6061铝合金表面氟钛酸盐转化新工艺
A Novel Fluorine-titanate Conversion Process on 6061 Aluminum Alloy Surface
摘 要
以6061铝合金为基体, 在由钛盐和氟化钠组成的转化液中制得无铬转化膜。以盐雾试验后试样未腐蚀面积为指标, 采用正交试验研究了转化液的组成和工艺条件对氟钛酸盐转化膜耐蚀性的影响。优化后氟钛酸盐转化工艺参数为: 钛盐1.5 g/L, 氟化钠3 g/L, H2O2 1.5 mL/L, 转化时间10 min, 处理液pH=5.0。
工艺优化
氟钛酸盐转化膜
耐蚀性
6061 aluminum alloy
process optimization
fluorine-titanate conversion coating
corrosion resistance
Abstract
A chromium-free conversion coating on 6061 aluminum substrate was prepared from a conversion solution containing titanate and sodium fluoride. The uncorroded area fraction of the sample after salt spray test was served as the index to study the effect of the composition of conversion solution and process parameters on the corrosion resistance of conversion coating. The optimized process parameters of fluorine-titanate conversion are as follow: titanium salt 1.5 g/L, sodium fluoride 3 g/L, hydrogen peroxide1.5 mL/L, normal temperature, pH=5.0, and conversion time 10 min.
中图分类号 TG174
所属栏目 应用技术
基金项目 河南省科技攻关重点项目(122102310321); 商丘市科技攻关项目(141003)
收稿日期 2014/4/22
修改稿日期
网络出版日期
作者单位点击查看
备注李红玲(1977-),讲师,硕士,从事金属材料表面改性方面的研究,
引用该论文: QIN Zhen-Hua,LI Hong-ling. A Novel Fluorine-titanate Conversion Process on 6061 Aluminum Alloy Surface[J]. Corrosion & Protection, 2014, 35(7): 742
被引情况:
【1】李红玲,刘双枝, "6061铝合金氟钛酸盐转化膜耐蚀性能的改性研究",腐蚀与防护 36, 938-941(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】龚伟慧, 陈东初, 李文芳,等. 环境友好型铝合金化学转化表面处理技术的发展概况［J］. 材料研究与应用, 2009, 3(1):1-4.
【2】HINTON B R W. Corrosion prevention and chromates:The End of an Era［J］. Metal Finishing, 1991, 89(9):55-58.
【3】韩哲, 熊金平, 左禹. 铝合金表面化学氧化工艺的研究进展[J]. 电镀与精饰, 2008, 30(11): 14-18.
【4】郭瑞光, 杨杰, 康娟. 铝合金表面钛酸盐化学氧化膜研究[J]. 电镀与涂饰, 2006, 25(1): 46-48.
【5】NORDLIEN J H, WALMSLEY J C, NISANCIOGLU K, et al. Formation of a zirconium-titanium based conversion layer on AA6060 aluminium[J]. Surface and Coatings Technology, 2002, 153(1): 72-78.
【6】LUNDER O, SIMENSEN C, YU Y, et al. Formation and characterisation of Ti-Zr based conversion layers on AA6060 aluminum[J]. Surface and Coatings Technology, 2004, 184(2/3): 278-290.
【7】王娜娜, 郭瑞光, 唐长斌, 等. 2024 铝合金氟铝酸盐转化膜的制备及其防腐蚀性能[J]. 材料保护, 2012, 45(5): 38-41.
【8】郭瑞光,王晓昌,耿志良,等. 环境友好型铝合金表面转化膜的制备及其耐蚀性能[J]. 材料保护, 2008, 41(12): 14-16.
【9】白锐, 丁晓莉, 肖雄,等. 一种新型环保铝合金无铬钝化处理液[J]. 广东化工, 2012, 39(6): 127-128.
【10】陈东初,黄柱周,李文芳. 铝合金表面无铬化学转化膜的研究[J]. 表面技术,2005,34(6):38-39.
【11】ANDREATTA F,TURCO A,GRAEVEL D,et al. SKPFM and SEM study of the deposition mechanism of Zr/Ti based pre-treatment on AA6016 aluminum alloy[J]. Surface & Coatings Teclmology,2007,201:7668-7685.
【12】LAHA P,SEHRAM T,TERRYN H. Use of spectroscopic elliPsometry to study Zr/Ti films on Al[J]. Surf Interface Anal,2002,34:677-680.
【2】HINTON B R W. Corrosion prevention and chromates:The End of an Era［J］. Metal Finishing, 1991, 89(9):55-58.
【3】韩哲, 熊金平, 左禹. 铝合金表面化学氧化工艺的研究进展[J]. 电镀与精饰, 2008, 30(11): 14-18.
【4】郭瑞光, 杨杰, 康娟. 铝合金表面钛酸盐化学氧化膜研究[J]. 电镀与涂饰, 2006, 25(1): 46-48.
【5】NORDLIEN J H, WALMSLEY J C, NISANCIOGLU K, et al. Formation of a zirconium-titanium based conversion layer on AA6060 aluminium[J]. Surface and Coatings Technology, 2002, 153(1): 72-78.
【6】LUNDER O, SIMENSEN C, YU Y, et al. Formation and characterisation of Ti-Zr based conversion layers on AA6060 aluminum[J]. Surface and Coatings Technology, 2004, 184(2/3): 278-290.
【7】王娜娜, 郭瑞光, 唐长斌, 等. 2024 铝合金氟铝酸盐转化膜的制备及其防腐蚀性能[J]. 材料保护, 2012, 45(5): 38-41.
【8】郭瑞光,王晓昌,耿志良,等. 环境友好型铝合金表面转化膜的制备及其耐蚀性能[J]. 材料保护, 2008, 41(12): 14-16.
【9】白锐, 丁晓莉, 肖雄,等. 一种新型环保铝合金无铬钝化处理液[J]. 广东化工, 2012, 39(6): 127-128.
【10】陈东初,黄柱周,李文芳. 铝合金表面无铬化学转化膜的研究[J]. 表面技术,2005,34(6):38-39.
【11】ANDREATTA F,TURCO A,GRAEVEL D,et al. SKPFM and SEM study of the deposition mechanism of Zr/Ti based pre-treatment on AA6016 aluminum alloy[J]. Surface & Coatings Teclmology,2007,201:7668-7685.
【12】LAHA P,SEHRAM T,TERRYN H. Use of spectroscopic elliPsometry to study Zr/Ti films on Al[J]. Surf Interface Anal,2002,34:677-680.
相关信息