白酒糟提取物对Q235钢在盐酸介质中的缓蚀作用和吸附行为
Corrosion Inhibition and Adsorption Behavior of Distiller′s Grains Extractive for Q235 Steel in Hydrochloric Acid Medium
摘 要
采用失重法和电化学法研究了白酒糟提取物作为酸洗缓蚀剂对Q235钢在盐酸介质中的缓蚀作用和吸附行为。失重法研究表明, 白酒糟提取物在盐酸介质中能有效抑制Q235钢的腐蚀, 25 ℃, 1 mol/L的HCl中, 白酒糟提取物浓度为24 g/L时, 缓蚀率达到94.41％; 电化学研究结果表明, 白酒糟提取物在1 mol/L HCl中属抑制阳极反应为主的混合型缓蚀剂; 另外, 利用失重试验数据进行吸附规律拟合结果表明, 白酒糟提取物在Q235钢表面吸附符合El-Awady动力学模型与Flory-Huggins等温线方程, 其吸附为几何覆盖效应的单分子层吸附。
酒糟
缓蚀剂
失重
极化
吸附
hydrochloric acid
distillers′ grain
corrosion inhibitor
weight loss
polarization
adsorption
Abstract
The corrosion inhibition and adsorption behavior of the extractive from distiller′s grains for Q235 steel in hydrochloric acid medium was studied by weight loss and electrochemical methods. The results of weight loss showed that the inhibition efficiency was up to 94.41％ when the inhibitor concentration was 24 g/L in 1 mol/L HCl solution at 25 ℃. The results of polarization curves showed that the extractive from distiller′s grains was a mixed-type inhibitor in hydrochloric acid medium. The fitting results showed that the adsorption met the El-Awady thermodynamic kinetic model and was inline with the Flory-Huggins isotherm.
中图分类号 TG174.42
所属栏目 试验研究
基金项目 泸州老窖科研奖学金项目(No.09ljzk10); 四川省科技厅科技支撑计划项目(No.2010GZ0130); 四川省教育厅重点项目(No.09ZA057)和腐蚀与防护四川省高校重点实验室重点项目(No.2008CL03)资助。
收稿日期 2010/10/28
修改稿日期 2010/11/16
网络出版日期
作者单位点击查看
联系人作者谢斌(lc860801@126.com)
备注谢斌, 教授,
引用该论文: LAI Chuan,XIE Bin,YI Bin,ZENG Ni,HUANG Chun,WANG Yan-mei,LU Zhong-ming. Corrosion Inhibition and Adsorption Behavior of Distiller′s Grains Extractive for Q235 Steel in Hydrochloric Acid Medium[J]. Corrosion & Protection, 2011, 32(8): 616
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】汤兵, 陈欣义. 酸洗过程中的缓蚀剂[J]. 清洗世界, 2006, 22(2):22-28.
【2】余志强, 徐强, 任志峰, 等. 金属在酸性介质中有机缓蚀剂的研究进展[J]. 电镀与精饰, 2008, 30(11):19-23.
【3】张宝宏, 丛文博, 杨萍. 金属电化学腐蚀与防护[M]. 北京:化学工业出版社, 2005.
【4】Ahamad I, Quraishi M A. Mebendazole: new and efficient corrosion inhibitor for mild steel in acid medium[J]. Corrosion Science, 2010, 52(2):651-656.
【5】Hegazy M A, Zaky M F. Inhibition effect of novel nonionic surfactants on the corrosion of carbon steel in acidic medium[J]. Corrosion Science, 2010, 52(4):1333-1341.
【6】杨尚军, 谭世语, 张研. 生物缓蚀剂的研究进展[J]. 表面技术, 2006, 35(1):12-13.
【7】黄艳仙, 蔡洁, 周建敏. 白玉兰叶提取物对A3钢在酸性介质中缓蚀性能的研究[J]. 应用化工, 2010, 39(4):538-540.
【8】印遇龙, 钟华宜. 酒糟作猪饲料的营养价值及其利用途径[J]. 资源开发与市场, 1991, 7(1):52-54.
【9】郑国锋, 钱和. 黄酒糟的成分分析和开发调味品可行性的研究[J]. 中国调味品, 2007, 338(4):20-25.
【10】张云鹏, 刘军, 陈娟. 白酒糟植酸提取条件的优化[J]. 中国酿造, 2010, 216(3):125-127.
【11】苏伟, 陆筑凤, 母应春. 酱香白酒糟综合利用新突破[J]. 酿酒科技, 2008, 168(6):102-105.
【12】刘晓牧, 吴乃科. 酒糟的综合开发与应用[J]. 畜牧与饲料工业, 2004, 25(5):9-10.
【13】Shukla S K, Quraishi M A. The efects of pharmaceutically active compound doxycycline on the corrosion of mild steel in hydrochloric acid solution[J]. Corrosion Science, 2010, 52(2):314-321.
【14】曹楚南. 腐蚀电化学原理[M]. 第三版, 北京:化学工业出版社, 2008.
【15】李向红, 付惠, 王毕辉, 等. 元宝枫叶提取物在盐酸溶液中对钢的缓蚀性能研究[J]. 清洗世界, 2009, 25(12):20-24.
