Analysis on Cracking Reason of Rolling Tube of Titanium Alloy TA10
摘 要
某两批次的TA10钛合金材料在轧制25 mm×1.65 mm管的过程中, 在半成品和成品的内外表面出现了不满足标准要求的裂纹和缺陷。通过对材料进行理化检验及分析得出: 镍、钼偏析使材料的物理性能不均匀, 是产生该现象的根本原因。在熔炼过程中采用中间合金TiMo和 TiNi作为配料溶入铸锭可以得到物理性能均匀、偏析程度低的TA10材料。
Abstract
In rolling process of 25 mm×1.65 mm tube of titanium alloy TA10, there were some cracks and defects which did not meet the standard requirements on the inner and outer surface of semi-finished and finished tubes. Through physical testing and chemical analysis on the material, the reason of the phenomenon was due to segregation of Ni and Mo caused uneven physical properties of materials. In the melting process, TiNi and TiMo was added into ingot casting as middle alloy, TA10 ingot with uniform physical properties and small segregation was obtained.
中图分类号 TG146.2+3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/5/10
修改稿日期
网络出版日期
作者单位点击查看
备注马红征(1969-), 女, 教授级高级工程师, 学士。
引用该论文: MA Hong-zheng,HUANG Zhang-hong,QU Heng-lei,HE Wei,NAN Li,YANG Ya-she,ZHU Kang-ping. Analysis on Cracking Reason of Rolling Tube of Titanium Alloy TA10[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(3): 223~226
马红征,黄张红,曲恒磊,何伟,南莉,杨亚社,朱康平. 轧制TA10钛合金管开裂原因分析[J]. 理化检验-物理分册, 2014, 50(3): 223~226
被引情况:
【1】何春艳,张嫦娟,冯辉,朱康平,祝建雯, "钛管生产用可靠性检验方法初探",理化检验-物理分册 51, 181-183(2015)
【2】李荣,魏东,许陆,武晶晶, "外科植入用TA3钛合金接骨板断裂失效分析",理化检验-物理分册 52, 897-899(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郭会民.钛合金焊接技术在燃料储罐上的应用[J].火箭推进, 2008, 34(4):38-42.
【2】高平, 赵永庆, 毛小南, 等.钛合金铸锭偏析规律的研究进展[J].钛工业进展, 2009, 26(1):1-5.
【3】莫畏.钛的金属学和热处理[M].北京: 冶金工业出版社, 2009:22.
【2】高平, 赵永庆, 毛小南, 等.钛合金铸锭偏析规律的研究进展[J].钛工业进展, 2009, 26(1):1-5.
【3】莫畏.钛的金属学和热处理[M].北京: 冶金工业出版社, 2009:22.
相关信息