Burst Analysis on High Temperature Superheated Pipe of 12Cr1MoV Steel
摘 要
某电厂的12Cr1MoV钢高温段过热器管在使用2 a(年)后发生爆裂。采用宏观和微观分析方法分析了爆裂的原因。结果表明:由于管壁穿孔引起锅炉的汽水循环不畅,高温过热器管局部超温运行,导致管材发生高温腐蚀及珠光体完全球化,引发多处横裂源,进一步导致两处发生同一径向的纵裂。
Abstract
A high temperature superheated pipe of 12Cr1MoV steel bursted after using for two years in a power plant. The burst reason was analyzed by means of macroscopic and microscopic examination. The results indicated that because of pipe wall perforation, the steam and water cycle was stumbled, the pipe had been operated under local overtemperature, which caused high temperature local corrosion and peralite spheroidization, many transverse fissures generated and the two longitudinal divisions was produced in the same radial direction.
中图分类号 TK223.1+1
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/3/26
修改稿日期
网络出版日期
作者单位点击查看
备注潘红涛(1971-),女,高级工程师,学士。
引用该论文: PAN Hong-tao. Burst Analysis on High Temperature Superheated Pipe of 12Cr1MoV Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(11): 842~844
潘红涛. 12Cr1MoV钢高温过热器管爆裂分析[J]. 理化检验-物理分册, 2014, 50(11): 842~844
被引情况:
【1】卢书媛,王卫忠,俞璐,徐海斌,朱一波, "锅炉过热器管爆裂原因分析",理化检验-物理分册 52, 807-810(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郭鲁阳,孙旭光,刘志超,等.锅炉水冷壁高温腐蚀原因分析及预防对策[J].中国电力, 2000,33(11):17-20.
【2】曾汉才.大型锅炉水冷壁的高温腐蚀故障分析[J].华中电力,2001,14(4):5-8.
【3】宋维锡.金属学[M].北京:冶金工业出版社,1989.
【4】朱日彰.金属腐蚀学[M].北京: 冶金工业出版社,1989.
【5】陈韶瑜.二级过热器管失效分析[J].天津电力技术,2004,14(4):37-39.
【2】曾汉才.大型锅炉水冷壁的高温腐蚀故障分析[J].华中电力,2001,14(4):5-8.
【3】宋维锡.金属学[M].北京:冶金工业出版社,1989.
【4】朱日彰.金属腐蚀学[M].北京: 冶金工业出版社,1989.
【5】陈韶瑜.二级过热器管失效分析[J].天津电力技术,2004,14(4):37-39.
相关信息