【16】Bentiss F, Bouanis M, Mernari B, et al. Understanding the adsorption of 4H-1, 2, 4-triazole deriva-tiveson mild steel surface in molar hydrochloric acid[J]. Applied Surface Science, 2007, 253(7):3696-3704.
【17】Abd-El-Nabey B A, El-Awady A A, Aziz S G. Structural effects and mechanism of the inhibition of acid corrosion of steel by some dithiocarbamate derivatives[J]. Corrosion Prevention& Control.1991, 38(3):68-74.
【18】El-Awady A A, Abd-El-Nabey B A, Aziz S G. Thermodynamic and kinetic factors in chloride ions pitting and nitrogen donor ligands inhibition of aluminum metal corrosion in aggressive acid media[J]. Journal of the Chemical Society.Faraday Transactions, 1993, 89(5):795-802.
【19】Ateya B G, El-Anadouli B E, El-Nizamy F M. The adsorption of thiourea on mild steel[J]. Corrosion Science, 1984, 24(6):509-515.
【20】郑兴文, 龚敏, 邹振, 等. 竹叶提取液的制备及其缓蚀性能[J]. 材料保护, 2010, 43(2):21-23.
【21】胡胜, 康笑阳, 付朝阳. 米糠提取液作为盐酸酸洗缓蚀剂的研究[J]. 中国腐蚀与防护学报, 2009, 29(2):149-153.
【2】余志强, 徐强, 任志峰, 等. 金属在酸性介质中有机缓蚀剂的研究进展[J]. 电镀与精饰, 2008, 30(11):19-23.
【3】张宝宏, 丛文博, 杨萍. 金属电化学腐蚀与防护[M]. 北京:化学工业出版社, 2005.
【4】Ahamad I, Quraishi M A. Mebendazole: new and efficient corrosion inhibitor for mild steel in acid medium[J]. Corrosion Science, 2010, 52(2):651-656.
【5】Hegazy M A, Zaky M F. Inhibition effect of novel nonionic surfactants on the corrosion of carbon steel in acidic medium[J]. Corrosion Science, 2010, 52(4):1333-1341.
【6】杨尚军, 谭世语, 张研. 生物缓蚀剂的研究进展[J]. 表面技术, 2006, 35(1):12-13.
【7】黄艳仙, 蔡洁, 周建敏. 白玉兰叶提取物对A3钢在酸性介质中缓蚀性能的研究[J]. 应用化工, 2010, 39(4):538-540.
【8】印遇龙, 钟华宜. 酒糟作猪饲料的营养价值及其利用途径[J]. 资源开发与市场, 1991, 7(1):52-54.
【9】郑国锋, 钱和. 黄酒糟的成分分析和开发调味品可行性的研究[J]. 中国调味品, 2007, 338(4):20-25.
【10】张云鹏, 刘军, 陈娟. 白酒糟植酸提取条件的优化[J]. 中国酿造, 2010, 216(3):125-127.
【11】苏伟, 陆筑凤, 母应春. 酱香白酒糟综合利用新突破[J]. 酿酒科技, 2008, 168(6):102-105.
【12】刘晓牧, 吴乃科. 酒糟的综合开发与应用[J]. 畜牧与饲料工业, 2004, 25(5):9-10.
【13】Shukla S K, Quraishi M A. The efects of pharmaceutically active compound doxycycline on the corrosion of mild steel in hydrochloric acid solution[J]. Corrosion Science, 2010, 52(2):314-321.
【14】曹楚南. 腐蚀电化学原理[M]. 第三版, 北京:化学工业出版社, 2008.
【15】李向红, 付惠, 王毕辉, 等. 元宝枫叶提取物在盐酸溶液中对钢的缓蚀性能研究[J]. 清洗世界, 2009, 25(12):20-24.
【16】Bentiss F, Bouanis M, Mernari B, et al. Understanding the adsorption of 4H-1, 2, 4-triazole deriva-tiveson mild steel surface in molar hydrochloric acid[J]. Applied Surface Science, 2007, 253(7):3696-3704.
【17】Abd-El-Nabey B A, El-Awady A A, Aziz S G. Structural effects and mechanism of the inhibition of acid corrosion of steel by some dithiocarbamate derivatives[J]. Corrosion Prevention& Control.1991, 38(3):68-74.
【18】El-Awady A A, Abd-El-Nabey B A, Aziz S G. Thermodynamic and kinetic factors in chloride ions pitting and nitrogen donor ligands inhibition of aluminum metal corrosion in aggressive acid media[J]. Journal of the Chemical Society.Faraday Transactions, 1993, 89(5):795-802.
【19】Ateya B G, El-Anadouli B E, El-Nizamy F M. The adsorption of thiourea on mild steel[J]. Corrosion Science, 1984, 24(6):509-515.
【20】郑兴文, 龚敏, 邹振, 等. 竹叶提取液的制备及其缓蚀性能[J]. 材料保护, 2010, 43(2):21-23.
【21】胡胜, 康笑阳, 付朝阳. 米糠提取液作为盐酸酸洗缓蚀剂的研究[J]. 中国腐蚀与防护学报, 2009, 29(2):149-153.
相关信息