N80油管断裂分析
Fracture Analysis of N80 Tubing
摘 要
采用化学成分分析、力学性能测试、受力分析、宏观及微观检验等手段对N80油管断裂的原因进行了分析。结果表明:该油管断裂的主要原因是在抽油机杆往复运动的过程中,管柱薄弱环节产生疲劳损伤,导致油管疲劳部位所承受的载荷超过了其承载能力,最终在外加拉应力的作用下发生断裂。
断裂
疲劳
交变载荷
tubing
fracture
fatigue
alternating load
Abstract
The fracture reason of N80 tubing was analyzed by means of chemical composition analysis, mechanical property testing, stress analysis, macro and micro examination. The results showed that the fatigue damage occurred in the weak positions of tubing in the process of reciprocating motion of oil pumping rod, then the load of tubing fatigue part exceeded the carrying capacity, at last the tubing fractured under the external tensile stress.
中图分类号 TE931+.2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/11/16
修改稿日期
网络出版日期
作者单位点击查看
备注孙蕊(1988-),女,硕士研究生。
引用该论文: SUN Rui,ZHANG Jun,WANG Wen-dong. Fracture Analysis of N80 Tubing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(11): 860～862
孙蕊,张钧,王温栋. N80油管断裂分析[J]. 理化检验－物理分册, 2014, 50(11): 860～862
被引情况:
【1】赵向杰,王温栋, "某输气管线穿孔原因分析",理化检验－物理分册 52, 584-588(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】何迪,周思柱,黄天成.油管失效判据的理论研究［J］.湖北工学院学报,2004(3):128-129.
【2】何富君,常忠伟,何富云,等.抽油机井油管柱断裂失效特征分析［J］.石油矿场机械,2005(5):48-51.
【3】束德林.工程材料力学性能［M］.北京:机械工业出版社,2011:1-2,22.
【4】陈传尧.疲劳与断裂［M］.武汉:华中科技大学出版社,2001:7-9.
【2】何富君,常忠伟,何富云,等.抽油机井油管柱断裂失效特征分析［J］.石油矿场机械,2005(5):48-51.
【3】束德林.工程材料力学性能［M］.北京:机械工业出版社,2011:1-2,22.
【4】陈传尧.疲劳与断裂［M］.武汉:华中科技大学出版社,2001:7-9.
相关信息