聚乙二醇月桂酸单酯席夫碱基非离子型表面活性剂的合成及缓蚀性能
Synthesis and Inhibition Performance of Polyethylene Glycol (Peg) Lauric Acid Monoester Schiff Bases of Non-ionic Surface Active Ggent
摘 要
合成了三种对氨基苯甲酸席夫碱(A1,A2,A3)，利用硼酸酯化法合成聚乙二醇(400)月桂酸单酯，并将席夫碱与乙二醇月桂酸单酯经缩合反应合成三种聚乙二醇月桂酸单酯席夫碱基表面活性剂(B1,B2,B3)。通过红外光谱法对A1,A2,A3及B1,B2,B3进行结构表征，并测定了B1,B2,B3的表面活性。通过失重法，扫描电镜法对B1、B2、B3在模拟油田水中对碳钢的缓蚀性能进行研究。结果表明,三种表面活性剂都具有良好的缓蚀性能。随浓度的增大，缓蚀率逐渐增大，当浓度达到100 mg/L时缓蚀性能最好，可达80%以上，其缓蚀能力的大小为B3>B2>B1。
碳钢
缓蚀
模拟油田水
schiff base surfactants
carbon steel
corrosion inhibition
simulated oilfield water
Abstract
Three new kinds of p-aminobenzoic acid Schiff base (A1, A2, A3) were synthesized. Using boric acid esterification synthesized ethylene glycol mono-laurate. And the Schiff bases with polyethylene glycol mono-laurate were condensed into three polyethylene glycol mono-laurate Schiff base surfactants(B1, B2, B3).Infrared spectroscopy (IR) was used to analyze the structure of A1, A2, A3 and B1, B2, B3. And the surface activity of B1, B2 and B3 was measured. The weight loss method and scanning electron microscopy were used to study the corrosion inhibition performance of B1, B2 and B3 for carbon steel in oilfield water. Experimental results show that the three kinds of surfactants have good corrosion inhibition performance. With increasing concentration, corrosion inhibition rate increased gradually, when the concentration was 100 mg/L the inhibition performance was the best, reached more than 80%. the order of inhibition ability was B3>B2>B1.
中图分类号 TG174.42
所属栏目 试验研究
基金项目 国家自然科学基金(21266006); 广西自然科学基金(2012GXNSFAA053034); 广西矿冶与环境科学实验中心项目(KH2012ZD002)
收稿日期 2013/9/30
修改稿日期
网络出版日期
作者单位点击查看
联系人作者刘峥(lisa4.6@163.com)
备注刘峥(1962-),教授,博士,从事应用有机合成研究,
引用该论文: ZHANG Jing,LIU Zheng,LIU Jin,SHANG Wei. Synthesis and Inhibition Performance of Polyethylene Glycol (Peg) Lauric Acid Monoester Schiff Bases of Non-ionic Surface Active Ggent[J]. Corrosion & Protection, 2014, 35(8): 775
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张卫丽,李淑英. 表面活性剂的应用和发展[J]. 全面腐蚀控制,2005,19(6):1-1.
【2】赵建国,鲍宇,梁作舟. 表面活性剂的活性与其对金属缓蚀行为的关系[J]. 腐蚀科学与防护技术,2012,24(3):249-252.
【3】李俊,赵景茂. Gemini表面活性剂作为金属缓蚀剂的研究进展[J]. 腐蚀与防护,2011,32(7):543-547.
【4】姚志钢,李干佐,董凤兰,等. Gemini表面活性剂合成进展[J]. 化学进展,2004,16(3):349-364.
【5】杨许召,王军,李刚森,等. 离子液体型表面活性剂的研究进展[J]. 日用化学工业,2009,39(5):338-343.
【6】李杰,王晶,陈巧梅,等. 新型低聚表面活性剂的合成及其性能[J]. 石油与天然气化工,2010,39(1):60-64.
【7】袁淑军,吕春绪,蔡春. 一种新席夫碱型表面活性剂的合成及其表面活性[J]. 精细化工,2002,19(11):626-627.
