传输装置转子转轴断裂原因分析

传输装置转子转轴断裂原因分析

Analysis on Fracture Reason of Rotor Shaft of Transmission Device

朱正

王春亮

摘要

利用直读光谱仪、光学显微镜、扫描电镜和电子能谱仪等检测仪器, 分析了某传输装置的转子转轴断裂的原因。结果表明: 由于应力腐蚀原因引起转子转轴钢管发生开裂, 并以疲劳形式扩展, 直至断裂。

标签传输装置

转子转轴

有缝钢管

断裂

应力腐蚀开裂

疲劳

transmission device

rotor shaft

seamed steel tube

fracture

stress corrosion cracking

fatigue

Abstract

The fracture reason of rotor shaft of transmission device was analyzed by optical direct reading spectrometer, optical microscope, scanning electron microscope (SEM) and election diffraction spectrometer (EDS). The results showed that the cracks were caused by stress corrosion, and expanded in the form of fatigue, until the fracture appeared in rotor shaft.

中图分类号 TH133.2

所属栏目质量控制与失效分析

基金项目

收稿日期 2013/11/25

修改稿日期

网络出版日期

作者单位点击查看

备注朱正(1980-), 男, 助理工程师, 学士。

引用该论文: ZHU Zheng,WANG Chun-liang. Analysis on Fracture Reason of Rotor Shaft of Transmission Device[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(1): 65～68
朱正,王春亮. 传输装置转子转轴断裂原因分析[J]. 理化检验－物理分册, 2015, 51(1): 65～68

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

参考文献

【1】桂立丰.机械工程材料测试手册:腐蚀与摩擦学卷［M］.沈阳:辽宁科学技术出版社,2002:266-277.

【2】中国机械工程学会焊接学会.焊接手册［M］.北京:机械工业出版社,2007:107-108.

相关信息

	标题	相关频次
	40Cr钢齿轴的断裂原因分析	4
	60Si2CrA热轧弹簧断裂失效分析	4
	GIS用不锈钢板簧断裂分析与预防	4
	H13钢上顶杆模具的早期断裂分析	4
	N80油管断裂分析	4
	P110S钢级油管断裂失效分析	4
	SKD61钢压铸模具开裂分析	4
	齿轮的失效分析	4
	抽油泵凡尔罩断裂失效分析	4
	储液筒吸气管断裂分析	4
	船用艉轴断裂失效分析	4
	电厂外供泵轴断裂原因分析	4
	电站连接螺栓断裂失效分析	4
	动力站碱液输送泵泵轴断裂原因分析	4
	分动箱齿轮断裂原因	4
	高压调节阀后热电偶套管断裂原因分析	4
	列车车轮辐板断裂原因分析	4
	某HL级35CrMo抽油杆断裂原因分析	4
	某超临界电站锅炉送风机叶片的断裂原因分析	4
	某供热管网用DN25铜阀断裂原因分析	4
	某锅炉换热器换热管断裂原因分析	4
	某挖掘机高强螺栓断裂原因分析	4
	某油管断裂原因	4
	某油井油管短节断裂原因分析	4
	凝结水泵轴断裂原因分析	4
	汽车后背门用植绒弹簧断裂失效分析	4
	汽车冷却装置护板断裂的原因	4
	汽轮机末级叶片断裂原因分析	4
	切胶机连接轴断裂原因分析	4
	石化重催装置安全阀弹簧断裂原因分析	4