氧化钇掺杂对铝合金表面硅烷膜耐蚀性的影响
Effect of Rare Earth Oxides on Corrosion Resistance of BTSE Silane Film on Al Alloy 6061 Surface
摘 要
采用电化学测试的方法, 研究了稀土氧化物对铝合金表面1, 2-双-三乙氧基乙烷(BTSE)硅烷膜在3.5% NaCl溶液中耐蚀性的影响。结果表明, BTSE硅烷膜的形成并未改变6061铝合金试样表面的电极反应动力学行为, 硅烷膜的存在主要抑制了电化学腐蚀中的阴极还原反应, 对腐蚀性介质起到物理阻挡作用。在BTSE硅烷膜制备过程中掺杂Y2O3可有效提高硅烷膜的耐蚀性, 在本试验工艺条件下, Y2O3的最佳掺杂量为10~20 mg/L。
硅烷膜
铝合金
极化曲线
电化学阻抗谱
rare earth oxide(Y2O3)
silane film: aluminum alloy
polarization curve
EIS
bis-1, 2[triethoxysily]ethanc(BTSE)
Abstract
The effect of rare earth oxides on corrosion resistance of the bis-1, 2[triethoxysily]ethanc(BTSE) silane film on the Al alloy 6061 surface in 3.5% NaCl was studied by means of electrochemical measurements. The results showed that BTSE silane film did not change the behaviors of the electrode reaction kinetics of the surface of AA6061 samples, the presence of silane film mainly inhibited the cathodic reduction reaction in the electrochemical corrosion and played a physical barrier to the aggressive media. Doping Y2O3 in the preparation of BTSE silane film can improve the corrosion resistance of silane film effectively. Under the technical conditions determined by this experiment, the optimum doped Y2O3 contents were 10~20 mg/L.
中图分类号 TG174
所属栏目 试验研究
基金项目
收稿日期 2011/1/24
修改稿日期 2011/3/14
网络出版日期
作者单位点击查看
备注张圣麟, 教授, 博士,
引用该论文: ZHANG Sheng-lin,ZHANG Xiao-lin. Effect of Rare Earth Oxides on Corrosion Resistance of BTSE Silane Film on Al Alloy 6061 Surface[J]. Corrosion & Protection, 2011, 32(12): 965
被引情况:
【1】李文超,张明明,雷 越,乔静飞,张圣麟, "氯化铈掺杂对6061铝合金表面硅烷膜性能的影响",腐蚀与防护 36, 832-835(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】谈华民. 铝及铝合金的铬酸盐转化膜[J]. 电镀与精饰, 2003, 25(2):10-12.
【2】Zhao J, Xia L, Sehgal A, et al. Effect of chromate and chromate conversion coatings on corrosion of aluminum alloy 2024-T3 [J]. Surf Coat Technol, 2001(140):51-57.
【3】郭鹤桐, 王为. 铝阳极氧化的回顾与展望[J]. 材料保护, 2000, 33(1):43-45.
【4】崔昌军, 彭乔. 铝及铝合金的阳极氧化研究综述[J]. 全面腐蚀控制, 2006, 16(6):12-17.
【5】李立新, 李安忠, 万军. 金属磷化技术的回顾与展望[J]. 材料保护, 2000, 33(1):71-75.
【6】唐维学, 张小琴, 杨改霞. 环境友好型铝合金表面钝化技术进展[J]. 腐蚀与防护, 2010, 31(4):272-275.
【7】胡会利, 陈丽姣. 表面转化膜无铬化技术的研究动向[J]. 腐蚀与防护, 2009, 30(10):727-731, 755.
【8】刘倞, 胡吉明, 张鉴清, 等. 金属表面硅烷化防护处理及其研究现状[J]. 中国腐蚀与防护学报, 2006, 26(1):59-64.
【9】吴海江, 卢锦堂, 陈锦虹. 热镀锌钢表面硅烷膜耐蚀性能的初步研究[J]. 腐蚀与防护, 2006, 27(1):14-17.
【10】Yuan W, van Ooij W J. Characterization of organo functional silane films on zinc subst rates[J]. Journal of Collid and Interface Science, 1997(1):197-209.
【11】Child T F, Van Ooij W J. Application of silane technology to prevent corrosion of metals and improve paint adhesion[J]. Trans IMF, 1999, 77(2):64-70.
