Influence of Heat Treatment Temperature on Corrosion Resistance of Ni-W-P Coating
摘 要
采用失重法及电化学方法对镀态和热处理后的Ni-W-P镀层在5%硫酸溶液中的耐蚀性能进行了研究。比较了不同温度热处理后Ni-P镀层和Ni-W-P镀层的耐蚀性能, 并结合X射线衍射(XRD)、扫描电镜(SEM)对镀层的耐蚀性机理进行了分析。结果表明, Ni-P镀层在400~700 ℃热处理后耐蚀性能下降, 而Ni-W-P镀层的耐蚀性能增加, 且随着热处理温度的上升而提高。
Abstract
The anti-corrosion performance of as-plated and heat-treated Ni-W-P coatings was studied by immersion corrosion and electrochemical tests in 5% H2SO4 solution. The heat-treated Ni-W-P coatings had better corrosion resistance than the heat-treated Ni-P coatings. The treated Ni-P coatings had worse anticorrosion performance than the untreated coating, while the corrosion resistance of treated Ni-W-P coatings was better than the as-plated coating. And the corrosion resistance performance of Ni-W-P was greatly improved with the increase heat-treated temperature.
中图分类号 TG174.44 TQ153.2
所属栏目 试验研究
基金项目 上海市重点学科建设项目(B503)
收稿日期 2010/5/17
修改稿日期 2010/6/26
网络出版日期
作者单位点击查看
备注姚志燕, 硕士研究生,
引用该论文: YAO Zhi-yan,XU Hong,HOU Feng,YAN Cao. Influence of Heat Treatment Temperature on Corrosion Resistance of Ni-W-P Coating[J]. Corrosion & Protection, 2011, 32(3): 173
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】徐瑞东, 郭忠诚, 朱晓云, 等. 高磷非晶态镍磷合金镀层的研究[J]. 电镀与环保, 2002, 22(3): 18-20.
【2】于晓鹏, 成科. PTA装置不锈钢设备的腐蚀及采用Ni-P合金镀层的应用可行性[J]. 腐蚀与防护, 2001, 22(11): 494-497.
【3】王雪英, 王璐. 化学镀Ni-W-P合金层的组织结构与耐蚀性能的研究[J]. 材料保护, 1992, 25(5): 19-23.
【4】于祖孝, 郝世雄, 孙亚丽, 等. 热处理工艺对化学镀Ni-W-Mo-P四元合金性能的影响[J]. 材料热处理技术, 2008, 37(22): 52-55.
【5】耿冰霜, 卫英慧, 侯利锋, 等. 不锈钢衬底化学镀Ni-W-P三元合金组织及性能研究[J]. 稀有金属材料与工程, 2009, 38(1): 71-75.
【6】Gao Y J, Zheng Z, Zhu M, et al. Corrosion resistance of electrolessly deposited Ni-P and Ni-W-P alloys with various structures[J]. Materials Science and Engineering, 2004, 381:98-103.
【7】Ashassi-Sorkhabi H, Rafizadeh S H. Effect of coating time and heat treatment on structures and corrosion characteristics of electroless Ni-P alloy deposits[J]. Surface and Technology, 2003, 176:318-326.
【8】宋玉强, 王引真, 何艳玲. 化学镀Ni-P镀层高温热处理后耐蚀性能的研究[J]. 材料保护, 2003, 36(5): 31-33.
【2】于晓鹏, 成科. PTA装置不锈钢设备的腐蚀及采用Ni-P合金镀层的应用可行性[J]. 腐蚀与防护, 2001, 22(11): 494-497.
【3】王雪英, 王璐. 化学镀Ni-W-P合金层的组织结构与耐蚀性能的研究[J]. 材料保护, 1992, 25(5): 19-23.
【4】于祖孝, 郝世雄, 孙亚丽, 等. 热处理工艺对化学镀Ni-W-Mo-P四元合金性能的影响[J]. 材料热处理技术, 2008, 37(22): 52-55.
【5】耿冰霜, 卫英慧, 侯利锋, 等. 不锈钢衬底化学镀Ni-W-P三元合金组织及性能研究[J]. 稀有金属材料与工程, 2009, 38(1): 71-75.
【6】Gao Y J, Zheng Z, Zhu M, et al. Corrosion resistance of electrolessly deposited Ni-P and Ni-W-P alloys with various structures[J]. Materials Science and Engineering, 2004, 381:98-103.
【7】Ashassi-Sorkhabi H, Rafizadeh S H. Effect of coating time and heat treatment on structures and corrosion characteristics of electroless Ni-P alloy deposits[J]. Surface and Technology, 2003, 176:318-326.
【8】宋玉强, 王引真, 何艳玲. 化学镀Ni-P镀层高温热处理后耐蚀性能的研究[J]. 材料保护, 2003, 36(5): 31-33.
相关信息