Ti-TiN Films Prepared by Cathodic Multi Arc Ion Plating on Magnesium Alloy AZ91C
摘 要
采用阴极多弧离子镀膜技术,在AZ91C镁合金基底上首次成功镀制了结合力强的以Ti为过渡层的TiN复合膜层,并利用高分辨扫描电子显微镜(SEM)、X射线能谱仪(EDS)、显微划痕测试等技术对复合膜层的形貌、组织结构及性能进行分析研究.结果表明,采用多弧离子镀膜工艺,能在经过恰当预处理的镁合金基底上制备出性能良好的TiN膜,膜层均匀、致密,膜基结合力达130 mN以上,复合硬度达500 HV左右(AZ91镁合金基底为125 HV).此外中性盐雾强化实验表明,经该方法处理后的镁合金在ASTM-B117标准测试条件下,腐蚀速率明显降低,经过200 h后,表面无明显腐蚀现象.真空多弧离子镀膜技术有望在镁合金表面防护领域得到应用.
Abstract
TiN films grown on Ti as interlayers were prepared on AZ91C magnesium alloy substrate by cathodic multi arc ion plating.The surface morphology,microstructure and hardness of the films were examined using high-resolution scanning electron microscope(SEM),X-ray energy diffraction spectrometers(EDS)and microcharacter hardness tester.The results show that TiN films with good performance can be obtained on the properly pretreated magnesium substrate by the multi arc ion plating technique.The adhesion force between the film and substrate was over 130 mN,and the complex hardness of the films was about 500 HV whereas that of AZ91C magnesium alloy was about 125 HV.The neutral salt spray accelerated testing indicated that corrosion rate of magnesium alloy after treated by this method declined significantly under ASTM-117 standard test condition.The surface of the films was not corroded obviously after salt spray test for 200 h.Vacuum multi arc ion plating technique can be applied to the area of magnesium alloy surface protection.
中图分类号 TG174.44 TG146.2+2
所属栏目 试验研究
基金项目 国家支撑计划项目(编号:2006BAE04B05-3);国家高技术研究发展计划(编号:2006AA05Z411);教育部长江学者与创新团队发展计划项目(编号:IRT0629);国家自然基金资助项目(编号:50505037)
收稿日期 2007/4/6
修改稿日期 2007/7/5
网络出版日期
作者单位点击查看
引用该论文: WANG Cheng-long,FAN Duo-wang,LIU Hong-zhong,ZHAO Lin,LU Ping,LENG Na. Ti-TiN Films Prepared by Cathodic Multi Arc Ion Plating on Magnesium Alloy AZ91C[J]. Corrosion & Protection, 2008, 29(4): 182~184
被引情况:
【1】马志康,高原,蔡航伟,王成磊,袁琳,张焱,吴炜钦, "201不锈钢表面弧光离子镀TiN和CrN薄膜的耐蚀性",腐蚀与防护 34, 670-672(2013)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Ohser-Wiedemann R,Hollstein F.Bayer U[J].Materials Research and Advanced Techniques,2005(96):818-822.
【2】赵家政,徐 洮.分析电子显微使用手册[M].宁夏:宁夏人民教育出版社,1996:100-101.
【3】范多旺,王成龙,范多进,等.镁及其合金表面真空镀层的制备方法[P].公开号:CN101086057,2007.
【2】赵家政,徐 洮.分析电子显微使用手册[M].宁夏:宁夏人民教育出版社,1996:100-101.
【3】范多旺,王成龙,范多进,等.镁及其合金表面真空镀层的制备方法[P].公开号:CN101086057,2007.
相关信息