可膨胀管变形前后的耐CO2腐蚀性能
CO2 Corrosion Resistance of L80 Casing Steel before and after Expansion
摘 要
油气井膨胀管技术是近年来油气井工程领域出现的一项新兴技术。本工作以L80套管为研究对象, 分别进行16％和22％的膨胀, 研究膨胀变形前后的微观组织变化规律。采用高压釜失重法、动电位极化和电化学阻抗谱技术研究了变形前后在饱和CO2溶液中L80套管的腐蚀行为。从电化学特征看, 膨胀变形后, 套管自腐蚀电位更负, 说明膨胀变形增大可增加腐蚀倾向, Icorr随着变形量的增加而增大; 该结果与失重法试验结果相吻合。
可膨胀管
微观组织
CO2腐蚀
电化学测试
L80 steel
expandable tube
microstructure
CO2 corrosion
electrochemical test
Abstract
Expandable tubular techlology is a new technology in the well engineering industry. The microstructure of L80 casing tubes expanded by 16% and 22% respectively was studied before and after expansion. The corrosion behaviors were studied by weight-loss method in autoclave and electrochemical tests before and after tube expansion. The electrochemical characteristics showed that the corrosion potential became more negative after the expansion deformation, and Icorr increased with the increase of the amount of deformation. The results matched well with the results of weight-loss experiment.
中图分类号 TG172
所属栏目 试验研究
基金项目
收稿日期 2010/7/2
修改稿日期 2010/8/6
网络出版日期
作者单位点击查看
备注蔡连庆, 工程师,
引用该论文: CAI Lian-qing,GAO Wei,PAN Zhi-yong. CO2 Corrosion Resistance of L80 Casing Steel before and after Expansion[J]. Corrosion & Protection, 2011, 32(5): 370
被引情况:
【1】刘飞,黄金营,夏成宇,周仕明,邓天安, "P110钢在不同温度含饱和H2S/CO2腐蚀溶液中的腐蚀行为",腐蚀与防护 37, 481-483(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Furlow W. Expandable casing program helps operator hit TD with larger tubular[J]. Offshore, 2000, 129(1), 48-51.
【2】盂庆昆, 谢正凯, 冯来. 可膨胀套管技术概述[J]. 石油钻采工艺, 2003, 26(4):67-74.
【3】Haut R C. Meeting economic challenges of deep water drilling with expandable-tubular technology[C]//Deep Offshore Technology International Conference, Stavanger, 1999.
【4】潘志勇, 高万夫, 高伟, 等. API L80套管的膨胀性能试验研究[J]. 石油机械, 2007, 35(4), 5-7.
【5】杨新田, 周琦. 管线钢带状组织对低温区CO2腐蚀行为影响的比较分析[J]. 甘肃科学学报, 2005, 17(2):110-113.
【6】李红英, 曾再德, 王长建. 冷轧变形量对PS版电解腐蚀性能的影响[J]. 腐蚀与防护, 2007, 28(8):383-386.
【7】王从曾. 材料性能学[M]. 北京:北京工业大学出版社, 2001.
【8】曹楚南. 腐蚀电化学原理[M]. 北京:化学工业出版社, 2004.
【2】盂庆昆, 谢正凯, 冯来. 可膨胀套管技术概述[J]. 石油钻采工艺, 2003, 26(4):67-74.
【3】Haut R C. Meeting economic challenges of deep water drilling with expandable-tubular technology[C]//Deep Offshore Technology International Conference, Stavanger, 1999.
【4】潘志勇, 高万夫, 高伟, 等. API L80套管的膨胀性能试验研究[J]. 石油机械, 2007, 35(4), 5-7.
【5】杨新田, 周琦. 管线钢带状组织对低温区CO2腐蚀行为影响的比较分析[J]. 甘肃科学学报, 2005, 17(2):110-113.
【6】李红英, 曾再德, 王长建. 冷轧变形量对PS版电解腐蚀性能的影响[J]. 腐蚀与防护, 2007, 28(8):383-386.
【7】王从曾. 材料性能学[M]. 北京:北京工业大学出版社, 2001.
【8】曹楚南. 腐蚀电化学原理[M]. 北京:化学工业出版社, 2004.
相关信息