T0103苯甲酸蒸馏塔内壁腐蚀沟槽产生原因
Inwall Corrosion of T0103 Distillation Tower of Benzoic Acid
摘 要
采用化学方法、金相显微镜和扫描电镜等对失效后的T0103苯甲酸蒸馏第十二层塔筒体上的腐蚀沟槽进行了分析。结果表明, 腐蚀沟槽位于设备补焊处的焊缝区; 补焊时所选焊条耐蚀性太低, 且与筒体316L不锈钢基体不匹配, 是导致其腐蚀失效的主要原因。
腐蚀
失效分析
316L stainless steel
corrosion
failure analysis
Abstract
The inwall corrosion of failed T0103 distillation tower of benzoic acid was investigated by chemical method, optical microscopy and SEM. The results showed that the corrosive groove of the tower inwall was formed due to the corrosion of repaired weld zone. The welding rod used to repaire failed to match with 316L stainless steel of tower basic, which induced the corrosion of the tower inwall.
中图分类号 TG172
所属栏目 应用技术
基金项目
收稿日期 2010/9/1
修改稿日期 2010/12/15
网络出版日期
作者单位点击查看
备注熊金平, 副教授, 博士,
引用该论文: LI Qing-hua,WANG Bo,YANG Gen-zhu,LI De-chao,XIONG Jin-ping,LU Zheng-liang. Inwall Corrosion of T0103 Distillation Tower of Benzoic Acid[J]. Corrosion & Protection, 2011, 32(7): 570
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】化学工业部化工机械研究院编. 腐蚀与防护手册——化工生产装置的腐蚀与防护[M]. 北京: 化学工业出版社, 1991.
【2】孙秋霞主编. 材料腐蚀与防护[M]. 北京: 冶金工业出版社, 2001.
【3】朱祖芳编. 有色金属的耐腐蚀性及其应用[M]. 北京: 化学工业出版社, 1995.
【4】中国腐蚀与防护学会编. 金属腐蚀手册[M]. 上海:上海科学技术出版社, 1987.
【5】华保定, 沈行素, 戴钟道, 等. 18铬-8镍型不锈钢的晶间腐蚀与电位关系[J]. 金属学报, 1961, 8(1):24-26.
【6】李异, 韦荣松, 褟浩文. 316L不锈钢非敏化态晶间腐蚀敏感性研究[J]. 腐蚀与防护, 1991, 12(4): 177-182.
【7】李异, 褟浩文, 韦荣松. 316L不锈钢晶间腐蚀机理的探讨[J]. 腐蚀科学与防护技术, 1993, 5(2): 131-135.
【8】于福洲, 许淳淳, 姚建明. 固溶态不锈钢在尿素生产介质中的晶间腐蚀与磷(硅)的晶界富集[J]. 中国腐蚀与防护学报, 1985, 5(1): 28-32.
【2】孙秋霞主编. 材料腐蚀与防护[M]. 北京: 冶金工业出版社, 2001.
【3】朱祖芳编. 有色金属的耐腐蚀性及其应用[M]. 北京: 化学工业出版社, 1995.
【4】中国腐蚀与防护学会编. 金属腐蚀手册[M]. 上海:上海科学技术出版社, 1987.
【5】华保定, 沈行素, 戴钟道, 等. 18铬-8镍型不锈钢的晶间腐蚀与电位关系[J]. 金属学报, 1961, 8(1):24-26.
【6】李异, 韦荣松, 褟浩文. 316L不锈钢非敏化态晶间腐蚀敏感性研究[J]. 腐蚀与防护, 1991, 12(4): 177-182.
【7】李异, 褟浩文, 韦荣松. 316L不锈钢晶间腐蚀机理的探讨[J]. 腐蚀科学与防护技术, 1993, 5(2): 131-135.
【8】于福洲, 许淳淳, 姚建明. 固溶态不锈钢在尿素生产介质中的晶间腐蚀与磷(硅)的晶界富集[J]. 中国腐蚀与防护学报, 1985, 5(1): 28-32.
相关信息