核用一回路18-8不锈钢管道腐蚀分析
Analyses of the Corrosion in Nuclear Primary Coolant Circuit Pipe of 18-8 Stainless Steel
摘 要
通过宏观检查、显微组织、断口形貌及扫描电镜能谱分析等方法对核用一回路0Cr18Ni10Ti管道存在的腐蚀问题进行了全面分析.结果表明:直管部位的点腐蚀出现较多,弯管部位出现较少的应力腐蚀,焊缝部位也出现较少的应力腐蚀和晶间腐蚀;产生上述腐蚀的原因主要是由于材料本身的性能欠佳和海水滴漏溅落到管道表面造成了氯离子聚集.
18-8不锈钢
腐蚀
primary coolant circuit pipe
18-8 stainless steel
corrosion
Abstract
Using macroscopical inspection,metallographical analysis,fractography analysis and SEM energy spectrum analysis,overall analysis of corrosions in nuclear primary coolant circuit 18-8 stainless steel pipe was performed.The results show that pitting corrosion occurre at the unbent pipe segment,sorme stress corrosion cracking occurre in bend pipe and welding line,and some intergranular corrosion occurre also at welding line.Above corrosions resulted from the properties of the pipe material and chloride ion assembling due to seawater dripping down on pipe surface.
中图分类号 TG172.9
所属栏目
基金项目
收稿日期 2006/7/3
修改稿日期 2006/9/12
网络出版日期
作者单位点击查看
备注苗中辉(1972-),男,吉林榆树人,工程师,硕士.
引用该论文: MIAO Zhong-hui,JIAO Zeng-geng,CAI Qi. Analyses of the Corrosion in Nuclear Primary Coolant Circuit Pipe of 18-8 Stainless Steel[J]. Materials for mechancial engineering, 2007, 31(7): 49～51
苗中辉,焦增庚,蔡琦. 核用一回路18-8不锈钢管道腐蚀分析[J]. 机械工程材料, 2007, 31(7): 49～51
被引情况:
【1】程晓波, "304不锈钢表面锈蚀原因分析",腐蚀与防护 31, 946-948(2010)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴连生.失效分析技术[M].成都:四川科学技术出版社,1985.
【2】上海交通大学《金属断口分析》编写组.金属断口分析[M].北京:国防工业出版社,1979.
【3】肖纪美,曹楚南.材料腐蚀学原理[M].北京:化学工业出版社,2002.
【2】上海交通大学《金属断口分析》编写组.金属断口分析[M].北京:国防工业出版社,1979.
【3】肖纪美,曹楚南.材料腐蚀学原理[M].北京:化学工业出版社,2002.
相关信息