Reasons Analysis on Leakage of TU2 Copper Tubes
摘 要
某公司在检漏工序中发现其生产的空调制冷用TU2铜管存在泄漏现象, 泄漏比例约为20%, 泄漏位置随机分布。采用断口分析、金相检验及氧含量测定等方法, 对TU2铜管的泄漏原因进行了分析。结果表明: 由于泄漏铜管中存在颗粒状沿晶分布的(α+Cu2O)共晶体, 在高温长时间H2保护的焊接环境中产生氢脆, 形成沿晶微裂纹, 继而在试压过程的压力作用下发生泄漏。
Abstract
Leakage was found for air conditioner refrigeration TU2 copper tubes produced by a company during leakage detection process. The ratio of leakage was up to 20% and the leakage locations distributed in random. Means such as fracture analysis, metallographic examination and oxygen content determination were used to analyze leakage reasons of the TU2 copper tubes. The results show that there was (α+Cu2O) eutectic distributing along the grain boundary of the leakage tubes, which caused hydrogen embrittlement with forming micro-cracks along the grain boundary in high temperature H2 atmosphere. So leakage occurred to the TU2 copper tubes under pressure of the leakage detection process.
中图分类号 TG142.45
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/5/16
修改稿日期
网络出版日期
作者单位点击查看
备注巴发海(1966-),男,教授级高级工程师,博士。
引用该论文: BA Fa-hai,CHAI Ze,CHEN Jun-wei. Reasons Analysis on Leakage of TU2 Copper Tubes[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(4): 306~309
巴发海,柴泽,陈俊伟. TU2铜管泄漏原因分析[J]. 理化检验-物理分册, 2014, 50(4): 306~309
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Q/BKJ024-2008制冷系统用铜管入厂检验标准[S].
【2】熊双奎,王顺兴. 空调制冷铜管在使用过程中常出现的问题[J]. 有色金属加工,2009,38(1):35-38.
【3】机械工业理化检验人员技术培训和资格鉴定委员会. 金相检验[M]. 北京: 中国计量出版社, 2008: 228.
【4】刘淑凤,王永兰,张智慧. 无氧铜弯头开裂分析[J]. 理化检验-物理分册,2008,44(9):504-506.
【5】张宝昌. 有色金属及其热处理[M]. 北京: 国防工业出版社, 1981: 132.
【2】熊双奎,王顺兴. 空调制冷铜管在使用过程中常出现的问题[J]. 有色金属加工,2009,38(1):35-38.
【3】机械工业理化检验人员技术培训和资格鉴定委员会. 金相检验[M]. 北京: 中国计量出版社, 2008: 228.
【4】刘淑凤,王永兰,张智慧. 无氧铜弯头开裂分析[J]. 理化检验-物理分册,2008,44(9):504-506.
【5】张宝昌. 有色金属及其热处理[M]. 北京: 国防工业出版社, 1981: 132.
相关信息