Performance of Metallic-Ceramic Anti-Corrosion Coating IPcote9183
摘 要
用一种进口水基含铝高温防腐蚀涂料制备了金属陶瓷涂层, 介绍了制备的工艺, 对该涂层的性能进行了研究。结果表明, 按照一定的喷涂压力和喷涂距离进行喷涂, 可获得表面均匀、结合良好的涂层。喷涂一层IPcote9183可以获得厚度为0.01 mm~0.02 mm的涂层; 可进行多层喷涂。厚度为0.02~0.03 mm的涂层, 中性盐雾试验可达到1000 h不出现红锈。
Abstract
An aluminium containing high-temperature anti-corrosion water-based paint was used to prepare metallic-ceramic coating, and performance of the coating was studied. The results showed that the coating was uniform and had good adhesion under the conditions of a certain spray pressure and nozzle/sample distance. The coating thickness was 0.01 ~ 0.02 mm for every IPcote9183 layer. The thickness could increase by repeating spray + dry. The coating with thickness of 0.02 ~ 0.03 mm was used to salt fog test and there was no red rust after 1000 h.
中图分类号 TG174.4
所属栏目 应用技术
基金项目
收稿日期 2010/7/25
修改稿日期 2010/8/13
网络出版日期
作者单位点击查看
备注王维, 工程师,
引用该论文: WANG Wei. Performance of Metallic-Ceramic Anti-Corrosion Coating IPcote9183[J]. Corrosion & Protection, 2011, 32(6): 480
被引情况:
【1】王云鹏,李淑琴,陈小虎,潘儒杰,张平则, "含铝磷酸盐防腐涂层的制备与性能",机械工程材料 40, 42-45(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨康, 王国志, 王志强, 等. 水基含铝耐高温防腐蚀涂料[J]. 现代涂料与涂装, 2006(7):9-11.
【2】贾中华. 料浆法制备铌合金与钼合金高温氧化涂层[J]. 粉末冶金技术, 2001, 19(2):74-76.
【3】曾爱香, 唐绍裘. 金属基陶瓷涂层的制备、应用及发展[J]. 陶瓷学报, 1998, 13(4):7-10.
【4】《航空制造工程手册》总编委会. 航空制造工程手册·表面处理[M]. 北京: 航空工业出版社, 1993.
【5】汤智慧, 宇波, 高玉魁, 等. 后处理对离子镀铝涂层腐蚀性能的影响研究[J]. 装备环境工程, 2007(1):27-31.
【2】贾中华. 料浆法制备铌合金与钼合金高温氧化涂层[J]. 粉末冶金技术, 2001, 19(2):74-76.
【3】曾爱香, 唐绍裘. 金属基陶瓷涂层的制备、应用及发展[J]. 陶瓷学报, 1998, 13(4):7-10.
【4】《航空制造工程手册》总编委会. 航空制造工程手册·表面处理[M]. 北京: 航空工业出版社, 1993.
【5】汤智慧, 宇波, 高玉魁, 等. 后处理对离子镀铝涂层腐蚀性能的影响研究[J]. 装备环境工程, 2007(1):27-31.
相关信息