【12】徐溢, 王楠, 张小凤, 等. 直接用作金属表面新型防护涂层的硅烷偶联剂水解效果分析[J]. 腐蚀与防护, 2000, 21(4):157-159.
【13】王雪明, 李爱菊, 李国丽, 等. 硅烷偶联剂在防腐涂层金属预处理中的应用研究[J]. 材料科学与工程学报, 2005, 23(1):146-150.
【14】张明宗, 管从胜, 王威强. 有机硅烷偶联剂在金属表面预处理中的应用[J]. 腐蚀科学与防护技术, 2001, 13(2):96-99.
【15】Vignesh Palanivel A, Y Huangb, Wim J van Ooij. Effects of addition of corrosion inhibitors to silane films on the performance of AA2024-T3 in a 0.5M NaCl solution[J]. Progress in Organic Coatings, 2005, 53(3):153-168.
【16】Trabelsi W, Triki E, Dhouibi L, et al. The use of pre-treatments based on doped silane solutions for improved corrosion resistance of galvanised steel substrates[J]. Surf Coat Technol, 2006, 200(14/15):4240-4250.
【17】Xiao Wei, Man Ruilin, Miao Chang, et al. Study on corrosion resistance of the BTESPT silane cooperating with rare earth cerium on the surface of aluminum-tube[J]. Journal of Rare Earths, 2010, 28(1):117-122.
【2】Zhao J, Xia L, Sehgal A, et al. Effect of chromate and chromate conversion coatings on corrosion of aluminum alloy 2024-T3 [J]. Surf Coat Technol, 2001(140):51-57.
【3】郭鹤桐, 王为. 铝阳极氧化的回顾与展望[J]. 材料保护, 2000, 33(1):43-45.
【4】崔昌军, 彭乔. 铝及铝合金的阳极氧化研究综述[J]. 全面腐蚀控制, 2006, 16(6):12-17.
【5】李立新, 李安忠, 万军. 金属磷化技术的回顾与展望[J]. 材料保护, 2000, 33(1):71-75.
【6】唐维学, 张小琴, 杨改霞. 环境友好型铝合金表面钝化技术进展[J]. 腐蚀与防护, 2010, 31(4):272-275.
【7】胡会利, 陈丽姣. 表面转化膜无铬化技术的研究动向[J]. 腐蚀与防护, 2009, 30(10):727-731, 755.
【8】刘倞, 胡吉明, 张鉴清, 等. 金属表面硅烷化防护处理及其研究现状[J]. 中国腐蚀与防护学报, 2006, 26(1):59-64.
【9】吴海江, 卢锦堂, 陈锦虹. 热镀锌钢表面硅烷膜耐蚀性能的初步研究[J]. 腐蚀与防护, 2006, 27(1):14-17.
【10】Yuan W, van Ooij W J. Characterization of organo functional silane films on zinc subst rates[J]. Journal of Collid and Interface Science, 1997(1):197-209.
【11】Child T F, Van Ooij W J. Application of silane technology to prevent corrosion of metals and improve paint adhesion[J]. Trans IMF, 1999, 77(2):64-70.
【12】徐溢, 王楠, 张小凤, 等. 直接用作金属表面新型防护涂层的硅烷偶联剂水解效果分析[J]. 腐蚀与防护, 2000, 21(4):157-159.
【13】王雪明, 李爱菊, 李国丽, 等. 硅烷偶联剂在防腐涂层金属预处理中的应用研究[J]. 材料科学与工程学报, 2005, 23(1):146-150.
【14】张明宗, 管从胜, 王威强. 有机硅烷偶联剂在金属表面预处理中的应用[J]. 腐蚀科学与防护技术, 2001, 13(2):96-99.
【15】Vignesh Palanivel A, Y Huangb, Wim J van Ooij. Effects of addition of corrosion inhibitors to silane films on the performance of AA2024-T3 in a 0.5M NaCl solution[J]. Progress in Organic Coatings, 2005, 53(3):153-168.
【16】Trabelsi W, Triki E, Dhouibi L, et al. The use of pre-treatments based on doped silane solutions for improved corrosion resistance of galvanised steel substrates[J]. Surf Coat Technol, 2006, 200(14/15):4240-4250.
【17】Xiao Wei, Man Ruilin, Miao Chang, et al. Study on corrosion resistance of the BTESPT silane cooperating with rare earth cerium on the surface of aluminum-tube[J]. Journal of Rare Earths, 2010, 28(1):117-122.
相关信息