Indication Analysis on Magnetic Particle Testing for Metering Valve of 9Cr18 Stainless Steel
摘 要
针对9Cr18不锈钢计量活门在磁粉检测过程中出现的线性磁痕显示,结合微观检验对磁痕形成的原因进行了分析。结果表明:组织中存在的铬偏析条带是造成磁粉探伤时出现线性显示的原因。
Abstract
The linear indication was detected on the surface of metering valve of 9Cr18 stainless steel in magnetic particle testing process, and the reason of linear indication was analyzed by microstructure examination. The results showed that the indication was caused by chromium segregation.
中图分类号 TG115.28+4
所属栏目 试验与研究
基金项目
收稿日期 2013/10/18
修改稿日期
网络出版日期
作者单位点击查看
备注王树志(1980-),男,工程师。
引用该论文: WANG Shu-zhi,JIA Yu-jun,YE Guan-ting,REN Xue-dong,QIAO Hai-yan. Indication Analysis on Magnetic Particle Testing for Metering Valve of 9Cr18 Stainless Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(11): 800~802
王树志,贾玉军,叶冠霆,任学冬,乔海燕. 9Cr18不锈钢计量活门磁粉检测磁痕分析[J]. 理化检验-物理分册, 2014, 50(11): 800~802
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】申坤,许东.9Cr18马氏体不锈钢的亚温淬火[J].热处理技术与装备,2011,33(3):19-22.
【2】李孟喜,龚建勋,李生新.大直径不锈钢轴承套圈热处理工艺分析[J].轴承,2010(7):42-44.
【3】王玉金,叶健熠,李红,等.9Cr18不锈钢轴承的加工[J].轴承,2005(3):10-13.
【4】国防科技工业无损检测人员资格鉴定与认证培训教材编审委员会.磁粉检测[M].北京:机械工业出版社,2004:98.
【5】霍连喆,赵鹏飞,孙丽坤,等.Cr8钢的动态再结晶行为及组织转变[J].理化检验-物理分册,2012,48(10):640-664.
【6】安治国,侯环宇,付成安,等.常化退火处理对无取向硅钢组织和织构的影响[J].理化检验-物理分册,2013,49(2):640-664.
【2】李孟喜,龚建勋,李生新.大直径不锈钢轴承套圈热处理工艺分析[J].轴承,2010(7):42-44.
【3】王玉金,叶健熠,李红,等.9Cr18不锈钢轴承的加工[J].轴承,2005(3):10-13.
【4】国防科技工业无损检测人员资格鉴定与认证培训教材编审委员会.磁粉检测[M].北京:机械工业出版社,2004:98.
【5】霍连喆,赵鹏飞,孙丽坤,等.Cr8钢的动态再结晶行为及组织转变[J].理化检验-物理分册,2012,48(10):640-664.
【6】安治国,侯环宇,付成安,等.常化退火处理对无取向硅钢组织和织构的影响[J].理化检验-物理分册,2013,49(2):640-664.
相关信息