Comparison for Corrosion Properties of Super 13Cr and High Strength 15Cr Martensitic Stainless Steels in Acid Solution
摘 要
通过在高温(120 ℃)、高压(10 MPa)和鲜酸(10%HCl+1.5%HF+3%HAc+5.1%TG201缓蚀剂)条件下的腐蚀试验, 对超级13Cr和高强15Cr马氏体不锈钢在此苛刻工况条件下的耐蚀性及其与酸化缓蚀剂的匹配性进行对比试验。结果表明: 超级13Cr和高强15Cr马氏体不锈钢在此条件下的均匀腐蚀速率分别为14.551 6, 13.495 4 mm·a-1, 远低于相关标准要求; 酸化缓蚀剂与两种试验钢的匹配性均较好, 但并不能防止点蚀的发生, 与高强15Cr钢相比, 超级13Cr钢的点蚀速率较高, 点蚀密度大; 高强15Cr钢在鲜酸中的耐蚀性要优于超级13Cr钢的。
Abstract
Comparative live acid (10%HCl+1.5%HF+3%HAc+5.1% TG201 inhibitor) experiment of corrosion resistance and matching ability of acidizing corrosion inhibitor in severe working environments of super 13Cr and high strength 15Cr martensitic stainless steels were investigated through high temperature and high pressure tests.The results show that the uniform corrosion rate of super 13Cr and high strength 15Cr martensitic stainless steel in severe working environments were 14.551 6 mm·a-1 and 13.495 4 mm·a-1 respectively, and those were far lower than standard specifications and requirements. Acidizing corrosion inhibitor displayed a good matching ability with super 13Cr and high strength 15Cr martensitic stainless steels, but appearance of pitting could not be fully prevented by adding acidizing corrosion inhibitor, and the pitting rate and pitting density of super 13Cr were greater than high strength 15Cr martensitic stainless steel. The corrosion resistance of high strength 15Cr martensitic stainless steel in live acid was better than that of the super 13Cr steel.
中图分类号 TG172.8
所属栏目 材料性能及其应用
基金项目 国家自然科学基金资助项目(51271146)
收稿日期 2013/7/13
修改稿日期 2014/3/16
网络出版日期
作者单位点击查看
备注王立翀(1986-), 男, 蒙古族, 内蒙古赤峰人, 硕士研究生。
引用该论文: WANG Li-chong,LV Xiang-hong,ZHAO Rong-huai,ZHAO Guo-xian,LI Na. Comparison for Corrosion Properties of Super 13Cr and High Strength 15Cr Martensitic Stainless Steels in Acid Solution[J]. Materials for mechancial engineering, 2014, 38(5): 57~61
王立翀,吕祥鸿,赵荣怀,赵国仙,李娜. 超级13Cr与高强15Cr马氏体不锈钢在酸化液中的耐蚀性能对比[J]. 机械工程材料, 2014, 38(5): 57~61
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】林冠发,相建民,常泽亮,等.3种13Cr110钢高温高压CO2腐蚀行为对比研究[J].装备环境工程, 2008, 5(5):1-4.
【2】吕祥鸿,赵国仙,杨延清.13Cr钢高温高压CO2腐蚀电化学特性研究[J].材料工程, 2004(10):16-20.
【3】周波,崔润炯,刘建中.增强型13Cr钢抗CO2 腐蚀套管的研制[J].钢管, 2006, 36(6): 22-26.
【4】MARCHEBOIS H, LEYER J. SSC performance of a super 13%Cr martensitic stainless steel for OCTG[C]// 62th NACE Annual Conference. Houston: Omnipress, 2007.
【5】荣海波, 李娜, 赵国仙,等.超级15Cr马氏体不锈钢超深超高压高温油气井中的腐蚀行为研究[J].石油矿场机械,2011, 40 (9): 57-62.
【6】王连成,李明朗,程万庆, 等.酸化压裂方法在碳酸盐岩热储层中的应用[J].水文地质工程地质,2010,37(5):128-132.
【7】SY/T 5405-1996 酸化用缓蚀剂性能试验方法及评价指标[S].
【8】MITSUO K, KEI S, KEN S. Corrosion resistance of martens-itic stainless steel OCTG in severe corrosion environments[C]// 62th NACE Annual Conference. Houston: Omnipress,2007.
【9】BOLES J, KE M J, PARKER C. Corrosion inhibition of new 15 chromium tubulars in acid stimulation fluids at high tempe-ratures[C]//The 2009 SPE Annual Technical Conference and Exhibition. New Orleans, Louisiana, USA: [s.n],2009.
【10】CHAMBERS B, VENKATESH A, GAMBALE D. Performance of tantalum-surface alloy on stainless steel and multiple corrosion resistant alloy in laboratory evaluation of deep well acidizing environment[C]// 66st NACE Annual Conference. Houston: Omnipress,2011.
【11】MINGJIE K, JOEL B. Corrosion behavior of various 13 chromium tubulars in acid stimulation fluids[C]//The 1st International Symposium on Oilfield Corrosion.[S.l.]:[s.n],2004.
【2】吕祥鸿,赵国仙,杨延清.13Cr钢高温高压CO2腐蚀电化学特性研究[J].材料工程, 2004(10):16-20.
【3】周波,崔润炯,刘建中.增强型13Cr钢抗CO2 腐蚀套管的研制[J].钢管, 2006, 36(6): 22-26.
【4】MARCHEBOIS H, LEYER J. SSC performance of a super 13%Cr martensitic stainless steel for OCTG[C]// 62th NACE Annual Conference. Houston: Omnipress, 2007.
【5】荣海波, 李娜, 赵国仙,等.超级15Cr马氏体不锈钢超深超高压高温油气井中的腐蚀行为研究[J].石油矿场机械,2011, 40 (9): 57-62.
【6】王连成,李明朗,程万庆, 等.酸化压裂方法在碳酸盐岩热储层中的应用[J].水文地质工程地质,2010,37(5):128-132.
【7】SY/T 5405-1996 酸化用缓蚀剂性能试验方法及评价指标[S].
【8】MITSUO K, KEI S, KEN S. Corrosion resistance of martens-itic stainless steel OCTG in severe corrosion environments[C]// 62th NACE Annual Conference. Houston: Omnipress,2007.
【9】BOLES J, KE M J, PARKER C. Corrosion inhibition of new 15 chromium tubulars in acid stimulation fluids at high tempe-ratures[C]//The 2009 SPE Annual Technical Conference and Exhibition. New Orleans, Louisiana, USA: [s.n],2009.
【10】CHAMBERS B, VENKATESH A, GAMBALE D. Performance of tantalum-surface alloy on stainless steel and multiple corrosion resistant alloy in laboratory evaluation of deep well acidizing environment[C]// 66st NACE Annual Conference. Houston: Omnipress,2011.
【11】MINGJIE K, JOEL B. Corrosion behavior of various 13 chromium tubulars in acid stimulation fluids[C]//The 1st International Symposium on Oilfield Corrosion.[S.l.]:[s.n],2004.
相关信息