARLAZAROV A,GOUNÉ M,BOUAZIZ O,et al.Evolution of microstructure and mechanical properties of medium Mn steels during double annealing[J].Materials Science and Engineering:A,2012,542:31-39.
【17】胡进朋,万德成,李杰,等.临界区退火温度对中锰钢组织性能和变形行为的影响[J].材料热处理学报,2022,43(2):104-111. HU J P,WAN D C,LI J,et al.Effect of intercritical annealing temperature on microstructure,properties and deformation behavior of medium manganese steel[J].Transactions of Materials and Heat Treatment,2022,43(2):104-111.
【18】ZHAO C,CAO W Q,ZHANG C,et al.Effect of annealing temperature and time on microstructure evolution of 0.2C-5Mn steel during intercritical annealing process[J].Materials Science and Technology,2014,30(7):791-799.
【19】黄龙,邓想涛,刘佳,等.0.12C-3.0Mn低碳中锰钢中残余奥氏体稳定性与低温韧性的关系[J].金属学报,2017,53(3):316-324. HUANG L,DENG X T,LIU J,et al.Relationship between retained austenite stability and cryogenic impact toughness in 0.12C-3.0Mn low carbon medium manganese steel[J].Acta Metallurgica Sinica,2017,53(3):316-324.
【2】宋仁伯,霍巍丰,周乃鹏,等.Fe-Mn-Al-C系中锰钢的研究现状与发展前景[J].工程科学学报,2020,42(7):814-828. SONG R B,HUO W F,ZHOU N P,et al.Research progress and prospect of Fe-Mn-Al-C medium Mn steels[J].Chinese Journal of Engineering,2020,42(7):814-828.
【3】张丽凤,王社则,田博彤.高强塑积汽车钢板的显微组织与力学性能[J].塑性工程学报,2021,28(11):181-188. ZHANG L F,WANG S Z,TIAN B T.Microstructure and mechanical properties of automobile steel sheet with high strength-ductility balance[J].Journal of Plasticity Engineering,2021,28(11):181-188.
【4】胡斌,屠鑫,王玉,等.中锰钢塑性失稳现象的研究进展及未来研究展望[J].工程科学学报,2020,42(1):48-59. HU B,TU X,WANG Y,et al.Recent progress and future research prospects on the plastic instability of medium-Mn steels:A review[J].Chinese Journal of Engineering,2020,42(1):48-59.
【5】WANG F L,YE X Y,REN S B,et al.Effect of intercritical annealing time on microstructure evolution and mechanical properties of low carbon medium manganese steel subjected to multi-step heat treatment process[J].Materials,2022,15(7):2425.
【6】MA Y.Medium-manganese steels processed by austenite-reverted-transformation annealing for automotive applications[J].Materials Science and Technology,2017,33(15):1713-1727.
【7】WENG Z J,GU K X,WANG K K,et al.The reinforcement role of deep cryogenic treatment on the strength and toughness of alloy structural steel[J].Materials Science and Engineering:A,2020,772:138698.
【8】李康丽,李永志,孙国栋.正火预热处理对42CrMo曲轴钢调质后的组织与性能影响[J].特殊钢,2020,41(4):26-29. LI K L,LI Y Z,SUN G D.Effect of normalizing preheat treatment on structure and properties of 42CrMo forging crankshaft steel after quenching and tempering treatment[J].Special Steel,2020,41(4):26-29.
【9】LIU G,LI B,XU S,et al.Effect of intercritical annealing temperature on multiphase microstructure evolution in ultra-low carbon medium manganese steel[J].Materials Characterization,2021,173:110920.
【10】邵成伟,惠卫军,张永健,等.一种新型高强度高塑性冷轧中锰钢的组织和力学性能[J].金属学报,2019,55(2):191-201. SHAO C W,HUI W J,ZHANG Y J,et al.Microstructure and mechanical properties of a novel cold rolled medium-Mn steel with superior strength and ductility[J].Acta Metallurgica Sinica,2019,55(2):191-201.
【11】YE Q Z,HAN G,XU J P,et al.Effect of a two-step annealing process on deformation-induced transformation mechanisms in cold-rolled medium manganese steel[J].Materials Science and Engineering:A,2022,831:142244.
【12】孙荣民,李国阳,王辉,等.逆相变退火处理Fe-Mn-C中锰钢的组织与性能[J].钢铁,2021,56(6):82-88. SUN R M,LI G Y,WANG H,et al.Microstructure and properties of Fe-Mn-C medium-Mn steel processed by ART-annealing[J].Iron & Steel,2021,56(6):82-88.
【13】WU Z Q,DING H,LI H Y,et al.Microstructural evolution and strain hardening behavior during plastic deformation of Fe-12Mn-8Al-0.8C steel[J].Materials Science and Engineering:A,2013,584:150-155.
【14】田亚强,蔡志新,毕文强,等.中锰钢两相区温轧淬火处理后的组织性能[J].材料热处理学报,2021,42(9):128-135. TIAN Y Q,CAI Z X,BI W Q,et al.Microstructure and properties of medium manganese steel after intercritical warm-rolling and quenching[J].Transactions of Materials and Heat Treatment,2021,42(9):128-135.
【15】HUANG C P,HUANG M X.Effect of processing parameters on mechanical properties of deformed and partitioned (D&P) medium Mn steels[J].Metals,2021,11(2):356.
【16】ARLAZAROV A,GOUNÉ M,BOUAZIZ O,et al.Evolution of microstructure and mechanical properties of medium Mn steels during double annealing[J].Materials Science and Engineering:A,2012,542:31-39.
【17】胡进朋,万德成,李杰,等.临界区退火温度对中锰钢组织性能和变形行为的影响[J].材料热处理学报,2022,43(2):104-111. HU J P,WAN D C,LI J,et al.Effect of intercritical annealing temperature on microstructure,properties and deformation behavior of medium manganese steel[J].Transactions of Materials and Heat Treatment,2022,43(2):104-111.
【18】ZHAO C,CAO W Q,ZHANG C,et al.Effect of annealing temperature and time on microstructure evolution of 0.2C-5Mn steel during intercritical annealing process[J].Materials Science and Technology,2014,30(7):791-799.
【19】黄龙,邓想涛,刘佳,等.0.12C-3.0Mn低碳中锰钢中残余奥氏体稳定性与低温韧性的关系[J].金属学报,2017,53(3):316-324. HUANG L,DENG X T,LIU J,et al.Relationship between retained austenite stability and cryogenic impact toughness in 0.12C-3.0Mn low carbon medium manganese steel[J].Acta Metallurgica Sinica,2017,53(3):316-324.
相关信息