W450QN钢大气腐蚀性能
Atmospheric Corrosion Performance of W450QN Steel
摘 要
对武钢生产的W450QN钢进行了3年的大气暴露试验, 结果表明, W450QN钢的耐蚀性优于Q345钢, 在青岛站 、江津站、琼海站, W450QN钢与Q345钢相比, 平均腐蚀速率之比分别为1∶1.48, 1∶1.45, 1∶1.44。带锈样的极化曲线测试结果显示, W450QN钢的致钝电流密度、维钝电流密度均比Q345钢小, 说明其锈层致密、传质能力差, 所以防护性能好。
大气腐蚀
锈层
weathering steel
atmospheric corrosion
rust layer
Abstract
Three years atmospheric corrosion of W450QN steel made by Wuhan Iron & Steel (Group) Corp was carried out. The results show that the corrosion resistance of W450QN was better than that of Q345, the average corrosion rate in Qingdao, Jiangjin and Qionghai decreased by a third compared with that of Q345. The polarization curves of 3-year exposed rusty steel showed that both of the initial passivity current and maintaining passivity current of W450QN were smaller than those of Q345, indicating a better protective performance of W450QN due to its compact rust layer and higher mass transfer resistance.
中图分类号 TG172.3
所属栏目 应用技术
基金项目
收稿日期 2010/6/4
修改稿日期 2010/7/24
网络出版日期
作者单位点击查看
备注刘建容, 高级工程师,
引用该论文: LIU Jian-rong,ZHANG Wan-ling,CAI Jie,SHI Zheng-ming. Atmospheric Corrosion Performance of W450QN Steel[J]. Corrosion & Protection, 2011, 32(4): 305
被引情况:
【1】李 琳,钟 彬,高 鹏,艾芳芳,徐小连,陈义庆,肖 宇, "Q690qENH钢暴晒两年的大气腐蚀性能",腐蚀与防护 36, 869-872(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】曹楚南. 悄悄进行的破坏——金属腐蚀[M]. 北京: 清华大学出版社, 暨南大学出版社, 2000.
【2】叶康民. 金属腐蚀与防护概论[M]. 北京:人民教育出版社, 1981.
【3】刘建容, 刘正生, 张万灵. 低合金钢大气腐蚀锈层的研究[J]. 工业建筑, 2001, 31:34-38.
【4】梁彩凤, 侯文泰. 碳钢及低合金钢8年大气暴露腐蚀研究[J]. 腐蚀科学与防护技术, 1995, 7(3):183-186.
【2】叶康民. 金属腐蚀与防护概论[M]. 北京:人民教育出版社, 1981.
【3】刘建容, 刘正生, 张万灵. 低合金钢大气腐蚀锈层的研究[J]. 工业建筑, 2001, 31:34-38.
【4】梁彩凤, 侯文泰. 碳钢及低合金钢8年大气暴露腐蚀研究[J]. 腐蚀科学与防护技术, 1995, 7(3):183-186.
相关信息