Corrosion of L360 Pipeline Steel Used in Puguang Gas-field Gathering and Transportation System
摘 要
对L360管线钢在普光气田集输系统中使用了2a的L360管线钢的腐蚀行为进行了研究, 并对L360钢的机械性能(屈服强度、断裂强度、冲击强度、延伸率、硬度)进行了研究。结果表明, 服役2 a后, 钢管内壁出现了部分氢致裂纹和点蚀, 但L360钢在使用前后的力学性能变化并不明显, 所产生的氢致裂纹也对于钢管的安全服役性能影响很小。通过对于固溶氢浓度以及服役后抗硫化物应力腐蚀(SSC)性能的研究, 认为L360钢具有很低的氢溶解度, 长期服役后的L360钢依然有足够的抗SSC能力。L360钢能够适用于高酸性气田集输系统。
Abstract
The corrosion behavior and mechanical properties (yield strength, impact strength, elongation, hardness, fracture toughness) of L360 used for two years in high sour environment of Puguang gas-field were investigated. The results showed that pitting corrosion and hydrogen-induced cracking were observed in L360 steel. But there was little change for the mechanical properties and anti-SSC performance of L360 steel. L360 steel can be applied to high sour gas-field gathering system.
中图分类号 TG174
所属栏目 试验研究
基金项目 中国博士后科学基金(2011M501193);河南省博士后科研启动基金(2010044)
收稿日期 2013/5/1
修改稿日期
网络出版日期
作者单位点击查看
备注张诚(1978-), 高级工程师, 博士, 从事油田防腐蚀研究,
引用该论文: GUAN Jian-qing,ZHANG Cheng,OU Tian-xiong,CHEN Chang-feng. Corrosion of L360 Pipeline Steel Used in Puguang Gas-field Gathering and Transportation System[J]. Corrosion & Protection, 2014, 35(3): 214
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】NYKYFORCHYN H. Environmentally assisted‘in-bulk’steel degradation of long term service gas trunkline[J]. Engineering Failure Analysis,2010,17:624-632.
【2】周丽萍, 穆海玲, 赵楠. X52管线钢抗氢致开裂试验裂纹成因分析[J]. 理化检验-物理分册,2013,49(4):270-273.
【3】王树涛, 郑新艳, 李明志, 等. 抗硫套管钢P110SS在高含H2S/CO2条件下的硫化物应力腐蚀开裂敏感性[J]. 腐蚀与防护,2013,34(3):189-192.
【4】HUANGA F. Effect of microstructure and inclusions on hydrogen induced cracking susceptibility and hydrogen trapping efficiency of X120 pipeline steel[J]. Materials Science and Engineering A,2010,527:6997-7001.
【5】IAN B. Sulfur isotope partitioning during experimental formation of pyrite via the polysulfide and hydrogen sulfide pathways:implications for the interpretation of sedimentary and hydrothermal pyrite isotope records[J]. Earth and Planetary Science Letters,2004,228:495-509.
【2】周丽萍, 穆海玲, 赵楠. X52管线钢抗氢致开裂试验裂纹成因分析[J]. 理化检验-物理分册,2013,49(4):270-273.
【3】王树涛, 郑新艳, 李明志, 等. 抗硫套管钢P110SS在高含H2S/CO2条件下的硫化物应力腐蚀开裂敏感性[J]. 腐蚀与防护,2013,34(3):189-192.
【4】HUANGA F. Effect of microstructure and inclusions on hydrogen induced cracking susceptibility and hydrogen trapping efficiency of X120 pipeline steel[J]. Materials Science and Engineering A,2010,527:6997-7001.
【5】IAN B. Sulfur isotope partitioning during experimental formation of pyrite via the polysulfide and hydrogen sulfide pathways:implications for the interpretation of sedimentary and hydrothermal pyrite isotope records[J]. Earth and Planetary Science Letters,2004,228:495-509.
相关信息