镀锌螺栓的断裂分析
Fracture Analysis of the Galvanizing Bolt
摘 要
镀锌螺栓在组装后放置1~2 d于根部或头部发生大量断裂，采用化学成分分析、金相检验、硬度检测及断口分析等方法对螺栓的断裂性质及断裂原因进行了分析。结果表明：螺栓断裂为典型的氢脆断裂;主要原因是螺栓在后期酸洗和电镀过程中除氢不彻底,吸入了大量的氢;次要原因是热处理工艺控制不当,使螺栓心度硬度偏高,增加了其对氢脆的敏感性;两者共同作用最终导致螺栓发生氢脆断裂。
显微组织
氢脆断裂
galvanizing bolt
microstructure
hydrogen embrittlement fracture
Abstract
The fracture of the galvanizing bolt happened after installed after 1~2 days. The fracture reason was investigated by means of chemical compositions analysis,microstructure analysis,hardness test and fracture analysis. The results show that the main reason which caused the bolt cracked was that hydrogen wasn’t removed thoroughly and a lot of hydrogen was existed in the bolt during the later acid cleaning and electroplating process. The other reason was that the improper heat treatment process which resulted the hardness of bott centre was highter than the required value. These co-caused hydrogen embrittlement fracture of galvanizing bolt.
中图分类号 TH13
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/10/7
修改稿日期
网络出版日期
作者单位点击查看
备注伍超群(1967-),女,高级工程师。
引用该论文: WU Chao-qun. Fracture Analysis of the Galvanizing Bolt[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(8): 519～521
伍超群. 镀锌螺栓的断裂分析[J]. 理化检验－物理分册, 2009, 45(8): 519～521
被引情况:
【1】骆 亍,宾远红,李培芬, "1018钢螺钉断裂失效分析",理化检验－物理分册 52, 281-283(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】纪贵. 世界钢号对照手册[M]. 北京: 中国标准出版社,2007．
【2】李秀兰. 小型零件的去氢检验方法与再去氢热处理[J]. 金属热处理,1999,24(2): 43-44．
【3】吴连生,张静江,刘正义,等. 机械装备失效分析图谱[M].广州: 广东科技出版社,1990．
【4】刘昌奎,臧金鑫,张兵. 30CrMnSiA螺栓断裂原因分析[J]. 失效分析与预防,2008,3(2): 42-47．
【5】王俊,汤宏才. 高强度螺栓断裂失效分析[J]. 机械工程材料,2007,31(10): 76-77,80．
【2】李秀兰. 小型零件的去氢检验方法与再去氢热处理[J]. 金属热处理,1999,24(2): 43-44．
【3】吴连生,张静江,刘正义,等. 机械装备失效分析图谱[M].广州: 广东科技出版社,1990．
【4】刘昌奎,臧金鑫,张兵. 30CrMnSiA螺栓断裂原因分析[J]. 失效分析与预防,2008,3(2): 42-47．
【5】王俊,汤宏才. 高强度螺栓断裂失效分析[J]. 机械工程材料,2007,31(10): 76-77,80．
相关信息