Effect of Sampling Positions on Stress Rupture Properties at Elevated Temperature of K002 Cast Superalloy Blades
摘 要
通过对K002铸造高温合金叶片高温持久试样的取样位置与叶片原来和现在两种不同的组合方式测得的高温持久性能数据和显微组织差异进行对比分析,发现现在的组合方式测得的高温持久性能更能代表实际叶片的性能。因为现组合方式的高温持久试样不易产生明显的组织疏松等铸造缺陷,试验结果均能达到规范要求,且有较大富余量,较好地解决了由于试样的铸造缺陷导致的高温持久试验结果不合格的问题。
Abstract
Through contrastively analyzing the differences of stress rupture properties at elevated temperature and microstructure of samples with original and current combination to the blades, it was found that the tested stress rupture properties of samples with current combination to the blades could represent the actual performance of the blades better that than that of the original combination. Because the stress rupture samples with current combination had no microporosity defect, the test results could meet the requirement of specification with more stock. By changing the sampling position, problem that the stress rupture properties test results were not acceptable caused by the test samples having casting defect was well solved.
中图分类号 TG115.5+7
所属栏目 试验与研究
基金项目
收稿日期 2013/11/7
修改稿日期
网络出版日期
作者单位点击查看
备注陆琪(1964-),女,研究员级高级工程师。
引用该论文: LU Qi,CHEN Jian-wei,GUO Zi-jing,LIU Wei,HUANG Yu-jiao,XU Jiang. Effect of Sampling Positions on Stress Rupture Properties at Elevated Temperature of K002 Cast Superalloy Blades[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(10): 735~737
陆琪,陈建伟,郭子静,刘伟,黄玉娇,徐江. K002铸造高温合金叶片取样位置对高温持久性能的影响[J]. 理化检验-物理分册, 2014, 50(10): 735~737
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】《中国航空材料手册》编辑委员会. 中国航空材料手册 第2卷:变形高温合金 铸造高温合金[M]. 北京: 中国标准出版社,2002.
【2】韩宏. 六联体导向叶片无余量精铸技术研究[J]. 铸造,2011,60(11):1137-1140.
【3】高成薇,于兴福,黄爱华,等. 型壳预热机浇注温度对某联体叶片铸造成形性的影响[J]. 铸造,2012,61(8):882-885.
【4】洪力,吴洪生,徐明华. 高温持久试验的若干影响因素[J]. 理化检验-物理分册,2012,48(2):117-119.
【5】田广明. 试样加工对金属材料拉伸性能的影响[J]. 理化检验-物理分册,2011,47(6):365-367.
【2】韩宏. 六联体导向叶片无余量精铸技术研究[J]. 铸造,2011,60(11):1137-1140.
【3】高成薇,于兴福,黄爱华,等. 型壳预热机浇注温度对某联体叶片铸造成形性的影响[J]. 铸造,2012,61(8):882-885.
【4】洪力,吴洪生,徐明华. 高温持久试验的若干影响因素[J]. 理化检验-物理分册,2012,48(2):117-119.
【5】田广明. 试样加工对金属材料拉伸性能的影响[J]. 理化检验-物理分册,2011,47(6):365-367.
相关信息