Analysis on Stress Corrosion Cracking of Welded Stainless Steel Pipe
摘 要
某公司不锈钢焊管使用过程中出现大面积开裂泄露。采用宏观检验、化学成分分析、金相检验、SEM、EDS能谱分析等方法,对该管道的开裂泄露进行失效分析。结果表明,该焊管的开裂主要为氯离子应力腐蚀开裂。焊管成型后未热处理造成的残余应力、管外面橡塑保温材料释放出的氯离子共同造成了该不锈钢焊管的应力腐蚀开裂。
Abstract
Large area of cracks and leakage were found on some welded stainless steel pipes. The pipes were analyzed by means of macroscopic examination, chemical composition analysis, metallographic examination, SEM and EDS. The results showed that the crack was stress corrosion cracking caused by chloride ion. The stress corrosion was due to the combined effects of residual stress which was caused by no heat-treatmnet after cold-working and chloride ion which came from rubber insulation material.
中图分类号 TG174
所属栏目 应用技术
基金项目
收稿日期 2013/7/24
修改稿日期
网络出版日期
作者单位点击查看
备注许万剑(1987-),工程师,硕士,从事不锈钢制品质量检验,
引用该论文: XU Wan-jian,YANG Chun-li,ZHAO Hong-zhu,TAO Xin-xiu,DING Fei,CHEN An-yuan. Analysis on Stress Corrosion Cracking of Welded Stainless Steel Pipe[J]. Corrosion & Protection, 2014, 35(5): 511
被引情况:
【1】邹章雄,金少申,刘昌禄,刘顺勤,马强,葛玉雄, "奥氏体不锈钢压力管道的应力腐蚀开裂及预防",理化检验-物理分册 51, 721-724(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】魏宝明. 金属腐蚀理论及应用[M]. 北京: 化学工业出版社,1984.
【2】张栋,钟培道,陶春虎,等. 失效分析[M]. 北京: 国防工业出版社,2008: 98.
【3】高克玮,乔利杰,诸武扬. 321奥氏体不锈钢单晶应力腐蚀断口的研究[J]. 金属学报,1998(8): 890.
【4】廖景娱. 金属构件失效分析[M]. 北京: 化学工业出版社,2003: 106,102.
【2】张栋,钟培道,陶春虎,等. 失效分析[M]. 北京: 国防工业出版社,2008: 98.
【3】高克玮,乔利杰,诸武扬. 321奥氏体不锈钢单晶应力腐蚀断口的研究[J]. 金属学报,1998(8): 890.
【4】廖景娱. 金属构件失效分析[M]. 北京: 化学工业出版社,2003: 106,102.
相关信息