电化学阻抗谱评价输电铁塔防护涂层配套性能
Evaluation of Protective Coating Systems for Transmission Tower by Electrochemical Impedance Spectroscopy
摘 要
研究了用于输电铁塔防护的带锈环氧底漆(A)、水性环氧防锈底漆(B)、氟硅改性丙烯酸面漆(C)、有机硅改性醇酸树脂面漆(D)所组成的4个涂层配套体系的电化学阻抗谱图特征。通过研究涂层电阻、涂层孔隙率和10 kHz下的涂层相对介电常数对4种涂料配套体系的防腐蚀性能进行了比较和评价。结果表明, 4个配套涂层体系防护性能的优劣顺序为: A-D＞B-C＞B-D＞A-C, 测试评价结果与中性盐雾试验结果一致。适合于输电铁塔防护用的涂料为A-D体系, 即带锈环氧底漆/有机硅改性醇酸树脂面漆。
防护涂料
电化学阻抗谱(EIS)
耐腐蚀性能
transmission tower
anti-corrosion coating
electrochemical impedance spectroscopy (EIS)
corrosion resistance
Abstract
The electrochemical behavior of four different coating systems for transmission tower protection was studied by electrochemical impedance spectroscopy (EIS). The protective properties of the four coating systems were compared and evaluated from the properties of coating resistance, coating porosity and relative dielectric constant at 10 kHz.The results showed that the order of protective properties was A-D＞B-C＞B-D＞A-C, and agreed with the results of neutral salt spray testing.
中图分类号 TG174.2+3
所属栏目 应用技术
基金项目 国家电网公司科技项目(CL71-09-001)
收稿日期 2010/12/1
修改稿日期 2010/12/22
网络出版日期
作者单位点击查看
引用该论文: CHEN Yun,YAO Ning-na,CHEN Xin,HAN Yu. Evaluation of Protective Coating Systems for Transmission Tower by Electrochemical Impedance Spectroscopy[J]. Corrosion & Protection, 2011, 32(9): 735
被引情况:
【1】陈云,徐利民,陈懿夫,药宁娜, "不同表面处理对输电线路铁塔涂层性能的影响",腐蚀与防护 35, 823-828(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】金晓鸿, 洪栋煌. 新型舰船船体防腐蚀涂料配套体系的研究[J]. 材料开发与应用, 2001, 16(3):27-32.
【2】陈云, 强春媚, 王国刚, 等. 输电铁塔的腐蚀与防护[J]. 电力建设, 2010, 31(8):55-58.
【3】张鉴清, 曹楚南. 电化学阻抗谱方法研究评价有机涂层[J]. 腐蚀与防护, 1998, 19(3):99-104.
【4】曹京宜, 熊金平, 李水冰, 等. 利用EIS高频区参数评价两种环氧涂层的性能[J]. 化工学报, 2008, 59(11):2851-2856.
【2】陈云, 强春媚, 王国刚, 等. 输电铁塔的腐蚀与防护[J]. 电力建设, 2010, 31(8):55-58.
【3】张鉴清, 曹楚南. 电化学阻抗谱方法研究评价有机涂层[J]. 腐蚀与防护, 1998, 19(3):99-104.
【4】曹京宜, 熊金平, 李水冰, 等. 利用EIS高频区参数评价两种环氧涂层的性能[J]. 化工学报, 2008, 59(11):2851-2856.
相关信息