316L不锈钢波纹管膨胀节开裂原因分析与预防
Cracking Reason Analysis and Prevention of Bellows Expansion Joint of 316L Stainless Steel
摘 要
某厂的316L不锈钢波纹管膨胀节在使用近3 a(年)发生了穿透性开裂。采用化学成分分析、宏观及微观检验等方法对该波纹管膨胀节开裂的原因进行了分析。结果表明: 氯化物应力腐蚀开裂是该波纹管开裂的主要原因, 并提出了相应的预防措施。
316L不锈钢
氯化物应力腐蚀开裂
bellows expansion joint
316L stainless steel
chloride stress corrosion cracking
Abstract
The bellows expansion joints used in nearly 3 years were penetrating cracking. The cracking reason was analyzed by means of chemical composition analysis, macro and micro observation. The results showed that the chloride stress corrosion cracking (Cl-SCC) was the main reason for the bellows cracking, and the corresponding prevention measures were put forward.
中图分类号 TQ055.8
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/9/29
修改稿日期
网络出版日期
作者单位点击查看
备注陈彩霞(1981-), 女, 工程师, 硕士。
引用该论文: CHEN Cai-xia,ZHENG Yang-yan. Cracking Reason Analysis and Prevention of Bellows Expansion Joint of 316L Stainless Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(1): 55～58
陈彩霞,郑杨艳. 316L不锈钢波纹管膨胀节开裂原因分析与预防[J]. 理化检验－物理分册, 2015, 51(1): 55～58
被引情况:
【1】江爱华,胡胜文,邓贤远,何山, "造船龙门起重机车轮轴断裂原因分析",理化检验－物理分册 52, 139-141(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵东,李京民,马彦东,等.316L不锈钢波纹管泄漏原因分析［J］.失效分析与预防,2009,4(4):217-220.
【2】康学勤,孙智.供热管道不锈钢波纹管膨胀节失效分析［J］.压力容器,2007,24(8):38-42.
【3】杜洪奎,盛水平.不锈钢波纹管膨胀节应力腐蚀研究进展［J］.中国安全生产科学技术,2011,7(6):54-57.
【4】王勤生.奥氏体不锈钢波纹管的应力腐蚀研究［D］.南京:南京工业大学,2004.
【5】赵彦芬,张路.奥氏体不锈钢波纹膨胀节失效分析［J］.理化检验-物理分册,2008,44(12):694-697.
【2】康学勤,孙智.供热管道不锈钢波纹管膨胀节失效分析［J］.压力容器,2007,24(8):38-42.
【3】杜洪奎,盛水平.不锈钢波纹管膨胀节应力腐蚀研究进展［J］.中国安全生产科学技术,2011,7(6):54-57.
【4】王勤生.奥氏体不锈钢波纹管的应力腐蚀研究［D］.南京:南京工业大学,2004.
【5】赵彦芬,张路.奥氏体不锈钢波纹膨胀节失效分析［J］.理化检验-物理分册,2008,44(12):694-697.
相关信息