某井S13Cr特殊螺纹接头油管柱腐蚀原因
Corrosion Causes of Premium Connection S13Cr Tubing in a Well
摘 要
为了掌握S13Cr特殊螺纹接头油管的耐蚀性,对某井特殊螺纹接头S13Cr油管柱腐蚀状况进行了全面检查,并对不同井深位置油管柱取样进行解剖分析。从油管接头关键结构尺寸和表面精度、井深、腐蚀介质等方面对腐蚀的影响进行了分析,结果表明,不同井段油管腐蚀程度不同,油管特殊螺纹接头内倒角越小,表面精度越高,油管抗腐蚀性能越好。
特殊螺纹接头
腐蚀
接头内倒角
tubing
premium connection
corrosion
joint inner chamfer
Abstract
In order to master the corrosion resistance of S13Cr,the corrosion status of premium connection S13Cr tubing in a well was checked,and the tubing specimens taken from different well depths were analyzed. Based on the analysis of the effects of main structure dimension and surface precision for the premium connection,well depth and corrosion medium,it was considered that the tubing corrosion degrees were not the same in different well depths,the less the tubing joint inner chamfer,the more the corrosion resistance;and the more the surface precision of tubing joint inner chamfer,the more the corrosion resistance.
中图分类号 TG174
所属栏目 失效分析
基金项目
收稿日期 2014/3/16
修改稿日期
网络出版日期
作者单位点击查看
备注吕拴录(1957-),教授级高级工程师,学士,从事失效分析工作,13565769572.
引用该论文: Lv Shuan-lu,SONG Wen-wen,YANG Xiang-tong,PENG Jian-xin,HAN Yong,ZHAO Guo-xian,Lv Xiang-hong,GUO Zhen-dong,WEN Ya-xin,ZHU Liang-liang. Corrosion Causes of Premium Connection S13Cr Tubing in a Well[J]. Corrosion & Protection, 2015, 36(1): 76
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Lv S L,XIANG J M,CHANG Z L,et al. Analysis of premium connection downhole tubing corrosion[J].Material Performance,2008,5:66-69.
【2】吕拴录,相建民,常泽亮,等. 牙哈301井油管腐蚀原因分析[J].腐蚀与防护,2008,29(11):706-709.
【3】张华民,齐公台. 钢铁表面高温氧化皮对基体钢腐蚀的影响[J].材料保护,1995,6.
【4】毕洪运,于杰,赵鹏,等. G105钻杆腐蚀失效分析[J].理化检验-物理分册,2005,41(6):304-306.
【5】齐慧滨,杜翠薇,李晓刚,等. 湿热环境中碱性泥浆附着下镀锌钢板的腐蚀行为[J].金属学报,2009,45(3):338-344.
【6】吕拴录. 特殊螺纹接头油套管选用注意事项[J].石油技术监督,2005,21(11):12-14.
【7】吕拴录,韩勇. 特殊螺纹接头油,套管使用及展望[J].石油工业技术监督,2003,3:1-4.
【8】吕拴录,骆发前,陈飞,等. 牙哈7X-1井套管压力升高原因分析[J].钻采工艺,2008,31(1):129-132.
【9】吕拴录,李元斌,王振彪,等. 某高压气井13Cr油管柱泄漏和腐蚀原因分析[J].腐蚀与防护,2010,31(11):902-904.
【10】Lv S L,ZHANG G Z. Analysis of N80 BTC downhole tubing corrosion[J].Material Performance,2004,43(10):35.
【11】吕拴录,赵国仙,王新虎,等. 特殊螺纹接头油管腐蚀原因分析[J].腐蚀与防护,2005,26(4):28.
【12】吕拴录,骆发前,相建民,等. API油管腐蚀原因分析[J].腐蚀科学与防护技术,2007,5:64-66.
【13】吕拴录,相建民,常泽亮,等. 牙哈301井油管腐蚀原因分析[J].腐蚀与防护,2008,29(11):706-709.
【14】袁鹏斌,郭生武,吕拴录. 低合金高强度油管应力导向氢致开裂腐蚀失效分析[J].腐蚀与防护,2010,31(5):407-410.
【15】张福祥,吕拴录,王振彪,等. 某高压气井套压升高及特殊螺纹接头不锈钢油管腐蚀原因分析[J].中国特种设备安全,2010,26(5):65-68.
【16】YUAN P B,GUO S W,L S L. Failure analysis of high-alloy oil well tubing coupling[J].Material Performance,2010,49(8):68-71.
【2】吕拴录,相建民,常泽亮,等. 牙哈301井油管腐蚀原因分析[J].腐蚀与防护,2008,29(11):706-709.
【3】张华民,齐公台. 钢铁表面高温氧化皮对基体钢腐蚀的影响[J].材料保护,1995,6.
【4】毕洪运,于杰,赵鹏,等. G105钻杆腐蚀失效分析[J].理化检验-物理分册,2005,41(6):304-306.
【5】齐慧滨,杜翠薇,李晓刚,等. 湿热环境中碱性泥浆附着下镀锌钢板的腐蚀行为[J].金属学报,2009,45(3):338-344.
【6】吕拴录. 特殊螺纹接头油套管选用注意事项[J].石油技术监督,2005,21(11):12-14.
【7】吕拴录,韩勇. 特殊螺纹接头油,套管使用及展望[J].石油工业技术监督,2003,3:1-4.
【8】吕拴录,骆发前,陈飞,等. 牙哈7X-1井套管压力升高原因分析[J].钻采工艺,2008,31(1):129-132.
【9】吕拴录,李元斌,王振彪,等. 某高压气井13Cr油管柱泄漏和腐蚀原因分析[J].腐蚀与防护,2010,31(11):902-904.
【10】Lv S L,ZHANG G Z. Analysis of N80 BTC downhole tubing corrosion[J].Material Performance,2004,43(10):35.
【11】吕拴录,赵国仙,王新虎,等. 特殊螺纹接头油管腐蚀原因分析[J].腐蚀与防护,2005,26(4):28.
【12】吕拴录,骆发前,相建民,等. API油管腐蚀原因分析[J].腐蚀科学与防护技术,2007,5:64-66.
【13】吕拴录,相建民,常泽亮,等. 牙哈301井油管腐蚀原因分析[J].腐蚀与防护,2008,29(11):706-709.
【14】袁鹏斌,郭生武,吕拴录. 低合金高强度油管应力导向氢致开裂腐蚀失效分析[J].腐蚀与防护,2010,31(5):407-410.
【15】张福祥,吕拴录,王振彪,等. 某高压气井套压升高及特殊螺纹接头不锈钢油管腐蚀原因分析[J].中国特种设备安全,2010,26(5):65-68.
【16】YUAN P B,GUO S W,L S L. Failure analysis of high-alloy oil well tubing coupling[J].Material Performance,2010,49(8):68-71.
相关信息