充气阀组件壳体断裂分析
Fracture Analysis of Charging Valve Shell
摘 要
某型直升机用气源装置T6态7A09铝合金充气阀组件壳体与气瓶连接的螺纹退刀槽根部发生断裂。结合气源装置的存储条件、使用及断裂情况, 通过断口分析、化学成分分析、金相检验、硬度测试等方法, 对失效现象进行了系统的分析。结果表明: 失效原因是应力腐蚀断裂, 并从原材料选择和腐蚀防护等方面提出了针对性建议。
7A09铝合金
壳体
应力腐蚀断裂
charging valve
aluminum alloy 7A09
shell
stress corrosion fracture
Abstract
Fracture occurred in the thread relief groove root of charging valve shell of a type of gas supply devices applied to helicopter connected to the cylinder shell. The charging valve shell was produced by aluminum alloy 7A09, T6 state. A study was conducted by means of fracture analysis, chemical composition analysis, metallographic examination, hardness testing, and combined with the storage, use and fracture conditions of gas supply devices. The results showed that the fracture of charging valve shell was attributed to the stress corrosion. According to the experiment results, measures had been suggested to prevent such failure.
中图分类号 V252.2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/9/15
修改稿日期
网络出版日期
作者单位点击查看
备注王宣(1985-), 女, 工程师。
引用该论文: WANG Xuan,MA Yan-qing,WANG Bin,LU Meng. Fracture Analysis of Charging Valve Shell[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(9): 696～698
王宣,马燕青,王斌,卢猛. 充气阀组件壳体断裂分析[J]. 理化检验－物理分册, 2014, 50(9): 696～698
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】韩德伟.金属硬度检测技术手册[M].长沙: 中南大学出版社, 2003.
【2】刘立春, 韩露, 何涛, 等.LF3铝合金导管应力腐蚀分析[J].材料工程, 2003(增刊1): 66-71.
【3】白明远, 马海全, 曲士昱, 等.铝合金框开裂的失效分析[J].装备环境工程, 2011, 8(2): 1-3.
【4】张栋, 钟培道, 陶春虎, 等.失效分析[M].北京: 国防工业出版社, 2008.
【5】《中国航空材料手册》编辑委员会.中国航空材料手册.第3卷: 铝合金 镁合金[M].北京: 中国标准出版社, 2002.
【2】刘立春, 韩露, 何涛, 等.LF3铝合金导管应力腐蚀分析[J].材料工程, 2003(增刊1): 66-71.
【3】白明远, 马海全, 曲士昱, 等.铝合金框开裂的失效分析[J].装备环境工程, 2011, 8(2): 1-3.
【4】张栋, 钟培道, 陶春虎, 等.失效分析[M].北京: 国防工业出版社, 2008.
【5】《中国航空材料手册》编辑委员会.中国航空材料手册.第3卷: 铝合金 镁合金[M].北京: 中国标准出版社, 2002.
相关信息