L360MCS级直缝埋弧焊管泄漏事故原因分析
Analysis of Leakage Accident of L360MCS Longitudinal Submerged Arc Welded (LSAW) Pipe
摘 要
调查了508 mm×16 mm的L360MCS直缝埋弧焊(LSAW)钢管发生泄漏事故的情况, 对管材进行了材质检验, 对泄漏断口进行了金相分析和扫描电镜分析。结果表明硫化物应力腐蚀是该直缝埋弧焊钢管发生泄漏的根本原因。补焊工艺不当使焊缝产生了表面刮痕、马氏体组织和较高的残余应力增大了焊缝的应力腐蚀敏感性。
焊缝
泄漏
硫化物应力腐蚀开裂
补焊
longitudinal submerged arc welded (LSAW) pipe
weld seam
leakage
sulfide stress corrosion cracking
repairing welding
Abstract
The leakage accident occurring in a 508 mm×16mm L360MCS LSAW (longitudinal submerged arc welded) pipe was investigated by testing the pipe material composition, analyzing the metallograph and smicro morphology of the fracture. The results showed that the leakage of the pipe was caused by sulfide stress corrosion cracking. The surface scratch martensite and high residual stress due to unproper repairing welding process could increase the susceptibility to sulfide stress corrosion cracking of the weld.
中图分类号 TG172.9
所属栏目 腐蚀失效分析
基金项目
收稿日期 2010/4/27
修改稿日期 2010/4/29
网络出版日期
作者单位点击查看
备注张良,助理工程师,
引用该论文: ZHANG Liang,LUO Jin-heng,FENG Yao-rong,LI Jin-feng. Analysis of Leakage Accident of L360MCS Longitudinal Submerged Arc Welded (LSAW) Pipe[J]. Corrosion & Protection, 2011, 32(2): 153
被引情况:
【1】袁军涛,林冠发,熊新民,王应全,成福田,宋恩鹏,石鑫,巴特,甘小平,殷树根, "西部某油田处理站外输气弯管爆裂原因分析",腐蚀与防护 37, 175-179(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】冯耀荣, 李铁虎, 李国兴,等. X60螺旋缝埋弧焊管在湿H2S环境中的腐蚀行为[C]//石油工程论文编选(2001-2005). 北京: 石油工业出版社, 2005: 562-566.
【2】NACE MR0175, 油田设备用抗硫化物应力开裂金属材料[S].
【3】ISO 3183-3, 石油和天然气工业管道用钢管的技术交货条件C级要求的钢管[S].
【4】刘瑞堂. 机械零件失效分析[M]. 哈尔滨: 哈尔滨工业大学出版社, 2003.
【5】薛锦. 应力腐蚀与环境氢脆[M]. 西安: 西安交通大学出版社, 1991.
【2】NACE MR0175, 油田设备用抗硫化物应力开裂金属材料[S].
【3】ISO 3183-3, 石油和天然气工业管道用钢管的技术交货条件C级要求的钢管[S].
【4】刘瑞堂. 机械零件失效分析[M]. 哈尔滨: 哈尔滨工业大学出版社, 2003.
【5】薛锦. 应力腐蚀与环境氢脆[M]. 西安: 西安交通大学出版社, 1991.
相关信息