【8】FENG Y Y,CHEN S H,YOU J M,et al. Investigation of alkylamine self-assembled films on iron electrodes by SEM,FT-IR,EIS and molecular simulations[J]. Electrochimica Acta,2007,53(4):1743-1753.
【9】MA H F,SONG T,SUN H,et al. Experimental and theoretical elucidation on the inhibition mechanism of 1-methyl-5-mercapto-1,2,3,4-tetrazole self-assembled films on corrosion of iron in 0.5 M H2SO4 Solutions[J]. Thin Solid Films,2008,516(6,30):1020-1024.
【10】韩晶. 氨基酸席夫碱类过渡金属超氧化物歧化酶模型化合物的设计、合成、表征及量子化学研究[D]. 大连:辽宁师范大学硕士学位论文,2008.
【11】吴宝庆,果学军,韩梅,等. 月桂酸单聚乙二醉醋的合成与研究[J]. 辽宁化工,1995,2(2):27-28.
【12】袁淑军. 新型金属络合性表面活性剂的合成、性质及应用研究[D]. 南京:南京理工大学博士学位论文,2003.
【13】YAN Y,LI W H,CAI L K,et al. Electrochemical and quantum chemical study of purines as corrosion inhibitors for mild steel in 1M HCl solution[J]. Electrochimica Acta,2008,53(7):5953-5960.
【14】郭卫. 咪唑啉缓蚀剂的合成及其缓蚀性能的研究[D]. 乌鲁木齐:新疆大学硕士学位论文,2004.
【2】赵建国,鲍宇,梁作舟. 表面活性剂的活性与其对金属缓蚀行为的关系[J]. 腐蚀科学与防护技术,2012,24(3):249-252.
【3】李俊,赵景茂. Gemini表面活性剂作为金属缓蚀剂的研究进展[J]. 腐蚀与防护,2011,32(7):543-547.
【4】姚志钢,李干佐,董凤兰,等. Gemini表面活性剂合成进展[J]. 化学进展,2004,16(3):349-364.
【5】杨许召,王军,李刚森,等. 离子液体型表面活性剂的研究进展[J]. 日用化学工业,2009,39(5):338-343.
【6】李杰,王晶,陈巧梅,等. 新型低聚表面活性剂的合成及其性能[J]. 石油与天然气化工,2010,39(1):60-64.
【7】袁淑军,吕春绪,蔡春. 一种新席夫碱型表面活性剂的合成及其表面活性[J]. 精细化工,2002,19(11):626-627.
【8】FENG Y Y,CHEN S H,YOU J M,et al. Investigation of alkylamine self-assembled films on iron electrodes by SEM,FT-IR,EIS and molecular simulations[J]. Electrochimica Acta,2007,53(4):1743-1753.
【9】MA H F,SONG T,SUN H,et al. Experimental and theoretical elucidation on the inhibition mechanism of 1-methyl-5-mercapto-1,2,3,4-tetrazole self-assembled films on corrosion of iron in 0.5 M H2SO4 Solutions[J]. Thin Solid Films,2008,516(6,30):1020-1024.
【10】韩晶. 氨基酸席夫碱类过渡金属超氧化物歧化酶模型化合物的设计、合成、表征及量子化学研究[D]. 大连:辽宁师范大学硕士学位论文,2008.
【11】吴宝庆,果学军,韩梅,等. 月桂酸单聚乙二醉醋的合成与研究[J]. 辽宁化工,1995,2(2):27-28.
【12】袁淑军. 新型金属络合性表面活性剂的合成、性质及应用研究[D]. 南京:南京理工大学博士学位论文,2003.
【13】YAN Y,LI W H,CAI L K,et al. Electrochemical and quantum chemical study of purines as corrosion inhibitors for mild steel in 1M HCl solution[J]. Electrochimica Acta,2008,53(7):5953-5960.
【14】郭卫. 咪唑啉缓蚀剂的合成及其缓蚀性能的研究[D]. 乌鲁木齐:新疆大学硕士学位论文,2004.
相关信息