4340合金钢电刷镀镉工艺的应用
Application of Electric-brush Plating Cadmium Porcess to 4340 Steel
摘 要
通过试验确定了4340合金钢电刷镀镉修复工艺的工艺流程及镀镉后钝化溶液的配方。镉镀层耐蚀性、氢含量以及结合力的检测结果表明, 电刷镀镉是一种耐腐蚀、结合力良好、低氢脆的工艺方法, 作为电镀镉层局部损伤后的修补镀层工艺, 解决了钢类零件电镀镉层损伤后零件局部耐蚀性下降的难题。
氢脆
耐蚀性
brush-plating cadmium
hydrogen brittleness
anti-corrosion property
Abstract
The technological process and passivating solution of electric-brush plating cadmium on 4340 steel were determined by tests. The results show that electric-brush plating cadmium is a technological method with anti-corrosion, good adherence and low hydrogen brittleness proved by the tests on corrosion performance, hydrogen content and adherence. As a local repair process, this technology can resolve the problem of local reduction in corrosion resistance of steel parts with plated Cd.
中图分类号 TG178
所属栏目 应用技术
基金项目
收稿日期 2013/11/16
修改稿日期
网络出版日期
作者单位点击查看
备注李海宏(1979-), 高级工程师, 硕士, 从事表面处理工艺应用研究,
引用该论文: ZHANG Xu,WANG Rui,SONG Yu-sheng,LI Hai-hong. Application of Electric-brush Plating Cadmium Porcess to 4340 Steel[J]. Corrosion & Protection, 2014, 35(10): 1037
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】章葆澄. 电镀工艺学[M]. 北京: 北京航空航天大学出版社, 1993.
【2】林玉珍, 杨德均. 腐蚀和腐蚀控制原理[M]. 北京: 中国石化出版社, 2007.
【3】马亚军, 朱张校. 电刷镀技术研究的最新进展[J]. 表面技术, 2001, 12: 21-23.
【4】李会录, 余竹焕, 李颖, 等. 高强钢氢脆敏感性和氢致附加应力的相关性[J]. 腐蚀与防护, 2009, 20(10): 801-803.
【5】李金桂. 现代表面工程设计手册[M]. 北京: 国防工业出版社, 2000.
【2】林玉珍, 杨德均. 腐蚀和腐蚀控制原理[M]. 北京: 中国石化出版社, 2007.
【3】马亚军, 朱张校. 电刷镀技术研究的最新进展[J]. 表面技术, 2001, 12: 21-23.
【4】李会录, 余竹焕, 李颖, 等. 高强钢氢脆敏感性和氢致附加应力的相关性[J]. 腐蚀与防护, 2009, 20(10): 801-803.
【5】李金桂. 现代表面工程设计手册[M]. 北京: 国防工业出版社, 2000.
相关信息