Metallographic Sample Preparation Method of Commercial Pure Titanium TA1
摘 要
针对工业纯钛TA1的金相制样方法进行了研究, 对比了机械抛光和电解抛光两种方法的抛光效果, 得到了机械抛光和电解抛光的最佳工艺参数。结果表明: 经4次机械抛光+化学侵蚀, 或在高氯酸+冰醋酸(体积比6∶94)电解液中60 V电压下电解抛光14 s, 均可得到无变形孪晶的显微组织; 但电解抛光相比机械抛光时间更短, 效率更高, 得到的显微组织形貌图质量也更好。
Abstract
The metallographic sample preparation method of commercial pure titanium TA1 was studied, and by comparing the polishing effect of mechanical polishing and electrolytic polishing, the optimal technological parameters of these two polishing methods were obtained. The results show that microstructure without deformation twin could be obtained through mechanical polishing adding chemical erosion for 4 times, or electrolytic polishing in perchlorate and glacial acetic acid with volume ratio of 6∶94 and electrolytic voltage of 60 V for 14 s. However, the efficiency of electrolytic polishing method was higher than that of the mechanical polishing method, and the obtained microstructure also showed better.
中图分类号 TG146.2+3 TG115.21+1.2
所属栏目 试验技术与方法
基金项目
收稿日期 2014/5/12
修改稿日期
网络出版日期
作者单位点击查看
备注夏雯(1982-),女,工程师,硕士。
引用该论文: XIA Wen,LIU Shu-feng,LI Yan,ZHANG Li-min. Metallographic Sample Preparation Method of Commercial Pure Titanium TA1[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(8): 578~579
夏雯,刘淑凤,李岩,张丽民. 工业纯钛TA1的金相制样方法[J]. 理化检验-物理分册, 2014, 50(8): 578~579
被引情况:
【1】李笑,王田, "纯钛丝脆断原因分析",理化检验-物理分册 52, 66-70(2016)
【2】郑艺,郭伟,丁洪生,付铁,张静武, "不同状态AZ80镁合金的金相试样制备方法",理化检验-物理分册 51, 477-479(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王怀柳. 工业纯钛TA1板材的研制[J]. 特钢技术,2008,14(57):7-9.
【2】余存烨. 钛及钛合金的金相制样实用技术与经验[J]. 理化检验-物理分册,2001,37(2):61-63.
【3】郭宇航,金云学,张丽华, 等. 金属电子背散射衍射试样的制备技术[J]. 理化检验-物理分册,2007,43(8): 399-403.
【4】王耿洁,赵西成,杨西荣, 等. 热轧TA1钛的电子背散射衍射分析[J]. 材料导报,2012,26(7):122-125.
【2】余存烨. 钛及钛合金的金相制样实用技术与经验[J]. 理化检验-物理分册,2001,37(2):61-63.
【3】郭宇航,金云学,张丽华, 等. 金属电子背散射衍射试样的制备技术[J]. 理化检验-物理分册,2007,43(8): 399-403.
【4】王耿洁,赵西成,杨西荣, 等. 热轧TA1钛的电子背散射衍射分析[J]. 材料导报,2012,26(7):122-125.
相关信息