Ultrasonic Testing for High Pressure Heater Transfer Tube Weld in Expanding Area
摘 要
某设备制造厂在进行某核电厂高压加热器完工后的气密性试验及水压试验过程中,发现个别管板胀接区域传热管存在泄漏现象。经相关试验及分析确定,所采用的TP439传热管具有缺口敏感特性,焊缝中个别未超标缺陷在胀接压力下扩大,从而导致泄漏。笔者介绍了针对此种传热管胀管区域焊缝的超声检测技术。
Abstract
An equipment manufacturer found some leakage in the transfer tube expanding area during the process of air tightness and hydrostatic tests for one High Pressure Heaters, it proved that the tube material TP439 was susceptive of notch, and some tiny flaws in weld expand under the pressure of expanding, and resulting in leakage. This article focuses on the ultrasonic testing technology for transfer tube weld in expanding area.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2013/3/5
修改稿日期
网络出版日期
作者单位点击查看
备注袁光华(1979-),男,工程师,学士,主要从事核电超声检测技术研究及应用。
引用该论文: YUAN Guang-hua,ZHOU Lu-sheng,ZHANG Guo-feng,JIN De-rong. Ultrasonic Testing for High Pressure Heater Transfer Tube Weld in Expanding Area[J]. Nondestructive Testing, 2014, 36(1): 32~34
袁光华,周路生,张国丰,金德荣. 高压加热器传热管胀管区焊缝超声检测[J]. 无损检测, 2014, 36(1): 32~34
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】RSEM SA-803/SA-803M(1998)给水加热器用焊接铁素体不锈钢管[S].
【2】RSEM A450/A450M碳钢、铁素体合金钢和奥氏体合金钢管(T)通用要求[S].
【2】RSEM A450/A450M碳钢、铁素体合金钢和奥氏体合金钢管(T)通用要求[S].
相关信息