螺杆泵主轴裂纹分析
Analysis on Crack in Main Spindle of Screw Pump
摘 要
某公司生产的螺杆泵主轴在运行过程中发生漏水, 磁粉探伤表明沿圆盘根部有裂纹。采用化学成分分析、力学性能试验、金相检验、扫描电镜观察等方法对裂纹形成原因进行分析。结果表明: 螺杆泵主轴失效的主要原因是过渡圆弧角较小, 导致应力集中, 促使疲劳裂纹形成。
主轴
疲劳裂纹
应力集中
screw pump
main spindle
fatigue cracks
stress concentration
Abstract
Leakage occurs during operation, the magnetic particle inspection found that there was a crack at the root of spindle. By means of chemical composition analysis, mechanical property testing, metallographic examination and scanning electron microscopy observation, the crack reason were analyzed. The results showed that the screw spindle cracking formed due to the unreasonable arc transition design of main spindle, and led to stress concentration to accelerate the fatigue process.
中图分类号 TH131.3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/9/17
修改稿日期
网络出版日期
作者单位点击查看
备注王立辉(1979-), 男, 高级工程师, 硕士。
引用该论文: WANG Li-hui,ZOU Ben-ren,LI Hui. Analysis on Crack in Main Spindle of Screw Pump[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(9): 685～687
王立辉,邹本仁,李辉. 螺杆泵主轴裂纹分析[J]. 理化检验－物理分册, 2014, 50(9): 685～687
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杜秀华,孟庆武,何富君.抽油机井油管断裂失效性质的判断[J].石油机械,2000, 28(3): 23-25.
【2】桂立丰.机械工程材料测试手册——物理金相卷[M].沈阳: 辽宁科学技术出版社, 1999.
【3】马小明,熊烨.高压水泵主轴断裂失效分析[J].石油化工设备技术,2010, 31(4): 35-37.
【4】李凤娥,徐绍勇,龙思远.轮辐过渡圆角对轮毂服役应力集中的影响[J].计算机应用技术——特种铸造及有色合金,2007, 27(11): 841-842.
【5】陈渝.汽车发动机曲轴断裂失效分析[J].理化检验-物理分册,2012, 48(8): 551-554.
【2】桂立丰.机械工程材料测试手册——物理金相卷[M].沈阳: 辽宁科学技术出版社, 1999.
【3】马小明,熊烨.高压水泵主轴断裂失效分析[J].石油化工设备技术,2010, 31(4): 35-37.
【4】李凤娥,徐绍勇,龙思远.轮辐过渡圆角对轮毂服役应力集中的影响[J].计算机应用技术——特种铸造及有色合金,2007, 27(11): 841-842.
【5】陈渝.汽车发动机曲轴断裂失效分析[J].理化检验-物理分册,2012, 48(8): 551-554.
相关信息