6063铝合金阳极氧化过程中麻点问题分析
Analyses of Rough Point Defects on 6063 Aluminum Alloy in Anodizing Process
摘 要
通过表面形态和显微组织观察, 采用扫描电镜(SEM)、能谱(EDS)等手段分析了6063铝型材在阳极氧化过程中出现麻点的原因。结果表明, 麻点实质为点腐蚀, 是由于合金中游离态Si、金属间化合物、过量Zn等导致的择优腐蚀, 以及Cl-加速了铝合金的活性溶解。
阳极氧化
麻点
aluminum alloy
anodizing
rough point
Abstract
The rough points on 6063 aluminum alloy formed in its anodizing process were analyzed by means of surface morphology analysis, microstructure analysis, SEM and EDS. The results showed that the rough point formed defect in the anodizing process was pitting corrosion, resulting from the selective corrosion of free Si, intermetalic compounds, superfluous Zn, etc, and rapid dissolution of aluminum alloy activated by Cl-. The corrosion resistance of aluminum alloy with rough points will be reduced remarkably.
中图分类号 TG178
所属栏目 应用技术
基金项目
收稿日期 2010/5/13
修改稿日期 2010/6/7
网络出版日期
作者单位点击查看
备注王雨顺, 硕士研究生,
引用该论文: WANG Yu-shun,DING Yi,MA Li-qun. Analyses of Rough Point Defects on 6063 Aluminum Alloy in Anodizing Process[J]. Corrosion & Protection, 2011, 32(4): 314
被引情况:
【1】郑戬,叶兵,丁文江, "高强度耐腐蚀铝合金的研究进展",腐蚀与防护 36, 511-515(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴纯素. 化学转化膜[M]. 北京: 化学工业出版社, 1988.
【2】杨杨, 陈秀琴, 徐志强, 等. 6063铝型材表面斑状缺陷成因探讨[J]. 矿冶工程, 2001, 21(2):75-77.
【3】卢燕平, 方百友, 余庆, 等. 6063铝型材碱洗过腐蚀原因分析[J]. 材料保护, 1998, 31(5):7-8.
【2】杨杨, 陈秀琴, 徐志强, 等. 6063铝型材表面斑状缺陷成因探讨[J]. 矿冶工程, 2001, 21(2):75-77.
【3】卢燕平, 方百友, 余庆, 等. 6063铝型材碱洗过腐蚀原因分析[J]. 材料保护, 1998, 31(5):7-8.
相关信息