摘 要
锅炉过热器进行化学清洗时, 涉及多种金属材料(如20G, T22, 15CrMoG, 12Cr1MoV, T91, TP347及Super 304等)。为了掌握清洗过程这些材料的腐蚀情况, 采用模拟清洗试验, 研究了常规清洗配方及工艺条件下这些材料的腐蚀速率。结果表明, EDTA氨盐和EDTA钠盐清洗配方对各种材料的腐蚀速率都维持在较低水平; 其他清洗介质中, T91的腐蚀速率远大于其他材料, 且采用羟基乙酸+甲酸配方清洗后奥氏体钢出现了晶间腐蚀。研究了不同缓蚀剂控制复合有机酸A中各种金属材料的腐蚀速率, 结果表明, 采用缓蚀剂配方调整可以有效地控制这些材料的腐蚀速率。
Abstract
During the superheater chemical cleaning, the cleaning system involves many metal materials such as 20G, T22, 15CrMoG, 12Cr1MoV, T91, TP347, Super 304 and so on. In order to master the corrosion situation of these materials during chemical cleaning, the corrosion rates of these materials in cleaning agents were studied by simulating tests. The results showed that the corrosion rates of these materials in NH-EDTA and Na-EDTA chemical agents were all at a relatively low level, but the corrosion rate of T91was much higher than that of other materials in other chemical agents and intergranular corrosion appeared on TP347 and Super 304 in hydroxyl acetic acid + formic acid agent. The corrosion rates of all materials can be controlled at a low level in complex-organic-acid-A by adjusting the inhibitor formula.
中图分类号 TG174
所属栏目 试验研究
基金项目
收稿日期 2013/3/14
修改稿日期
网络出版日期
作者单位点击查看
备注林卫丽(1975-),讲师,硕士,从事材料研究,
引用该论文: LIN Wei-li,DENG Yu-qiang,ZHANG Xiang-jin,SONG Fei,LIU Feng,QI Dong-dong,NI Rui-tao. Metal Materials Corrosion during Superheater Chemical Cleaning[J]. Corrosion & Protection, 2014, 35(1): 74
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】曹杰玉, 陈洁. 电厂锅炉化学清洗需注意的几个问题[J]. 中国电力, 2003, 36(7): 20-22.
【2】吴文龙, 李长鸣, 常剑冰,等. 警惕锅炉酸洗不当引起的爆管事故[J]. 热力发电, 2008, 37(12): 54-56.
【3】余存烨. 工业设备化学清洗中的腐蚀与控制[J]. 腐蚀与防护, 2002, 23(10): 454-457.
【4】王立坤, 王艳芳, 赵久国, 等. 某热电厂炉管开裂失效分析[J]. 理化检验-物理分册, 2013,48(12): 828-830.
【5】OWEN W D,SCOT Martin. Surface complexation and dissolution of hematite by C1-C6 dicarboxylic acids[J]. Geochimica Cosmochimica Acta,2001, 65(23): 4289-4301.
【6】PRINCE A A M,VELMURUGAN S,NARASIMHAN S V,et al. Dissolution behavior of magnetite film formed over carbon steel in dilute organic acid media[J]. Journal of Nuclear Materials,2001,289:281-290.
【2】吴文龙, 李长鸣, 常剑冰,等. 警惕锅炉酸洗不当引起的爆管事故[J]. 热力发电, 2008, 37(12): 54-56.
【3】余存烨. 工业设备化学清洗中的腐蚀与控制[J]. 腐蚀与防护, 2002, 23(10): 454-457.
【4】王立坤, 王艳芳, 赵久国, 等. 某热电厂炉管开裂失效分析[J]. 理化检验-物理分册, 2013,48(12): 828-830.
【5】OWEN W D,SCOT Martin. Surface complexation and dissolution of hematite by C1-C6 dicarboxylic acids[J]. Geochimica Cosmochimica Acta,2001, 65(23): 4289-4301.
【6】PRINCE A A M,VELMURUGAN S,NARASIMHAN S V,et al. Dissolution behavior of magnetite film formed over carbon steel in dilute organic acid media[J]. Journal of Nuclear Materials,2001,289:281-290.
相关信息