65Mn钢锁片断裂分析
Fracture Analysis of 65Mn Locking Plate
摘 要
通过宏观检验、化学成分分析、硬度测试、金相检验和断口分析等方法,对65Mn钢锁片在装配过程中出现断裂的原因进行了分析。结果表明:断裂锁片由于热处理时回火工艺不当,产生了回火脆性,在装配外力作用下导致锁片发生了脆性断裂。据此提出了采取调整回火工艺参数的措施,从而消除了回火脆性,锁片在装配过程中再未出现断裂现象,确保了产品质量。
锁片
回火脆性
断裂
热处理
65Mn steel
locking plate
temper brittleness
fracture
heat treatment
Abstract
The fracture reason of 65Mn locking plate in assembly process was analyzed by means of macroscopic examination, chemical composition analysis, hardness testing, metallographic examination, fracture analysis and so on. The results showed that the brittle fracture appeared in locking plate under assembly force due to temper brittleness caused by improper tempering processing in heat treatment. By adjusting the tempering process parameters, the temper brittleness was eliminated. Now locking plate in assembly process is normal, the product quality is ensured.
中图分类号 U463.1
所属栏目 质量控制与失效分析
基金项目 国家科技支撑计划(2011BAG03B04)
收稿日期 2013/10/30
修改稿日期
网络出版日期
作者单位点击查看
备注杨当友(1963-),男,高级工程师,工学学士。
引用该论文: YANG Dang-you. Fracture Analysis of 65Mn Locking Plate[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(11): 826～828
杨当友. 65Mn钢锁片断裂分析[J]. 理化检验－物理分册, 2014, 50(11): 826～828
被引情况:
【1】张海峰, "方钢管断裂原因分析",理化检验－物理分册 51, 908-910(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王广生．金属热处理缺陷分析及案例[M]．北京：机械工业出版社,2001:445-448.
【2】戚正风．金属热处理原理[M]．北京：机械工业出版社,1986:176-179.
【2】戚正风．金属热处理原理[M]．北京：机械工业出版社,1986:176-179.
相关信息