Analysis on Internal Defects in Rotor of 34CrMo1A Steel
摘 要
34CrMo1A钢转子在制造过程中经超声波探伤发现内部有缺陷,采用宏观检验、金相检验、化学成分分析及断口分析等方法,对转子内部缺陷的类型进行了分析。结果表明:转子内部缺陷性质为白点,其微观断口形貌呈现典型的四周放射状条纹的白点特征,且伴有氧化铝类夹杂物。该批转子氢含量偏高是产生白点缺陷的主要原因。
Abstract
The internal defects were found by ultrasonic testing in manufacturing process of 34CrMo1A rotor. The internal flaw type of rotor was analyzed by means of macroscopic examination, metallographic examination, chemical composition analysis, fracture analysis and so on. The results showed that the type of internal defects was flake, whose micro fractography showed as radial stripes typical characteristics of flake, and alumina inclusions were also found in the rotor. The high content of residual hydrogen in rotor was the main reason of flake defect.
中图分类号 TG142.1+3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/11/1
修改稿日期
网络出版日期
作者单位点击查看
备注王明建(1987-),男,助理工程师,硕士。
引用该论文: WANG Ming-jian,LI Xue-feng,GUO Hai-xia. Analysis on Internal Defects in Rotor of 34CrMo1A Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(11): 832~834
王明建,李雪峰,郭海霞. 34CrMo1A钢转子内部缺陷分析[J]. 理化检验-物理分册, 2014, 50(11): 832~834
被引情况:
【1】王长健, "42CrMo钢轮毂锻件超声波探伤缺陷分析",理化检验-物理分册 52, 136-138(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李国华,吴淼.现代无损检测与评价[M].北京:化学工业出版社,2009.
【2】康大韬,叶国斌.大型锻件材料及热处理[M].上海:龙门书局,1998:110.
【3】赵晗,周小明,陈栋,等.GCr15轴承钢的白点特征[J].理化检验-物理分册,2005,41(1):17-18.
【4】索会迎.超声波无损检测技术应用研究[D].南京:南京邮电大学,2012.
【5】庞钧.大型铸锻件缺陷分析图谱[M].北京:机械工业出版社,1990.
【6】崔忠圻,覃耀春.金属学与热处理[M].北京:机械工业出版社,2007.
【2】康大韬,叶国斌.大型锻件材料及热处理[M].上海:龙门书局,1998:110.
【3】赵晗,周小明,陈栋,等.GCr15轴承钢的白点特征[J].理化检验-物理分册,2005,41(1):17-18.
【4】索会迎.超声波无损检测技术应用研究[D].南京:南京邮电大学,2012.
【5】庞钧.大型铸锻件缺陷分析图谱[M].北京:机械工业出版社,1990.
【6】崔忠圻,覃耀春.金属学与热处理[M].北京:机械工业出版社,2007.
相关信息