Influence of Fe Content on Performance of Al-Zn-In-Cd Sacrificial Anode
摘 要
改变Al-Zn-In-Cd合金牺牲阳极杂质铁的含量, 在20 ℃天然海水中研究其电化学性能。采用4 d加速试验法测定了开路电位、闭路电位和电化学容量及电流效率,并采用循环伏安法研究了牺牲阳极的极化性能。结果表明,铁含量的变化对Al-Zn-In-Cd牺牲阳极开路电位以及闭路电位影响较小,而对牺牲阳极电流效率的影响较为显著。随着铁元素含量的增加,电流效率呈现下降趋势,但是在0.15%范围内仍可达到国标的要求,电流效率大于85%,且溶解形貌良好。循环伏安曲线表明,Al-Zn-In-Cd牺牲阳极极化性能良好。
Abstract
The electrochemical performance of Al-Zn-In-Cd sacrificial anodes with different concentrations of Fe was studied in natural seawater at 20 ℃. Open circuit potential, closed circuit voltage, electrochemical capacity and current efficiency were determined by 4 days accelerated experiment method. Cyclic voltammetry method was used to study the sacrificial anode polarization performance. The results showed that the open circuit potential and closed circuit voltage of the Al-Zn-In-Cd sacrificial anodes were affected little by Fe concentration, but the current efficiency was affected a lot. The current efficiency decreased as the concentration of Fe increased and was bigger than 85% when Fe concentration was not more than 0.15 %. And the dissolution morphology of all samples were good. Cycle volt-ampere curves showed that the Al-Zn-In-Cd sacrificial anode had good polarization performance.
中图分类号 TG174.41
所属栏目 试验研究
基金项目 国家科技重大专项(2008ZX05056-03-05)
收稿日期 2013/3/10
修改稿日期
网络出版日期
作者单位点击查看
备注张有慧(1982-),工程师,学士,从事金属腐蚀与防护工作,
引用该论文: ZHANG You-hui,SHI Da-li,ZHANG Lin,DU Min,CHENG Guo-dong,ZHAO Zen-yuan. Influence of Fe Content on Performance of Al-Zn-In-Cd Sacrificial Anode[J]. Corrosion & Protection, 2014, 35(9): 895
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】邢少华,姚萍,闰永贵,等. 合金元素对Al-Zn-In系牺牲阳极溶解行为的影响[J]. 腐蚀与防护,2008,29(12):717-719.
【2】王庆璋,杜敏. 海洋腐蚀与防护技术[M]. 青岛:青岛海洋大学出版社,2001,7:163-170.
【3】马丽杰,宋曰海,郭忠诚,等. Al-Zn-In-Cd牺牲阳极材料的电化学性能研究[J]. 材料开发与应用,2004,3(2):32-34.
【4】齐公台,张盈盈. 电池用含稀土铝合金阳极性能的研究[J]. 稀有金属,2004,28(6):1010-1014.
【5】齐公台,郭稚弧,林汉同,等. 腐蚀保护常用的几种牺牲阳极材料[J]. 材料开发与应用,2001,16(1):73-83.
【6】宋曰海,郭忠诚,樊爱民,等. 牺牲阳极材料的研究现状[J]. 腐蚀科学与防护技术,2004,16(1):24-28.
【7】张信义,王元玺. Al-Zn-Mg-In-Ga-Ca合金牺牲阳极电化学性能的研究[J]. 腐蚀科学与防护技术,1995,7(1):53-57.
【8】马景灵,文九巴,李光福,等. 含Mn元素的铝合金牺牲阳极材料的研究[J]. 金属热处理,2008,33(8):57-59.
【9】浦志强. 铝合金牺牲阳极的研究方法[J]. 建材与装饰,2008:206-207.
【10】印飞,杨江波,孙宝德. 高含铁量铝硅合金中铁相的凝固行为与形貌控制[J]. 上海交通大学学报,2002,36(1):43-50.
【11】SAIDMAN S B. Electrochemical behavior of Al-In alloy in chloride solutions[J]. Applied electrochemistry,1995,25:252-258.
【12】DNV-RP-B401Cathodic potection design[S].
【2】王庆璋,杜敏. 海洋腐蚀与防护技术[M]. 青岛:青岛海洋大学出版社,2001,7:163-170.
【3】马丽杰,宋曰海,郭忠诚,等. Al-Zn-In-Cd牺牲阳极材料的电化学性能研究[J]. 材料开发与应用,2004,3(2):32-34.
【4】齐公台,张盈盈. 电池用含稀土铝合金阳极性能的研究[J]. 稀有金属,2004,28(6):1010-1014.
【5】齐公台,郭稚弧,林汉同,等. 腐蚀保护常用的几种牺牲阳极材料[J]. 材料开发与应用,2001,16(1):73-83.
【6】宋曰海,郭忠诚,樊爱民,等. 牺牲阳极材料的研究现状[J]. 腐蚀科学与防护技术,2004,16(1):24-28.
【7】张信义,王元玺. Al-Zn-Mg-In-Ga-Ca合金牺牲阳极电化学性能的研究[J]. 腐蚀科学与防护技术,1995,7(1):53-57.
【8】马景灵,文九巴,李光福,等. 含Mn元素的铝合金牺牲阳极材料的研究[J]. 金属热处理,2008,33(8):57-59.
【9】浦志强. 铝合金牺牲阳极的研究方法[J]. 建材与装饰,2008:206-207.
【10】印飞,杨江波,孙宝德. 高含铁量铝硅合金中铁相的凝固行为与形貌控制[J]. 上海交通大学学报,2002,36(1):43-50.
【11】SAIDMAN S B. Electrochemical behavior of Al-In alloy in chloride solutions[J]. Applied electrochemistry,1995,25:252-258.
【12】DNV-RP-B401Cathodic potection design[S].
相关信息