Effect of Temperature on Corrosion Resistance of 5Cr Steel in Carbon Dioxide Corrosion Environment
摘 要
模拟塔里木油田现场环境,利用高温高压实验设备辅以失重法,研究了CO2腐蚀环境中温度对油、套管钢5Cr钢腐蚀速率的影响.采用扫描电镜(SEM)、电子能谱(EDS)和X射线衍射(XRD)等方法对试样表面腐蚀产物的形貌及成分进行了分析.结果表明:5Cr钢的平均腐蚀速率随温度的升高而增大,90 ℃时到达最大值,温度继续升高平均腐蚀速率降低.各种温度下,均没有局部腐蚀发生.所有温度条件下,腐蚀产物均为FeCO3,并且腐蚀产物膜中出现了Cr的富集现象.
Abstract
The effect of temperature on corrosion resistance of 5Cr steel in CO2 corrosion environment was investigated in high temperature and pressure autoclave by simulating the downhole environment of Tarim oil field,and the corrosion rate was measured by the weight loss method.The corrosion product was analyzed by SEM,EDS and XRD.The results showed that the corrosion rate of 5Cr increased with the temperature.The corrosion rate was maximum when the temperature was 90 ℃,and then decreased with the increasing of temperature.The pitting corrosion was not discovered at all temperatures.When the temperature was lower than 180 ℃,the corrosion product was mainly composed of FeCO3.Cr element was enriched in the corrosion product.
中图分类号 TG172.6 TE980
所属栏目 试验研究
基金项目
收稿日期 2009/6/6
修改稿日期 2009/10/11
网络出版日期
作者单位点击查看
备注董会,工程师.
引用该论文: DONG Hui,ZHAO Guo-xian,XUE Yan,Lü Xiang-hong,ZHANG Chun-wan,ZHAO Ying-hui. Effect of Temperature on Corrosion Resistance of 5Cr Steel in Carbon Dioxide Corrosion Environment[J]. Corrosion & Protection, 2010, 31(5): 365~368
被引情况:
【1】胡志兵, "16Mn集输管线钢在含CO2凝析气田的腐蚀行为",腐蚀与防护 34, 269-272(2013)
【2】刘飞,黄金营,夏成宇,周仕明,邓天安, "P110钢在不同温度含饱和H2S/CO2腐蚀溶液中的腐蚀行为",腐蚀与防护 37, 481-483(2016)
【3】刘飞,黄金营,周仕明,高元,邓天安, "H2S/CO2介质中P110钢表面的局部电偶腐蚀行为",腐蚀与防护 36, 527-530(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Ikeda A,Ueda M,Mukai S.CO2 corrosion behaviour and mechanism of carbon steel and alloy steel[C]//Corrosion/83,Paper No45.Houston TX:NACE,1983.
【2】Ueda M,Ikeda A.Effect of microstructure and Cr content in steel on CO2 corrosion[C]//Corrosion/96,Paper No13.Houston TX:NACE International,1996.
【3】Kimura M,Saito Y,Nakano Y.Effects of alloying elements on corrosion resistance of High strength linepipe steel in wet CO2 environment[C]//Corrosion/94,Paper No8.Houston TX:NACE International,1994.
【4】Schmitt G,Engels D.SEM/EDX Analysis of corrosion products for investigations on metallurgy and solution effects in CO2 corrosion[C]//Corrosion/88,Paper No149.Houston TX:NACE,1988.
【5】Videm K,Kvarekvaal J,Perez T,et al.Surface effects on the electrochemistry of iron and carbon steel electrodes in aqueous CO2 solutions[C]//Corrosion/96,Paper No1.Houston TX:NACE International,1996.
【6】Cross D.Mesa-type CO2 corrosion and its control[C]//Corrosion/93,Paper No118.Houston TX:NACE,1993.
【7】Ikeda A,Ueda M,Mukai S.CO2 behavior of carbon and Cr steels[C]//In:Hausler R H,Giddard H P (Eds),Advances in CO2 Corrosion.Vol1,Houston TX:NACE,1984.
【8】张忠铧,黄子阳,孙元宁,等.3Cr抗CO2和H2S腐蚀系列油套管开发[J].宝钢技术,2006(3):5-8.
【9】Rogne T,Eggen T G,Steinsmo U.Corrosion of C-MN-Steel and 0.5% CR steel in flowing CO2 saturated brines[C]//Corrosion/1996,Paper No33.Houston:NACE,1996.
【10】陈长风,路民旭,赵国仙,等.油套管钢CO2腐蚀产物膜特征[J].金属学报,2002,38(4):411-416.
【2】Ueda M,Ikeda A.Effect of microstructure and Cr content in steel on CO2 corrosion[C]//Corrosion/96,Paper No13.Houston TX:NACE International,1996.
【3】Kimura M,Saito Y,Nakano Y.Effects of alloying elements on corrosion resistance of High strength linepipe steel in wet CO2 environment[C]//Corrosion/94,Paper No8.Houston TX:NACE International,1994.
【4】Schmitt G,Engels D.SEM/EDX Analysis of corrosion products for investigations on metallurgy and solution effects in CO2 corrosion[C]//Corrosion/88,Paper No149.Houston TX:NACE,1988.
【5】Videm K,Kvarekvaal J,Perez T,et al.Surface effects on the electrochemistry of iron and carbon steel electrodes in aqueous CO2 solutions[C]//Corrosion/96,Paper No1.Houston TX:NACE International,1996.
【6】Cross D.Mesa-type CO2 corrosion and its control[C]//Corrosion/93,Paper No118.Houston TX:NACE,1993.
【7】Ikeda A,Ueda M,Mukai S.CO2 behavior of carbon and Cr steels[C]//In:Hausler R H,Giddard H P (Eds),Advances in CO2 Corrosion.Vol1,Houston TX:NACE,1984.
【8】张忠铧,黄子阳,孙元宁,等.3Cr抗CO2和H2S腐蚀系列油套管开发[J].宝钢技术,2006(3):5-8.
【9】Rogne T,Eggen T G,Steinsmo U.Corrosion of C-MN-Steel and 0.5% CR steel in flowing CO2 saturated brines[C]//Corrosion/1996,Paper No33.Houston:NACE,1996.
【10】陈长风,路民旭,赵国仙,等.油套管钢CO2腐蚀产物膜特征[J].金属学报,2002,38(4):411-416.
相关信息