304不锈钢薄壁容器焊缝腐蚀泄漏原因
Causes of Welded Corrosion and Leakage of 304 Stainless Steel Thin-wall Container
摘 要
采用宏观检验、化学成分分析、金相检验、SEM、EDS能谱分析等手段，对某公司的304不锈钢薄壁容器焊缝腐蚀泄漏进行了失效分析。结果表明，不合适的焊接方法、焊接质量控制较差和焊后未酸洗钝化造成了该不锈钢薄壁容器焊缝处早期腐蚀泄漏失效。
二氧化碳气体保护焊
晶间腐蚀
氩弧焊
酸洗钝化
stainless steel thin-wall container
CO2 gas protective welding
intergranular corrosion
argon arc welding
pickling and passivation
Abstract
The welded corrosion and leakage of a 304 stainless steel thin-wall container were analyzed by means of macroscopic examination, chemical composition analysis, metallographic examination, SEM and EDS analysis. The results showed that unsuitable welding method, poor weld quality and no pickling and passivation after welding caused the early corrosion and leakage.
中图分类号 TG174
所属栏目 失效分析
基金项目
收稿日期 2013/7/24
修改稿日期
网络出版日期
作者单位点击查看
备注许万剑(1987-),工程师,硕士,从事不锈钢制品质量检验,
引用该论文: YANG Chun-li,XU Wan-jian,TAO Xin-xiu,MA Yuan-yuan,DING Fei,CHEN An-yuan. Causes of Welded Corrosion and Leakage of 304 Stainless Steel Thin-wall Container[J]. Corrosion & Protection, 2014, 35(6): 623
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵昌盛. 不锈钢的应用及热处理[M]. 北京: 机械工业出版社，2010: 33.
【2】王国栋. 浅议薄壁不锈钢给水管焊接施工技术[J]. 甘肃科技，2011,17: 154.
【3】王晓雷. 承压类特种设备无损检测相关知识[M]. 北京: 中国劳动社会保障出版社，2007: 43.
【4】何德孚，王晶滢. 不锈钢管制造及使用过程中的酸洗和钝化[J]. 应用与开发，2012(5): 30-31.
【2】王国栋. 浅议薄壁不锈钢给水管焊接施工技术[J]. 甘肃科技，2011,17: 154.
【3】王晓雷. 承压类特种设备无损检测相关知识[M]. 北京: 中国劳动社会保障出版社，2007: 43.
【4】何德孚，王晶滢. 不锈钢管制造及使用过程中的酸洗和钝化[J]. 应用与开发，2012(5): 30-31.
相关信息