高强度螺栓断裂原因分析
Analysis on Fracture Reason of High Strength Bolts
摘 要
通过对10.9级高强度紧固件M20~M24 mm螺栓的延迟断裂进行了宏观、微观检验及分析, 得出了氢脆是引起断裂的主要原因。通过对氢脆的机理、影响因素等方面的理论分析, 得出对于高强度紧固件的氢脆, 硬度的高低是主要的影响因素。
螺栓
延迟断裂
氢脆
硬度
high strength fasteners
bolt
delayed fracture
hydrogen embrittlement
hardness
Abstract
Based on the macro and micro analysis on the delayed fracture of M20-M24 mm bolts of 10.9 level high strength fastener, it was obtained that the hydrogen embrittlement was the main cause of fracture. By theoretical analysis on mechanism of hydrogen embrittlement and its influencing factors, the conclusion was presented that the hardness was the main influencing factor for hydrogen embrittlement of high strength fasteners.
中图分类号 TH131.3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/2/17
修改稿日期
网络出版日期
作者单位点击查看
备注周艳(1967-), 女, 高级工程师, 学士。
引用该论文: ZHOU Yan,ZHANG Jie. Analysis on Fracture Reason of High Strength Bolts[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(7): 526～527
周艳,张洁. 高强度螺栓断裂原因分析[J]. 理化检验－物理分册, 2014, 50(7): 526～527
被引情况:
【1】骆 亍,宾远红,李培芬, "1018钢螺钉断裂失效分析",理化检验－物理分册 52, 281-283(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈华锋, 王荣, 王滨, 等.高强度螺栓断裂原因分析[J].理化检验-物理分册, 2009, 45(4): 224-227.
【2】任学冲, 金莹, 王莎莎, 等.贝氏体车轮钢的氢脆敏感性[J].腐蚀与防护, 2011, 32(11):863-867.
【3】黄志涛, 田文怀, 苏永安, 等.普通碳素钢渗氮后的氢脆敏感性[J].理化检验-物理分册, 2010, 46(7):423-426.
【2】任学冲, 金莹, 王莎莎, 等.贝氏体车轮钢的氢脆敏感性[J].腐蚀与防护, 2011, 32(11):863-867.
【3】黄志涛, 田文怀, 苏永安, 等.普通碳素钢渗氮后的氢脆敏感性[J].理化检验-物理分册, 2010, 46(7):423-426.
相关信息